Abstract: The using of waste materials in the construction
industry can reduce the dependence on the natural aggregates which
are going at the end to deplete. The glass waste is generated in a huge
amount which can make one of its disposals in concrete industry
effective not only as a green solution but also as an advantage to
enhance the performance of mechanical properties and durability of
concrete. This article reports the performance of concrete specimens
containing different percentages of milled glass waste as a partial
replacement of cement (Powder), when they are subject to cycles of
freezing and thawing. The tests were conducted on 75-mm cubes and
75 x 75 x 300-mm prisms. Compressive strength based on laboratory
testing and non-destructive ultrasonic pulse velocity test were
performed during the action of freezing-thawing cycles (F/T). The
results revealed that the incorporation of glass waste in concrete
mixtures is not only feasible but also showed generally better strength
and durability performance than control concrete mixture. It may be
said that the recycling of waste glass in concrete mixes is not only a
disposal way, but also it can be an exploitation in concrete industry.
Abstract: Liners are made to protect the groundwater table from
the infiltration of leachate which normally carries different kinds of
toxic materials from landfills. Although these liners are engineered to
last for long period of time; unfortunately these liners fail; therefore,
toxic materials pass to groundwater. This paper focuses on the
changes of the hydraulic conductivity of a sand-bentonite liner due to
the infiltration of biofuel and ethanol fuel. Series of laboratory tests
were conducted in 20-cm-high PVC columns. Several compositions
of sand-bentonite liners were tested: 95% sand: 5% bentonite; 90%
sand: 10% bentonite; and 100% sand (passed mesh #40). The
columns were subjected to extreme pressures of 40 kPa, and 100 kPa
to evaluate the transport of alternative fuels (biofuel and ethanol
fuel). For comparative studies, similar tests were carried out using
water. Results showed that hydraulic conductivity increased due to
the infiltration of alternative fuels through the liners. Accordingly,
the increase in the hydraulic conductivity showed significant
dependency on the type of liner mixture and the characteristics of the
liquid. The hydraulic conductivity of a liner (subjected to biofuel
infiltration) consisting of 5% bentonite: 95% sand under pressure of
40 kPa and 100 kPa had increased by one fold. In addition, the
hydraulic conductivity of a liner consisting of 10% bentonite: 90%
sand under pressure of 40 kPa and 100 kPa and infiltrated by biofuel
had increased by three folds. On the other hand, the results obtained
by water infiltration under 40 kPa showed lower hydraulic
conductivities of 1.50×10-5 and 1.37×10-9 cm/s for 5% bentonite:
95% sand, and 10% bentonite: 90% sand, respectively. Similarly,
under 100 kPa, the hydraulic conductivities were 2.30×10-5 and
1.90×10-9 cm/s for 5% bentonite: 95% sand, and 10% bentonite: 90%
sand, respectively.