Abstract: Friction Stir Welding is a solid state welding technique which can be used to produce sound welds between similar and dissimilar materials. Dissimilar welds which include welds between the different series of aluminium alloys, aluminium to magnesium, steel and titanium has been successfully produced by many researchers. This review covers the work conducted in the above mentioned materials and further concludes by showing the need to fully understand the FSW process in order to expand the latter industrially.
Abstract: Friction stir welding is a solid state joining process. High strength aluminum alloys are widely used in aircraft and marine industries. Generally, the mechanical properties of fusion welded aluminum joints are poor. As friction stir welding occurs in solid state, no solidification structures are created thereby eliminating the brittle and eutectic phases common in fusion welding of high strength aluminum alloys. In this review the process parameters, microstructural evolution, and effect of friction stir welding on the properties of weld specific to aluminum alloys have been discussed.
Abstract: In this study, Friction Stir Processing (FSP) a recent grain refinement technique was employed to disperse micron-sized (2 *m) SiCp particles into aluminum alloy AA6063. The feasibility to fabricate bulk composites through FSP was analyzed and experiments were conducted at different traverse speeds and wider volumes of the specimens. Micro structural observation were carried out by employing optical microscopy test of the cross sections in both parallel and perpendicular to the tool traverse direction. Mechanical property including micro hardness was evaluated in detail at various regions on the specimen. The composites had an excellent bonding with aluminum alloy substrate and a significant increase of 30% in the micro hardness value of metal matrix composite (MMC) as to that of the base metal has observed. The observations clearly indicate that SiC particles were uniformly distributed within the aluminum matrix.
Abstract: Solidification cracking and hydrogen cracking are some defects generated in the fusion welding of ultrahigh carbon steels. However, friction stir welding (FSW) of such steels, being a solid-state technique, has been demonstrated to alleviate such problems encountered in traditional welding. FSW include different process parameters that must be carefully defined prior processing. These parameters included but not restricted to: tool feed, tool RPM, tool geometry, tool tilt angle. These parameters form a key factor behind avoiding warm holes and voids behind the tool and in achieving a defect-free weld. More importantly, these parameters directly affect the microstructure of the weld and hence the final mechanical properties of weld. For that, 3D finite element (FE) thermo-mechanical model was developed using DEFORM 3D to simulate FSW of carbon steel. At points of interest in the joint, tracking is done for history of critical state variables such as temperature, stresses, and strain rates. Typical results found include the ability to simulate different weld zones. Simulations predictions were successfully compared to experimental FSW tests. It is believed that such a numerical model can be used to optimize FSW processing parameters to favor desirable defect free weld with better mechanical properties.
Abstract: This paper reports the tensile fracture location
characterizations of dissimilar friction stir welds between 5754
aluminium alloy and C11000 copper. The welds were produced using
three shoulder diameter tools; namely, 15, 18 and 25 mm by varying
the process parameters. The rotational speeds considered were 600,
950 and 1200 rpm while the feed rates employed were 50, 150 and
300 mm/min to represent the low, medium and high settings
respectively. The tensile fracture locations were evaluated using the
optical microscope to identify the fracture locations and were
characterized. It was observed that 70% of the tensile samples failed
in the Thermo Mechanically Affected Zone (TMAZ) of copper at the
weld joints. Further evaluation of the fracture surfaces of the pulled
tensile samples revealed that welds with low Ultimate Tensile
Strength either have defects or intermetallics present at their joint
interfaces.
Abstract: Friction Stir Welding (FSW) is a solid state welding
process invented and patented by The Welding Institute (TWI) in the
United Kingdom in 1991 for butt and lap welding of metals and plastics. This paper highlights the benefits of friction stir welding
process as an energy efficient and a green technology process in the
field of welding. Compared to the other conventional welding processes, its benefits, typical applications and its use in joining
similar and dissimilar materials are also presented.