Abstract: The application of carbon materials in the branches of the electrochemical industry shows an increasing tendency each year due to the many interesting properties they possess. These are, among others, a well-developed specific surface, porosity, high sorption capacity, good adsorption properties, low bulk density, electrical conductivity and chemical resistance. All these properties allow for their effective use, among others in supercapacitors, which can store electric charges of the order of 100 F due to carbon electrodes constituting the capacitor plates. Coals (including expanded graphite, carbon black, graphite carbon fibers, activated carbon) are commonly used in electrochemical methods of removing oil derivatives from water after tanker disasters, e.g., phenols and their derivatives by their electrochemical anodic oxidation. Phenol can occupy practically the entire surface of carbon material and leave the water clean of hydrophobic impurities. Regeneration of such electrodes is also not complicated, it is carried out by electrochemical methods consisting in unblocking the pores and reducing resistances, and thus their reactivation for subsequent adsorption processes. Graphite is commonly used as an anode material in lithium-ion cells, while due to the limited capacity it offers (372 mAh g-1), new solutions are sought that meet both capacitive, efficiency and economic criteria. Increasingly, biodegradable materials, green materials, biomass, waste (including agricultural waste) are used in order to reuse them and reduce greenhouse effects and, above all, to meet the biodegradability criterion necessary for the production of lithium-ion cells as chemical power sources. The most common of these materials are cellulose, starch, wheat, rice, and corn waste, e.g., from agricultural, paper and pharmaceutical production. Such products are subjected to appropriate treatments depending on the desired application (including chemical, thermal, electrochemical). Starch is a biodegradable polysaccharide that consists of polymeric units such as amylose and amylopectin that build an ordered (linear) and amorphous (branched) structure of the polymer. Carbon is also used as a catalyst. Elemental carbon has become available in many nano-structured forms representing the hybridization combinations found in the primary carbon allotropes, and the materials can be enriched with a large number of surface functional groups. There are many examples of catalytic applications of coal in the literature, but the development of this field has been hampered by the lack of a conceptual approach combining structure and function and a lack of understanding of material synthesis. In the context of catalytic applications, the integrity of carbon environmental management properties and parameters such as metal conductivity range and bond sequence management should be characterized. Such data, along with surface and textured information, can form the basis for the provision of network support services.
Abstract: Maximal radar wave absorbing cannot be achieved by shaping alone. We have to focus on the parameters of absorbing materials such as permittivity, permeability, and thickness so that best absorbing according to our necessity can happen. The real and imaginary parts of the relative complex permittivity (εr' and εr") and permeability (µr' and µr") were obtained by simulation. The microwave absorbing property of carbon and Ni(C) is simulated in this study by MATLAB software; the simulation was in the frequency range between 2 to 12 GHz for carbon black (C), and carbon coated nickel (Ni(C)) with different thicknesses. In fact, we draw reflection loss (RL) for C and Ni-C via frequency. We have compared their absorption for 3-mm thickness and predicted for other thicknesses by using of electromagnetic wave transmission theory. The results showed that reflection loss position changes in low frequency with increasing of thickness. We found out that, in all cases, using nanocomposites as absorbance cannot get better results relative to pure nanoparticles. The frequency where absorption is maximum can determine the best choice between nanocomposites and pure nanoparticles. Also, we could find an optimal thickness for long wavelength absorbing in order to utilize them in protecting shields and covering.
Abstract: In the present work, the effects of additives, including
contents of the added antioxidants and type of the selected metallic
stearates (either calcium stearate (CaSt) or zinc stearate (ZnSt)), on
the thermal stabilities of carbon black (CB)/high density polyethylene
(HDPE) compounds were studied. The results showed that the AO
contents played a key role in the thermal stabilities of the CB/HDPE
compounds — the higher the AO content, the higher the thermal
stabilities. Although the CaSt-containing compounds were slightly
superior to those with ZnSt in terms of the thermal stabilities, the
remaining solid residue of CaSt after heated to the temperature of 600
°C (mainly calcium carbonate (CaCO3) as characterized by the X-ray
diffraction (XRD) technique) seemed to catalyze the decomposition
of CB in the HDPE-based compounds. Hence, the quantification of
CB in the CaSt-containing compounds with a muffle furnace gave an
inaccurate CB content — much lower than actual value. However,
this phenomenon was negligible in the ZnSt-containing system.
Abstract: This research investigated treatment of crude carbon black produced from pyrolysis of waste tyres in order to evaluate its quality and possible industrial applications. A representative sample of crude carbon black was dry screened to determine the initial particle size distribution. This was followed by pulverizing the crude carbon black and leaching in hot concentrated sulphuric acid for the removal of heavy metals and other contaminants. Analysis of the refined carbon black showed a significant improvement of the product quality compared to crude carbon black. It was discovered that refined carbon black can be further classified into multiple high value products for various industrial applications such as filler, paint pigment, activated carbon and fuel briquettes.
Abstract: This study shows the effect of carbon towards
molybdenum carbide alloy when exposed to Microwave. This
technique is also known as Microwave Induced Alloying (MIA) for
the preparation of molybdenum carbide. In this study ammonium
heptamolybdate solution and carbon black powder were
heterogeneously mixed and exposed to microwave irradiation for 2
minutes. The effect on amount of carbon towards the produced alloy
on morphological and oxidation states changes during microwave is
presented. In this experiment, it is expected carbon act as a reducing
agent with the ratio 2:7 molybdenum to carbon as the optimum for
the production of molybdenum carbide alloy. All the morphological
transformations and changes in this experiment were followed and
characterized using X-Ray Diffraction and FESEM.
Abstract: The main issue in sweetening natural gas is H2S
dissociation. The present study is concerned with simulating thermal
dissociation of H2S in industrial natural gas carbon black furnace.
The comparison of calculated results against experimental
measurements shows good agreement. The results show that sulfur
derived from H2S thermal dissociation peaked at φ=0.95. H2S
thermal dissociation is enhanced in equivalence ratio upper than 1
and H2S oxidization is increased in equivalence ratio lower than 1.
H2 concentration of H2S thermal dissociation is increased with
increase of equivalence ratio up to 1. Also, H2S concentration
decreased in outlet as equivalence ratio increases. H2S thermal
dissociation to hydrogen and Sulfur reduces its toxic characteristics
and make economical benefits.