Abstract: Martensitic texture-phase transition in Selective Laser Melting (SLM) Ti-6Al-4V (ELI) alloys was found. Electron Backscatter Diffraction (EBSD) analysis showed the initial cubic beta < 100 > (001) BCC texture. Such kind of texture is observed in BCC metals with flat rolling texture when axis is in the direction of rolling and the texture plane coincides with the plane of rolling. It was found that the texture of the parent BCC beta-phase determined the texture of low-temperature HCP alpha-phase limited the choice of its orientation variants. The {10-12} < -1011 > twinning system in titanium alloys after SLM was determined. Analysis of the oxygen contamination in SLM alloys was done. Comparison of the obtained results with the conventional titanium alloys is also provided.
Abstract: The commercially available titanium alloy, Ti-6Al-4V, was oxynitrided in the deoxygenated nitrogen gas at high temperatures followed by cooling in oxygen-containing nitrogen in order to analyze the influence of oxynitriding parameters on the phase modification, hardness, and the microstructural evolution of the oxynitrided coating. The surface microhardness of the oxynitrided alloy increased due to the strengthening effect of the formed titanium oxynitrides, TiNxOy. The maximum microhardness was obtained, when TiNxOy had near equiatomic composition of nitrogen and oxygen. It could be attained under the optimum oxygen partial pressure and temperature-time condition.
Abstract: Ti6Al4V alloy is highly used in the automotive and
aerospace industry due to its good machining characteristics. Micro
EDM drilling is commonly used to drill micro hole on extremely hard
material with very high depth to diameter ratio. In this study, the
parameters of micro-electrical discharge machining (EDM) in drilling
of Ti6Al4V alloy is optimized for higher machining accuracy with
less hole-dilation and hole taper ratio. The micro-EDM machining
parameters includes, peak current and pulse on time. Fuzzy analysis
was developed to evaluate the machining accuracy. The analysis
shows that hole-dilation and hole-taper ratio are increased with the
increasing of peak current and pulse on time. However, the surface
quality deteriorates as the peak current and pulse on time increase.
The combination that gives the optimum result for hole dilation is
medium peak current and short pulse on time. Meanwhile, the
optimum result for hole taper ratio is low peak current and short pulse
on time.
Abstract: Asymmetric incremental sheet forming (AISF) could significantly reduce costs incurred by the fabrication of complex industrial components with a minimal environmental impact. The AISF experiments were carried out on commercially pure titanium (Ti-Gr2), Timetal (15-3-3-3) alloy, and Ti-6Al-4V (Ti-Gr5) alloy. A special testing geometry was used to characterize the titanium alloys properties from the point of view of the forming zone and titanium structure effect. The structure and properties of the materials were assessed by means of metallographic analyses and microhardness measurements.The highest differences in the parameters assessed as a function of the sampling zone were observed in the case of alpha-phase Ti-Gr2at the expense of the most substantial sheet thinning occurrence. A springback causes a smaller stored deformation in Timetal (β alloy) resulting in less pronounced microstructure refinement and microhardness increase. Ti-6Al-4V alloy exhibited early failure due to its poor formability at ambient temperature.
Abstract: Minimum Quantity Lubrication (MQL) technique
obtained a significant attention in machining processes to reduce
environmental loads caused by usage of conventional cutting fluids.
Recently nanofluids are finding an extensive application in the field
of mechanical engineering because of their superior lubrication and
heat dissipation characteristics. This paper investigates the use of a
nanofluid under MQL mode to improve grinding characteristics of
Ti-6Al-4V alloy. Taguchi-s experimental design technique has been
used in the present investigation and a second order model has been
established to predict grinding forces and surface roughness.
Different concentrations of water based Al2O3 nanofluids were
applied in the grinding operation through MQL setup developed in
house and the results have been compared with those of conventional
coolant and pure water. Experimental results showed that grinding
forces reduced significantly when nano cutting fluid was used even at
low concentration of the nano particles and surface finish has been
found to improve with higher concentration of the nano particles.
Abstract: Ti-6Al-4V alloy has demonstrated a high strength to
weight ratio as well as good properties at high temperature. The
successful application of the alloy in some important areas depends
on suitable joining techniques. Friction welding has many
advantageous features to be chosen for joining Titanium alloys. The
present work investigates the feasibility of producing similar metal
joints of this Titanium alloy by rotary friction welding method. The
joints are produced at three different speeds and the performances of
the welded joints are evaluated by conducting microstructure studies,
Vickers Hardness and tensile tests at the joints. It is found that the
weld joints produced are sound and the ductile fractures in the tensile
weld specimens occur at locations away from the welded joints. It is
also found that a rotational speed of 1500 RPM can produce a very
good weld, with other parameters kept constant.
Abstract: This paper reports the fatigue crack growth behaviour
of gas tungsten arc, electron beam and laser beam welded Ti-6Al-4V
titanium alloy. Centre cracked tensile specimens were prepared to
evaluate the fatigue crack growth behaviour. A 100kN servo
hydraulic controlled fatigue testing machine was used under constant
amplitude uniaxial tensile load (stress ratio of 0.1 and frequency of
10 Hz). Crack growth curves were plotted and crack growth
parameters (exponent and intercept) were evaluated. Critical and
threshold stress intensity factor ranges were also evaluated. Fatigue
crack growth behaviour of welds was correlated with mechanical
properties and microstructural characteristics of welds. Of the three
joints, the joint fabricated by laser beam welding exhibited higher
fatigue crack growth resistance due to the presence of fine lamellar
microstructure in the weld metal.