Abstract: The modified Arcan fixture was used in order to
investigate the mixed mode fracture properties of high strength steel
butt weld through experimental and numerical analysis. The fixture
consisted of a central section with "butterfly-shaped" specimen that
had central crack. The specimens were under pure mode I (opening),
pure mode II (shearing) and all in plane mixed mode loading angles
starting from 0 to 90 degrees. The geometric calibration factors were
calculated with the aid of finite element analysis for various loading
mode and different crack length (0.45≤ a/w ≤0.55) and the critical
fracture loads obtained experimentally. The critical fracture
toughness (KIC & KIIC) estimated with experimental and numerical
analysis under mixed mode loading conditions.
Abstract: Fatigue tests of specimen-s with numerous holes are
presented. The tests were made up till fatigue cracks have been
created on both sides of the hole. Their extension was stopping with
pressed plastic deformation at the mouth of the detected crack. It is
shown that the moments of occurrence of cracks on holes are
stochastically dependent. This dependence has positive and negative
correlation relations. Shown that the positive correlation is formed
across of the applied force, while negative one – along it. The
negative relationship extends over a greater distance. The
mathematical model of dependence area formation is represented as
well as the estimating of model parameters. The positive correlation
of fatigue cracks origination can be considered as an extension of one
main crack. With negative correlation the first crack locates the place
of its origin, leading to the appearance of multiple cracks; do not
merge with each other.
Abstract: The kinetics of palm oil catalytic cracking over
aluminum containing mesoporous silica Al-MCM-41 (5% Al) was
investigated in a batch autoclave reactor at the temperatures range of
573 – 673 K. The catalyst was prepared by using sol-gel technique
and has been characterized by nitrogen adsorption and x-ray
diffraction methods. Surface area of 1276 m2/g with average pore
diameter of 2.54 nm and pore volume of 0.811 cm3/g was obtained.
The experimental catalytic cracking runs were conducted using 50 g
of oil and 1 g of catalyst. The reaction pressure was recorded at
different time intervals and the data were analyzed using Levenberg-
Marquardt (LM) algorithm using polymath software. The results
show that the reaction order was found to be -1.5 and activation
energy of 3200 J/gmol.
Abstract: The National Bridge Inventory (NBI) includes more
than 600,000 bridges within the United States of America.
Prestressed concrete girder bridges represent one of the most widely
used bridge systems. The majority of these girder bridges were
constructed using 0.5 and 0.6 inch diameter strands. The main
impediments to using larger strand diameters are: 1) lack of prestress
bed capacities, 2) lack of structural knowledge regarding the transfer
and development length of larger strands, and 3) the possibility of
developing wider end zone cracks upon strand release.
This paper presents a study about using 0.7 inch strands in girder
fabrication. Transfer and development length were evaluated, and
girders were fabricated using 0.7 inch strands at different spacings.
Results showed that 0.7 inch strands can be used at 2.0 inch spacing
without violating the AASHTO LRFD Specifications, while attaining
superior performance in shear and flexure.
Abstract: This work presents the mixed-mode II/III prestressed split-cantilever beam specimen for the fracture testing of composite materials. In accordance with the concept of prestressed composite beams one of the two fracture modes is provided by the prestressed state of the specimen, and the other one is increased up to fracture initiation by using a testing machine. The novel beam-like specimen is able to provide any combination of the mode-II and mode-III energy release rates. A simple closed-form solution is developed using beam theory as a data reduction scheme and for the calculation of the energy release rates in the new configuration. The applicability and the limitations of the novel fracture mechanical test are demonstrated using unidirectional glass/polyester composite specimens. If only crack propagation onset is involved then the mixed-mode beam specimen can be used to obtain the fracture criterion of transparent composite materials in the GII - GIII plane in a relatively simple way.
Abstract: Magnesium alloys have gained increased attention in recent years in automotive, electronics, and medical industry. This because of magnesium alloys have better properties than aluminum alloys and steels in respects of their low density and high strength to weight ratio. However, the main problems of magnesium alloy welding are the crack formation and the appearance of porosity during the solidification. This paper proposes a unique technique to weld two thin sheets of AZ31B magnesium alloy using a paste containing Ag nanoparticles. The paste containing Ag nanoparticles of 5 nm in average diameter and an organic solvent was used to coat the surface of AZ31B thin sheet. The coated sheet was heated at 100 °C for 60 s to evaporate the solvent. The dried sheet was set as a lower AZ31B sheet on the jig, and then lap fillet welding was carried out by using a pulsed Nd:YAG laser in a closed box filled with argon gas. The characteristics of the microstructure and the corrosion behavior of the joints were analyzed by opticalmicroscopy (OM), energy dispersive spectrometry (EDS), electron probe micro-analyzer (EPMA), scanning electron microscopy (SEM), and immersion corrosion test. The experimental results show that the wrought AZ31B magnesium alloy can be joined successfully using Ag nanoparticles. Ag nanoparticles insert promote grain refinement, narrower the HAZ width and wider bond width compared to weld without and insert. Corrosion rate of welded AZ31B with Ag nanoparticles reduced up to 44 % compared to base metal. The improvement of corrosion resistance of welded AZ31B with Ag nanoparticles due to finer grains and large grain boundaries area which consist of high Al content. β-phase Mg17Al12 could serve as effective barrier and suppressed further propagation of corrosion. Furthermore, Ag distribution in fusion zone provide much more finer grains and may stabilize the magnesium solid solution making it less soluble or less anodic in aqueous
Abstract: The main objectives of this study are to inspect and
identify any damage of jaimusi highway prestressed concrete bridge
after repair and strengthening of damaged structural members and to
evaluate the performance of the bridge structural members by
adopting static load test. Inspection program after repair and
strengthening includes identifying and evaluating the structural
members of bridge such as T-shape cantilever structure, hanging
beams, corbels, external tendons, anchor beams, sticking steel plate,
and piers. The results of inspection show that the overall state of the
bridge structural member after repair and strengthening is good. The
results of rebound test of concrete strength show that the average
strength of concrete is 46.31Mpa. Whereas, the average value of
concrete strength of anchor beam is 49.82Mpa. According to the
results of static load test, the experimental values are less than
theoretical values of internal forces, deflection, and strain, indicating
that the stiffness of the experimental structure, overall deformation
and integrity satisfy the designed standard and the working
performance is good, and the undertaking capacity has a certain
surplus. There is not visible change in the length and width of cracks
and there are not new cracks under experimental load.
Abstract: In this paper the fatigue crack initiation location of double shear lap joints, treated by interference fit and bolt clamping, have been investigated both experimentally and numerically. To do so, using the fracture section of available fatigue tested specimens of interference fitted and torque tightened Aluminum 2024-T3 plates, the crack initiation location was determined. The stress distribution attained from the finite element analysis was used to help explain the results observed in the experimental tests. The results showed that the fatigue crack initiation location changes from top and mid plane at the hole edge to somewhere far from the hole edge (stress concentration region) in different combination of clamping force, interference fit size and applied cyclic load ranges. It is worth mentioning that the fatigue crack initiation location affects the fatigue life of the specimens too.
Abstract: The dominant judgment for earthquake damaged reinforced concrete (RC) structures is to rebuild them with the new ones. Consequently, this paper estimates if there is chance to repair earthquake RC beams and obtain economical contribution to modern day society. Therefore, the totally damaged (damaged in shear under cyclic load) reinforced concrete (RC) beams repaired and strengthened by externally bonded carbon fibre reinforced polymer (CFRP) strips in this study. Four specimens, apart from the reference beam, were separated into two distinct groups. Two experimental beams in the first group primarily tested up to failure then appropriately repaired and strengthened with CFRP strips. Two undamaged specimens from the second group were not repaired but strengthened by the identical strengthening scheme as the first group for comparison. This study studies whether earthquake damaged RC beams that have been repaired and strengthened will validate similar strength and behavior to equally strengthened, undamaged RC beams. Accordingly, a strength correspondence according to strengthened specimens was acquired for the repaired and strengthened specimens. Test results confirmed that repair and strengthening, which were estimated in the experimental program, were effective for the specimens with the cracking patterns considered in the experimental program.
Abstract: Stainless steel has been employed in many
engineering applications ranging from pharmaceutical equipment to
piping in the nuclear reactors and storage to chemical products. In
this attempt, simulation of fatigue crack growth based on
experimental results of austenitic stainless steel 304L was presented
using AFGROW code when NASGRO mode laws adopted. Double
through crack at hole specimen is used in this investigation under
constant amplitude loading. Effect of mean stress is highlighted.
Results show that fatigue crack growth rate (FCGR) and fatigue life
were affected by maximum applied load and dimension of hole. An
equivalent of Paris law for this material was estimated.
Abstract: Industrial radiography is a famous technique for the identification and evaluation of discontinuities, or defects, such as cracks, porosity and foreign inclusions found in welded joints. Although this technique has been well developed, improving both the inspection process and operating time, it does suffer from several drawbacks. The poor quality of radiographic images is due to the physical nature of radiography as well as small size of the defects and their poor orientation relatively to the size and thickness of the evaluated parts. Digital image processing techniques allow the interpretation of the image to be automated, avoiding the presence of human operators making the inspection system more reliable, reproducible and faster. This paper describes our attempt to develop and implement digital image processing algorithms for the purpose of automatic defect detection in radiographic images. Because of the complex nature of the considered images, and in order that the detected defect region represents the most accurately possible the real defect, the choice of global and local preprocessing and segmentation methods must be appropriated.
Abstract: Non-saturated soils that while saturation greatly
decrease their volume, have sudden settlement due to increasing
humidity, fracture and structural crack are called loess soils. Whereas
importance of civil projects including: dams, canals and
constructions bearing this type of soil and thereof problems, it is
required for carrying out more research and study in relation to loess
soils. This research studies shear strength parameters by using
grading test, Atterberg limit, compression, direct shear and
consolidation and then effect of using cement and lime additives on
stability of loess soils is studied. In related tests, lime and cement are
separately added to mixed ratios under different percentages of soil
and for different times the stabilized samples are processed and effect
of aforesaid additives on shear strength parameters of soil is studied.
Results show that upon passing time the effect of additives and
collapsible potential is greatly decreased and upon increasing
percentage of cement and lime the maximum dry density is
decreased; however, optimum humidity is increased. In addition,
liquid limit and plastic index is decreased; however, plastic index
limit is increased. It is to be noted that results of direct shear test
reveal increasing shear strength of soil due to increasing cohesion
parameter and soil friction angle.
Abstract: Drying characteristics of rough rice (variety of lenjan) with an initial moisture content of 25% dry basis (db) was studied in a hot air dryer assisted by infrared heating. Three arrival air temperatures (30, 40 and 500C) and four infrared radiation intensities (0, 0.2 , 0.4 and 0.6 W/cm2) and three arrival air speeds (0.1, 0.15 and 0.2 m.s-1) were studied. Bending strength of brown rice kernel, percentage of cracked kernels and time of drying were measured and evaluated. The results showed that increasing the drying arrival air temperature and radiation intensity of infrared resulted decrease in drying time. High bending strength and low percentage of cracked kernel was obtained when paddy was dried by hot air assisted infrared dryer. Between this factors and their interactive effect were a significant difference (p
Abstract: The present paper reports results of an experimental
program conducted to study performance of fly ash based
geopolymer pastes at elevated temperature. Three series of
geopolymer pastes differing in Na2O content (8.5%, 10% and 11.5%)
were manufactured by activating low calcium fly ash with a mixture
of sodium hydroxide and sodium silicate solution. The paste
specimens were subjected to temperatures as high as 900oC and the
behaviour at elevated temperatures were investigated on the basis of
physical appearance, weight losses, residual strength, shrinkage
measurements and sorptivity tests at different temperatures. Scanning
electron microscopy along with EDX and XRD tests were also
conducted to examine microstructure and mineralogical changes
during the thermal exposure. Specimens which were initially grey
turned reddish accompanied by appearance of small cracks as the
temperature increased to 900oC. Loss of weight was more in
specimens manufactured with highest Na2O content. Geopolymer
paste specimen containing minimum Na2O performed better than
those with higher Na2O content in terms of residual compressive
strength.
Abstract: In this paper, the strength of a stabilizer is determined when the static and fatigue multiaxial loading are applied. Stabilizer is a part of suspension system in the heavy truck for stabilizing the cabin against the vibration of the road which composes of a thin-walled tube joined to a forge component by fillet weld. The component is loaded by non proportional random sequence of torsion and bending. Residual stress of welding process is considered here for static loading. This static loading with road irregularities are applied in this study as fatigue case that can affected in the fillet welded area of this part. The stresses in the welded structure are calculated using FEA. In addition, the fatigue with multi axial loading in the fillet weld is also investigated and the critical zone of the stabilizer is specified and presented by graphs. Residual stresses that have been resulted by the thermal forces are considered in FEA. Force increasing is the element of finding the critical point of the component.
Abstract: This paper presented the results of an experimental
investigation into the axial fatigue behavior of a 5086 aluminum
alloy which have several notch-aspect ratios a0/c0 and notch
thickness ratio a/t with semi-elliptical surface cracks. Tests were
conducted in la b air for stress levels of 50 % of their yield
strength. Experiments were carried out for various notch to
thickness ratios. Crack growth rates of test specimens both in
surface and depth directions were determined by using die
penetration method. Fuzzy Logic method was used to predict the
deep direction crack growth because the dept of the crack is
considerably difficult to measure.
Abstract: In this study the mixed mode fracture mechanics
parameters were investigated for high tensile steel butt welded joint
based on modified Arcan test and finite element analysis was used to
evaluate the effect of crack length on fracture criterion. The nondimensional
stress intensity factors, strain energy release rates and Jintegral
energy on crack tip were obtained for various in-plane
loading combinations on Arcan specimen starting from pure mode-I
to pure mode-II loading conditions. The specimen and apparatus were
modeled by finite element method and analyzed under various
loading angles (between 0 to 90 degrees with 15 degree interval) to
simulate the pure mode-I, II and mixed mode fracture. Since the
analytical results are independent from elasticity modules for
isotropic materials, therefore the results in elastic fields can be used
for Arcan specimens. The main objective of this study was to
evaluate the geometric calibration factors for modified Arcan test
specimen in order to obtain fracture toughness under mixed mode
loading conditions.
Abstract: It is necessary to evaluate the bridges conditions and
strengthen bridges or parts of them. The reinforcement necessary due
to some reasons can be summarized as: First, a changing in use of
bridge could produce internal forces in a part of structural which
exceed the existing cross-sectional capacity. Second, bridges may
also need reinforcement because damage due to external factors
which reduced the cross-sectional resistance to external loads. One of
other factors could listed here its misdesign in some details, like
safety of bridge or part of its.This article identify the design demands
of Qing Shan bridge located in is in Heilongjiang Province He gang -
Nen Jiang Road 303 provincial highway, Wudalianchi area, China, is
an important bridge in the urban areas. The investigation program
was include the observation and evaluate the damage in T- section
concrete beams , prestressed concrete box girder bridges section in
additional evaluate the whole state of bridge includes the pier ,
abutments , bridge decks, wings , bearing and capping beam, joints,
........etc. The test results show that the bridges in general structural
condition are good. T beam span No 10 were observed, crack
extended upward along the ribbed T beam, and continue to the T
beam flange. Crack width varying between 0.1mm to 0.4mm, the
maximum about 0.4mm. The bridge needs to be improved flexural
bending strength especially at for T beam section.
Abstract: Solidification cracking and hydrogen cracking are some defects generated in the fusion welding of ultrahigh carbon steels. However, friction stir welding (FSW) of such steels, being a solid-state technique, has been demonstrated to alleviate such problems encountered in traditional welding. FSW include different process parameters that must be carefully defined prior processing. These parameters included but not restricted to: tool feed, tool RPM, tool geometry, tool tilt angle. These parameters form a key factor behind avoiding warm holes and voids behind the tool and in achieving a defect-free weld. More importantly, these parameters directly affect the microstructure of the weld and hence the final mechanical properties of weld. For that, 3D finite element (FE) thermo-mechanical model was developed using DEFORM 3D to simulate FSW of carbon steel. At points of interest in the joint, tracking is done for history of critical state variables such as temperature, stresses, and strain rates. Typical results found include the ability to simulate different weld zones. Simulations predictions were successfully compared to experimental FSW tests. It is believed that such a numerical model can be used to optimize FSW processing parameters to favor desirable defect free weld with better mechanical properties.
Abstract: The objective of this work is to study the influence of the properties of the substrate on the retrofit (thin repair) of damaged concrete elements, with the SCC. Fluidity, principal characteristic of the SCC, would enable it to cover and adhere to the concrete to be repaired. Two aspects of repair are considered, the bond (Adhesion) and the tensile strength and the cracking. The investigation is experimental; It was conducted over test specimens made up of ordinary concrete prepared and hardened in advance (the material to be repaired) over which a self compacting concrete layer is cast. Three alternatives of SC concrete and one ordinary concrete (comparison) were tested. It appears that the self-compacting concrete constitutes a good material for repairing. It follows perfectly the surfaces- forms to be repaired and allows a perfect bond. Fracture tests made on specimens of self-compacting concrete show a brittle behaviour. However when a small percentage of fibres is added, the resistance to cracking is very much improve.