Abstract: Solid Oxide Fuel Cell (SOFC) is a promising solution for the energy resources leakage. Ferritic stainless steel becomes a suitable candidate for the SOFCs interconnects due to the recent advancements. Different steel alloys were designed to satisfy the needed characteristics in SOFCs interconnect as conductivity, thermal expansion and corrosion resistance. Refractory elements were used as alloying elements to satisfy the needed properties. The oxidation behaviour of the developed alloys was studied where the samples were heated for long time period at the maximum operating temperature to simulate the real working conditions. The formed scale and oxidized surface were investigated by SEM. Microstructure examination was carried out for some selected steel grades. The effect of alloying elements on the behaviour of the proposed interconnects material and the performance during the working conditions of the cells are explored and discussed. Refractory metals alloying of chromium steel seems to satisfy the needed characteristics in metallic interconnects.
Abstract: In this study, thermal fatigue properties of 400 series
ferritic stainless steels have been evaluated in the temperature ranges
of 200-800oC and 200-900oC. Systematic methods for control of
temperatures within the predetermined range and measurement of load
applied to specimens as a function of temperature during thermal
cycles have been established. Thermal fatigue tests were conducted
under fully constrained condition, where both ends of specimens were
completely fixed. It has been revealed that load relaxation behavior at
the temperatures of thermal cycle was closely related with the thermal
fatigue property. Thermal fatigue resistance of 430J1L stainless steel
is found to be superior to the other steels.
Abstract: Protective coatings that resist oxide scale growth and
decrease chromium evaporation are necessary to make stainless steel
interconnect materials for long-term durable operation of solid oxide
fuel cells (SOFCs). In this study a layer of cobalt was electroplated
on the surface of AISI 441 ferritic stainless steel which is used in
solid oxide fuel cells for interconnect applications. The oxidation
behavior of coated substrates was studied as a function of time at
operating conditions of SOFCs. Cyclic oxidation has been also tested
at 800ÂșC for 100 cycles. Cobalt coating during isothermal oxidation
caused to the oxide growth resistance by limiting the outward
diffusion of Cr cation and the inward diffusion of oxygen anion.
Results of cyclic oxidation exhibited that coated substrates
demonstrate an excellent resistance against the spallation and
cracking.