Abstract: Roller-compacted concrete pavement (RCCP), an environmental friendly pavement of which load carry capacity benefitted from both hydration and aggregate interlock from roller compacting, demonstrated a superb structural performance for a relatively small amount of water and cement content. Even though an excellent structural performance can be secured, it is required to investigate roller-compacted concrete (RCC) under environmental loading and its long-term durability under critical conditions. In order to secure long-term durability, an appropriate internal air-void structure is required for this concrete. In this study, a method for improving the long-term durability of RCCP is suggested by analyzing the internal air-void structure and corresponding durability of RCC. The method of improving the long-term durability involves measurements of air content, air voids, and air-spacing factors in RCC that experiences changes in terms of type of air-entraining agent and its usage amount. This test is conducted according to the testing criteria in ASTM C 457, 672, and KS F 2456. It was found that the freezing-thawing and scaling resistances of RCC without any chemical admixture was quite low. Interestingly, an improvement of freezing-thawing and scaling resistances was observed for RCC with appropriate the air entraining (AE) agent content; Relative dynamic elastic modulus was found to be more than 80% for those mixtures. In RCC with AE agent mixtures, large amount of air was distributed within a range of 2% to 3%, and an air void spacing factor ranging between 200 and 300 μm (close to 250 μm, recommended by PCA) was secured. The long-term durability of RCC has a direct relationship with air-void spacing factor, and thus it can only be secured by ensuring the air void spacing factor through the inclusion of the AE in the mixture.
Abstract: A number of studies have been conducted recently to
investigate the influence of randomly oriented fibers on some
engineering properties of cohesive and cohesionless soils. However,
few studies have been carried out on freezing-thawing behavior of
fine-grained soils modified with discrete fiber inclusions and additive
materials. This experimental study was performed to investigate the
effect of randomly distributed polypropylene fibers (PP) and some
additive materials [e.g.., borogypsum (BG), fly ash (FA) and cement
(C)] on freezing-thawing durability (mass losses) of a fine-grained
soil for 6, 12, and 18 cycles. The Taguchi method was applied to the
experiments and a standard L9 orthogonal array (OA) with four
factors and three levels were chosen. A series of freezing-thawing
tests were conducted on each specimen. 0-20% BG, 0-20% FA, 0-
0.25% PP and 0-3% of C by total dry weight of mixture were used in
the preparation of specimens. Experimental results showed that the
most effective materials for the freezing-thawing durability (mass
losses) of the samples were borogypsum and fly ash. The values of
mass losses for 6, 12 and 18 cycles in optimum conditions were
16.1%, 5.1% and 3.6%, respectively.
Abstract: The using of waste materials in the construction
industry can reduce the dependence on the natural aggregates which
are going at the end to deplete. The glass waste is generated in a huge
amount which can make one of its disposals in concrete industry
effective not only as a green solution but also as an advantage to
enhance the performance of mechanical properties and durability of
concrete. This article reports the performance of concrete specimens
containing different percentages of milled glass waste as a partial
replacement of cement (Powder), when they are subject to cycles of
freezing and thawing. The tests were conducted on 75-mm cubes and
75 x 75 x 300-mm prisms. Compressive strength based on laboratory
testing and non-destructive ultrasonic pulse velocity test were
performed during the action of freezing-thawing cycles (F/T). The
results revealed that the incorporation of glass waste in concrete
mixtures is not only feasible but also showed generally better strength
and durability performance than control concrete mixture. It may be
said that the recycling of waste glass in concrete mixes is not only a
disposal way, but also it can be an exploitation in concrete industry.