Abstract: Eco-friendly textiles are gaining importance among the consumers and textile manufacturers in the healthcare sector due to increased environmental pollution which leads to several health and environmental hazards. Hence, the research was designed to cultivate and develop the organic cotton knit, to prepare and characterize the Vetiver oil microcapsules for textile finishing and to access the wash durability of finished knits. The cotton SAHANA variety grown under organic production systems was processed and spun into 30 single yarn dyed with four natural colorants (Arecanut slurry, Eucalyptus leaves, Pomegranate rind and Indigo) and eco dyed yarn was further used for development of single jersy knitted fabric. Vetiveria zizanioides is an aromatic grass which is being traditionally used in medicine and perfumery. Vetiver essential oil was used for preparation of microcapsules by interfacial polymerization technique subjected to Gas Chromatography Mass Spectrometry (GCMS), Fourier Transform Infrared Spectroscopy (FTIR), Thermo Gravimetric Analyzer (TGA) and Scanning Electron Microscope (SEM) for characterization of microcapsules. The knitted fabric was finished with vetiver oil microcapsules by exhaust and pad dry cure methods. The finished organic knit was assessed for laundering on antimicrobial efficiency and aroma intensity. GCMS spectral analysis showed that, diethyl phthalate (28%) was the major compound found in vetiver oil followed by isoaromadendrene epoxide (7.72%), beta-vetivenene (6.92%), solavetivone (5.58%), aromadenderene, azulene and khusimol. Bioassay explained that, the vetiver oil and diluted vetiver oil possessed greater zone of inhibition against S. aureus and E. coli than the coconut oil. FTRI spectra of vetiver oil and microcapsules possessed similar peaks viz., C-H, C=C & C꞊O stretching and additionally oil microcapsules possessed the peak of 3331.24 cm-1 at 91.14 transmittance was attributed to N-H stretches. TGA of oil microcapsules revealed that, there was a minimum weight loss (5.835%) recorded at 467.09°C compared to vetiver oil i.e., -3.026% at the temperature of 396.24°C. The shape of the microcapsules was regular and round, some were spherical in shape and few were rounded by small aggregates. Irrespective of methods of application, organic cotton knits finished with microcapsules by pad dry cure method showed maximum zone of inhibition compared to knits finished by exhaust method against S. aureus and E. coli. The antimicrobial activity of the finished samples was subjected to multiple washing which indicated that knits finished with pad dry cure method showed a zone of inhibition even after 20th wash and better aroma retention compared to knits finished with the exhaust method of application. Further, the group of respondents rated that the 5th washed samples had the greater aroma intensity in both the methods than the other samples. Thus, the vetiver microencapsulated organic cotton knits are free from hazardous chemicals and have multi-functional properties that can be suitable for medical and healthcare textiles.
Abstract: The current study aims to investigate the effect of fillers with different geometries and sizes on the interfacial shear properties of PA6 composites with de-sized carbon fiber. The fillers which have been investigated are namely; nano-layer silicates (nanoclay), sub-micro aluminum titanium (ALTi) particles, and multiwall carbon nanotube (MWCNT). By means of X-ray photoelectron spectroscopy (XPS), epoxide group which defined as a sizing agent, has been removed. Sizing removal can reduce the acid parameter of carbon fibers surface promoting bonding strength at the fiber/matrix interface which is a desirable property for the carbon fiber composites. Microdroplet test showed that the interfacial shear strength (IFSS) has been enhanced with the addition of 10wt% ALTi by about 23% comparing with neat PA6. However, with including other types of fillers into PA6, the results did not show enhancement of IFSS.
Abstract: Soy polyol obtained from hydroxylation of soy
epoxide with ethylene glycol were prepared as pre-polyurethane. The
two step process method were applied in the polyurethane synthesis.
The blending of soy polyol with synthetic polyol then simultaneously
carried out to TDI (2,4): MDI (4,4-) (80:20), blowing agent, and
surfactant. Ethylene glycol were not taking part in the polyurethane
synthesis. The inclusion of ethylene glycol were used as a control.
Characterization of polyurethane foam through impact resillience,
indentation deflection, and density can visualize the polyurethane
classifications.
Abstract: The epoxidation of soybean oil at temperature of 600C
was provided the best result in terms of attaching the –OH
functionality. Temperatures below and above 600C it is likely the
attaching reaction did not proceed sufficiently fast. The considerable
yield below 40%, implies the oil is not completely converted, it is not
possible by conventional methods, because the epoxide decomposes
at the temperature required. The objective of this work was the
development of catalyst toward the conversion of epoxide and polyol
with reaction temperature at 50,60, and 700C. The effect of different
type of catalyst were studied, the effect of alcohols with different
molecular configuration was determined which leads to selective
addition of alcohols to the epoxide oils.
Abstract: Polyurethane foam (PUF) were prepared by
reacting polyols synthesized from soy-oil into mixture of 2,4-
Toluene diisocyanate (TDI) with 4,4--Methylene Diamine
Isocyanate (MDI) with ratio of 70:30. The polyols obtained
via esterification reaction were categorize into different
temperature of reaction and by used of varied concentration
of phosphoric acid catalyst. The purpose of catalysts is to
shifting selectivity to a desired and value added of product.
The effect of stoichiometric balance (molar ratio of
epoxide/ethylene glycol) to the concentration of the catalyst
on the final properties was evaluated.