Abstract: Freeze-thaw cycles are one of the greatest threats to concrete durability. Lately, protection against this threat excites scientists’ attention. Air-entraining admixtures have been widely used to produce freeze-thaw resistant at concretes. The use of air-entraining agents (AEAs) enhances not only freeze-thaw endurance but also the properties of fresh concrete such as segregation, bleeding and flow ability. This paper examines the effects of air-entraining on compressive strength of concrete. Air-entraining is used between 0.05% and 0.4% by weight of cement. One control and four fiber reinforced concrete mixes are prepared and three specimens are tested for each mix. It is concluded from the test results that when air entraining is increased the compressive strength of concrete reduces for all mixes with AEAs.
Abstract: The using of waste materials in the construction
industry can reduce the dependence on the natural aggregates which
are going at the end to deplete. The glass waste is generated in a huge
amount which can make one of its disposals in concrete industry
effective not only as a green solution but also as an advantage to
enhance the performance of mechanical properties and durability of
concrete. This article reports the performance of concrete specimens
containing different percentages of milled glass waste as a partial
replacement of cement (Powder), when they are subject to cycles of
freezing and thawing. The tests were conducted on 75-mm cubes and
75 x 75 x 300-mm prisms. Compressive strength based on laboratory
testing and non-destructive ultrasonic pulse velocity test were
performed during the action of freezing-thawing cycles (F/T). The
results revealed that the incorporation of glass waste in concrete
mixtures is not only feasible but also showed generally better strength
and durability performance than control concrete mixture. It may be
said that the recycling of waste glass in concrete mixes is not only a
disposal way, but also it can be an exploitation in concrete industry.
Abstract: The first and basic cause of the failure of concrete is repeated freezing (thawing) of moisture contained in the pores, microcracks, and cavities of the concrete. On transition to ice, water existing in the free state in cracks increases in volume, expanding the recess in which freezing occurs. A reduction in strength below the initial value is to be expected and further cycle of freezing and thawing have a further marked effect. By using some experimental parameters like nuclear magnetic resonance variation (NMR), enthalpy-temperature (or heat capacity) variation, we can resolve between the various water states and their effect on concrete properties during cooling through the freezing transition temperature range. The main objective of this paper is to describe the principal type of water responsible for the reduction in strength and structural damage (frost damage) of concrete following repeated freeze –thaw cycles. Some experimental work was carried out at the institute of cryogenics to determine what happens to water in concrete during the freezing transition.