Abstract: In this investigation variation of cyclic loading effect on fatigue crack growth is the studied. This study is performed on 2024 T351 and 7050-T74 aluminum alloys, used in aeronautical structures. The propagation model used in this study is NASGRO model. In constant amplitude loading (CA), effect of stress ratio has been investigated. Fatigue life and fatigue crack growth rate were affected by this factor. Results showed an increasing in fatigue crack growth rates (FCGRs) with increasing stress ratio. Variable amplitude loading (VAL) can take many forms i.e. with a single overload, overload band… etc. The shape of these loads affects strongly the fracture life and FCGRs. The application of a single overload (ORL) decrease the FCGR and increase the delay crack length caused by the formation of a larger plastic zone compared to the plastic zone due without VAL. The fatigue behavior of the both material under single overload has been compared.
Abstract: In this investigation an empirical study was made on fatigue crack initiation on 7075 T6 and 7075 T71 Al-alloys under constant amplitude loading. In initiation stage, local strain approach at the notch was applied. Single Edge Notch Tensile specimen with semi circular notch is used. Based on experimental results, effect of mean stress, is highlights on fatigue initiation life. Results show that fatigue life initiation is affected by notch geometry and mean stress.
Abstract: In this paper fatigue crack initiation and propagation in notched plate under constant amplitude loading through tensile residual stress field of 2024 T351 Al-alloy plate were investigated. Residual stress field was generated by plastic deformation using finite element method (FEM) where isotropic hardening in Von Mises model was applied. Simulation of fatigue behavior was made on AFGROW code. It was shown that the fatigue crack initiation and propagation were affected by level of residual stress filed. In this investigation, the presence of tensile residual stresses at notch (hole) reduces considerably the total fatigue life. It was shown that the decreasing in stress reduces the fatigue crack growth rates.
Abstract: In this paper fatigue crack growth behavior of
aeronautical aluminum alloy 2024 T351 was studied. Effects of
various loading and geometrical parameters are studied such as stress
ratio, amplitude loading, etc. The fatigue crack growth with constant
amplitude is studied using the AFGROW code when NASGRO
model is used. The effect of the stress ratio is highlighted, where one
notices a shift of the curves of crack growth. The comparative study
between two orientations L-T and T-L on fatigue behavior are
presented and shows the variation on the fatigue life. L-T orientation
presents a good fatigue crack growth resistance. Effects of crack
closure are shown in Paris domain and that no crack closure
phenomenons are present at high stress intensity factor.
Abstract: This study reports an empirical investigation of
fatigue crack initiation and propagation in 2024 T351 aluminium
alloy using constant amplitude loading. In initiation stage, local
strain approach at the notch was used and in stable propagation stage
NASGRO model was applied.
In this investigation, the flat plate of double through crack at hole
is used. Based on experimental results (AFGROW Database), effect
of stress ratio, R, is highlights on fatigue initiation life (FIL) and
fatigue crack growth rate (FCGR). The increasing of dimension of
hole characterizing the notch effect decrease the fatigue life.
Abstract: The knowledge of the nature of loading is very
important in order to hold account on the total behavior such as
vibration, shock, fatigue, etc. Fatigue present 90% of failure when
loadings fatigues are very complex. In this paper a study of double
through crack at hole for plate subjected to fatigue loading is
presented. Various modes loading are studied where the applied load
is the same one. The fatigue life is given where the effect of stress
ratio is highlighted. This work is conducted on aluminum alloy 2024
T351 used for much aerospace and aeronautics applications. The
fatigue crack growth behavior with constant amplitude is studied
using the AFGROW code when Forman model is applied. The
fatigue crack growth rate and fatigue life for different loading modes
are compared with variation of others geometrical parameter such as
thickness and dimensions of notch hole.
Abstract: Stainless steel has been employed in many
engineering applications ranging from pharmaceutical equipment to
piping in the nuclear reactors and storage to chemical products. In
this attempt, simulation of fatigue crack growth based on
experimental results of austenitic stainless steel 304L was presented
using AFGROW code when NASGRO mode laws adopted. Double
through crack at hole specimen is used in this investigation under
constant amplitude loading. Effect of mean stress is highlighted.
Results show that fatigue crack growth rate (FCGR) and fatigue life
were affected by maximum applied load and dimension of hole. An
equivalent of Paris law for this material was estimated.