Abstract: Iron ore and coal are the two major important raw
materials being used in Iron making industries. Usually ore fines
containing around 5% Alumina are rejected due to higher proportion
of alumina. Therefore, a technology or process which may reduce
the alumina content by 2% by beneficiation process will be highly
attractive . In addition fine coals with ash content is used nearly 12%
is directly injected in blast furnace. Fast fluidization is a technology
by using dry beneficiation of coal and iron ore can be done. During
the fluidization process the iron ore band coal is fluidized at high
velocity in the riser of a fast fluidized bed, the heavier and coarse
particles is generally settled at the bottom in a dense zone of the riser
while the finer and lighter particle are entrained to the top dilute zone
and then via a cyclone is fed back to the bottom of the riser column.
Most of the alumina and low ash fine size coals being lighter are
expected to move up to the riser and by a natural beneficiation of
ores is expected to take place in the riser. Therefore in this study an
attempt has been made for dry beneficiation of iron ore and coal in a
fluidized bed and its hydrodynamic characterization.
Abstract: Hydrodesulfurization (HDS) of dibenzothiophene
(DBT) in a high pressure batch reactor was done at 320 °C on
CoMoS/Al2O3-B2O3 (4, 10, and 16 wt. % of Boria) using nhexadecane
as solvent, dimethyldisulfide (DMDS) in tetradecane as
sulfur agent, and stirring at 1000 rpm. The effects of boria were
investigated by using X-ray diffraction (XRD), Temperature
programmed desorption (TPD) of ammonia, and Brunauer-Emmet-
Teller (BET) experiments. The results showed that the catalyst
prepared with low boria content (4 wt. %) had HDS activity (in
pseudo first order kinetic constant basis) value ~1.45 times higher to
that of CoMoS/Al2O3 catalyst.
Abstract: In this work, grinding or microcutting tools in the form of pellets were manufactured using a bounded alumina abrasive grains. The bound used is a vitreous material containing quartz feldspars, kaolinite and a quantity of hematite. The pellets were used in glass grinding process to replace the free abrasive grains lapping process. The study of the elaborated pellets were done to define their effectiveness in the grinding process and to optimize the influence of the pellets elaboration parameters. The obtained results show the existence of an optimal combination of the pellets elaboration parameters for each glass grinding phase (coarse to fine grinding). The final roughness (rms) reached by the elaborated pellets on a BK7 glass surface was about 0.392 μm.
Abstract: Three alumina-supported Pt-Sn catalysts have been
prepared by means of co-impregnation and characterized by XRD and
N2 adsorption. The influence of catalyst composition and reaction
conditions on the conversion and selectivity were investigated in the
hydrogenation of acetic acid in an isothermal integral fixed bed
reactor. The experiments were performed on the temperature interval
468-548 K, liquid hourly space velocity (LHSV) of 0.3-0.7h-1,
pressures between 1.0 and 5.0Mpa. A good compromise of
0.75%Pt-1.5%Sn can act as an optimized acetic acid hydrogenation
catalyst, and the conversion and selectivity can be tuned through the
variation of reaction conditions.
Abstract: In this study, an experimental investigation was carried
out to fix CO2 into the electronic arc furnace (EAF) reducing slag from
stainless steelmaking process under wet grinding. The slag was ground
by the vibrating ball mill with the CO2 and pure water. The reaction
behavior was monitored with constant pressure method, and the
change of CO2 volume in the experimental system with grinding time
was measured. It was found that the CO2 absorption occurred as soon
as the grinding started. The CO2 absorption under wet grinding was
significantly larger than that under dry grinding. Generally, the
amount of CO2 absorption increased as the amount of water, the
amount of slag, the diameter of alumina ball and the initial pressure of
CO2 increased. However, the initial absorption rate was scarcely
influenced by the experimental conditions except for the initial CO2
pressure. According to this research, the CO2 reacted with the CaO
inside the slag to form CaCO3.
Abstract: An efficient and green protocol for the synthesis of α-
aminonitriles derivatives by one-pot reaction of different aldehydes
with amines and trimethylsilyl cyanides has been developed using
natural alumina, alumina sulfuric acid (ASA), nano-γ-alumina, nanoalumina
sulfuric acid (nano-ASA) under microwave irradiation and
solvent-free conditions. The advantages of methods are short reaction
times, high yields, milder conditions and easy work up. The catalysts
can be recovered for the subsequent reactions and reused without any
appreciable loss of efficiency.
Abstract: The effect of Alumina nanoparticle size on thermophysical
properties, heat transfer performance and pressure loss characteristics of
Aviation Turbine Fuel (ATF)-Al2O3 nanofluids is studied experimentally for
the proposed application of regenerative cooling of semi-cryogenic rocket
engine thrust chambers. Al2O3 particles with mean diameters of 50 nm or 150
nm are dispersed in ATF. At 500C and 0.3% particle volume concentration,
the bigger particles show increases of 17% in thermal conductivity and 55% in
viscosity, whereas the smaller particles show corresponding increases of 21%
and 22% for thermal conductivity and viscosity respectively. Contrary to these
results, experiments to study the heat transfer performance and pressure loss
characteristics show that at the same pumping power, the maximum
enhancement in heat transfer coefficient at 500C and 0.3% concentration is
approximately 47% using bigger particles, whereas it is only 36% using
smaller particles.
Abstract: Tungsten trioxide has been prepared by using P-PTA
as a precursor on alumina substrates by spin coating method.
Palladium introduced on WO3 film via electrolysis deposition by
using palladium chloride as catalytic precursor. The catalytic
precursor was introduced on the series of films with different
morphologies. X-ray diffractometry (XRD), Scanning electron
microscopy (SEM) and XPS were applied to analyze structure and
morphology of the fabricated thin films. Then we measured variation
of samples- electrical conductivity of pure and Pd added films in air
and diluted hydrogen. Addition of Pd resulted in a remarkable
improvement of the hydrogen sensing properties of WO3 by detection
of Hydrogen below 1% at room temperature. Also variation of the
electrical conductivity in the presence of diluted hydrogen revealed
that response of samples depends rather strongly on the palladium
configuration on the surface.