Abstract: Due to their fluidity and simplicity of use, self-compacting concretes (SCCs) have undeniable advantages. In recent years, the role of metakaolin as a one of pozzolanic materials in concrete has been considered by researchers. It can modify various properties of concrete, due to high pozzolanic reactions and also makes a denser microstructure. The objective of this paper is to examine the influence of three type of Portland cement and metakaolin on fresh state, compressive strength and sulfuric acid attacks in self- consolidating concrete at early age up to 90 days of curing in lime water. Six concrete mixtures were prepared with three types of different cement as Portland cement type II, Portland Slag Cement (PSC), Pozzolanic Portland Cement (PPC) and 15% substitution of metakaolin by every cement. The results show that the metakaolin admixture increases the viscosity and the demand amount of superplasticizer. According to the compressive strength results, the highest value of compressive strength was achieved for PSC and without any metakaolin at age of 90 days. Conversely, the lowest level of compressive strength at all ages of conservation was obtained for PPC and containing 15% metakaolin. According to this study, the total substitution of PSC and PPC by Portland cement type II is beneficial to the increasing in the chemical resistance of the SCC with respect to the sulfuric acid attack. On the other hand, this increase is more noticeable by the use of 15% of metakaolin. Therefore, it can be concluded that metakaolin has a positive effect on the chemical resistance of SCC containing of Portland cement type II, PSC, and PPC.
Abstract: Lignin is a molecule derived from wood and also generated as waste from the paper industry. With a view to its valorization and protection of the environment, we are interested in its use as a superplasticizer-type adjuvant in mortars and concretes to improve their mechanical strengths. The additives of the concrete have a very strong influence on the properties of the fresh and / or hardened concrete. This study examines the development and use of industrial waste and lignin extracted from a renewable natural source (wood) in cementitious materials. The use of these resources is known at present as a definite resurgence of interest in the development of building materials. Physicomechanical characteristics of mortars are determined by optimization quantity of the natural superplasticizer. The results show that the mechanical strengths of mortars based on natural adjuvant have improved by 20% (64 MPa) for a W/C ratio = 0.4, and the amount of natural adjuvant of dry extract needed is 40 times smaller than commercial adjuvant. This study has a scientific impact (improving the performance of the mortar with an increase in compactness and reduction of the quantity of water), ecological use of the lignin waste generated by the paper industry) and economic reduction of the cost price necessary to elaboration of self-compacting mortars and concretes).
Abstract: The aim of this article is to access the optimal mix design of self-compacting light weight concrete. The effects of magnetic water, superplasticizer based on polycarboxylic-ether, and silica fume on characteristics of this type of concrete are studied. The workability of fresh concrete and the compressive strength of hardened concrete are considered here. For this purpose, nine mix designs were studied. The percentages of superplasticizer were 0.5, 1, and 2% of the weight of cement, and the percentages of silica fume were 0, 6, and 10% of the weight of cement. The water to cementitious ratios were 0.28, 0.32, and 0.36. The workability of concrete samples was analyzed by the devices such as slump flow, V-funnel, L box, U box, and Urimet with J ring. Then, the compressive strengths of the mixes at the ages of 3, 7, 28, and 90 days were obtained. The results show that by using magnetic water, the compressive strengths are improved at all the ages. In the concrete samples with ordinary water, more superplasticizer dosages were needed. Moreover, the combination of superplasticizer and magnetic water had positive effects on the mixes containing silica fume and they could flow easily.
Abstract: This paper aimed to introduce the solution of concrete
slump recovery using chemical admixture type-F (superplasticizer,
naphthalene base) to the practice in order to solve unusable concrete
problem due to concrete loss its slump, especially for those tropical
countries that have faster slump loss rate. In the other hand, randomly
adding superplasticizer into concrete can cause concrete to segregate.
Therefore, this paper also develops the estimation model used to
calculate amount of second dose of superplasticizer need for concrete
slump recovery. Fresh properties of ordinary Portland cement
concrete with volumetric ratio of paste to void between aggregate
(paste content) of 1.1-1.3 with water-cement ratio zone of 0.30 to
0.67 and initial superplasticizer (naphthalene base) of 0.25%-1.6%
were tested for initial slump and slump loss for every 30 minutes for
one and half hour by slump cone test. Those concretes with slump
loss range from 10% to 90% were re-dosed and successfully
recovered back to its initial slump. Slump after re-dosed was tested
by slump cone test. From the result, it has been concluded that, slump
loss was slower for those mix with high initial dose of
superplasticizer due to addition of superplasticizer will disturb
cement hydration. The required second dose of superplasticizer was
affected by two major parameters, which were water-cement ratio
and paste content, where lower water-cement ratio and paste content
cause an increase in require second dose of superplasticizer. The
amount of second dose of superplasticizer is higher as the solid
content within the system is increase, solid can be either from cement
particles or aggregate. The data was analyzed to form an equation use
to estimate the amount of second dosage requirement of
superplasticizer to recovery slump to its original.
Abstract: This work is focused on the study of valuation of
recycled concrete aggregates, by measuring certain properties of
concrete in the fresh and hardened state. In this study, rheological
tests and physic-mechanical characterization on concretes and
mortars were conducted with recycled concrete whose geometric
properties were identified aggregates. Mortars were elaborated with
recycled fine aggregate (0/5mm) and concretes were manufactured
using recycled coarse aggregates (5/12.5 mm and 12.5/20 mm). First,
a study of the mortars was conducted to determine the effectiveness
of polycarboxylate superplasticizer on the workability of these and
their action deflocculating of the recycled sand. The rheological
behavior of mortars based on fine aggregate recycled was
characterized. The results confirm that the mortars composed of
different fractions of recycled sand (0 /5) have a better mechanical
properties (compressive and flexural strength) compared to normal
mortar. Also, the mechanical strengths of concretes made with
recycled aggregates (5/12.5 mm and 12.5/20 mm), are comparable to
those of conventional concrete with conventional aggregates,
provided that the implementation can be improved by the addition of
a superplasticizer.