Abstract: Ductile iron samples alloyed with 2.5% Si, 0.78% Cu, 0.421% Mo and 0.151% Ni were austempered at 345 °C and 380 °C for 150 and 180 mins and then tested for wear strength. Ductile iron was also included in the study for comparison purposes. A pin-on-disc machine was employed for wear study. The investigations were carried out for a speed of 3 m/s, under the contact load of 29.43 N with varying sliding distances ranging from 1000 m to 5000 m. The experimental outcome indicates that ADI austempered at 345 °C is more wear resistant than the one austempered at 380 °C. Also for only a sliding distance of 3000 m, both exhibited almost same wear resistance. SEM analysis indicates running sliding marks more or less parallel to one another. Spalled layers and large voids which resemble delamination were observed on worn surface of ADI380. This indicated the occurrence of severe wear. Dark patches observed indicate oxidized surface.
Abstract: This study is concerned with the microstructural analysis and improvement of wear resistance of 356 aluminum alloy by a high energy electron beam. Shock hardening on material by high energy electron beam improved wear resistance. Particularly, in the surface of material by shock hardening, the wear resistance was greatly enhanced to 29% higher than that of the 356 aluminum alloy substrate. These findings suggested that surface shock hardening using high energy electron beam irradiation was economical and useful for the development of surface shock hardening with improved wear resistance.
Abstract: In this research (using induction furnace process)
nodular iron with three different percentages of copper (residual,
0.5% and 1,2%) was obtained. Chemical analysis was performed by
mass spectrometry and microstructures were characterized by Optical
Microscopy (ASTM E3) and Scanning Electron Microscopy (SEM).
The study of mechanical behavior was carried out in a mechanical
test machine (ASTM E8) and a Pin on disk tribometer (ASTM G99)
was used to assess wear resistance. It is observed that the dissolution
of copper in crystal lattice increases the pearlite structure improving
the wear and hardness behavior, but producing a contrary effect on
the energy absorption.
Abstract: The commercial white tyres are usually used for forklifts in food and medicine industries. Conventionally, silica is used as reinforcement in the tyres. However, the adhesion between silica particles and rubber is remarkably poor. To improve the problem of adhesion and hence enhance wear resistance, modification of silica surface is one of the solutions. In this work, the natural rubber compound blending with polyisoprene-coated silica prepared by admicellar polymerization technique was studied to compare with the natural rubber compound of unmodified silica. The surface characterization of modified silica was also examined by SEM, FTIR, and TGA. The results show that polyisoprene-coated silica/natural rubber compound gave better overall mechanical properties, especially wear resistance with the improvement of the adhesion between silica and natural rubber matrix that can be seen in the SEM micrograph.
Abstract: The paper is concerned with the technological process of renovation of shafts used in industrial manufacturing for extruding of sheet material. In the classical renovation technologies, a chrome based coating is applied to the working surface of the shaft in galvanic baths. The process, however, is known to be exclusively harmful due to the waste cyanide products. In this work, we present an advanced nanotechnology based on nonelectric chemical laying of a nickel coating with included nanoparticles. The technology is environmentally harmless and the new coating features an increased hardness and wear resistance. Results from experimental tests of the nanostructured nickel coating are presented and discussed.
Abstract: A group of Stellite alloys are studied in consideration
of temperature effects on their hardness and wear resistance. The
hardness test is conducted on a micro-hardness tester with a hot stage
equipped that allows heating the specimen up to 650°C. The wear
resistance of each alloy is evaluated using a pin-on-disc tribometer
with a heating furnace built-in that provides the temperature capacity
up to 450°C. The experimental results demonstrate that the hardness
and wear resistance of Stellite alloys behave differently at room
temperature and at high temperatures. The wear resistance of Stellite
alloys at room temperature mainly depends on their carbon content and
also influenced by the tungsten content in the alloys. However, at high
temperatures the wear mechanisms of Stellite alloys become more
complex, involving multiple factors. The relationships between
chemical composition, microstructure, hardness and wear resistance of
these alloys are studied, with focus on temperature effect on these
relations.
Abstract: Nowadays, engineering ceramics have significant
applications in different industries such as; automotive, aerospace,
electrical, electronics and even martial industries due to their
attractive physical and mechanical properties like very high hardness
and strength at elevated temperatures, chemical stability, low friction
and high wear resistance. However, these interesting properties plus
low heat conductivity make their machining processes too hard,
costly and time consuming. Many attempts have been made in order
to make the grinding process of engineering ceramics easier and
many scientists have tried to find proper techniques to economize
ceramics' machining processes. This paper proposes a new diamond
plunge grinding technique using ultrasonic vibration for grinding
Alumina ceramic (Al2O3). For this purpose, a set of laboratory
equipments have been designed and simulated using Finite Element
Method (FEM) and constructed in order to be used in various
measurements. The results obtained have been compared with the
conventional plunge grinding process without ultrasonic vibration
and indicated that the surface roughness and fracture strength
improved and the grinding forces decreased.