Abstract: The production of olive oil is considered as one of the most important agri-food industries. However, some of the by-products generated in the process are potential pollutants and cause environmental problems. Consequently, the management of these by-products is currently considered as a challenge for the olive oil industry. In this context, several technologies have been developed and tested. In this sense, the autohydrolysis of these by-products could be considered as a promising technique. Therefore, this study focused on autohydrolysis treatments of a solid residue from the olive oil industry denominated olive cake. This one comes from the olive pomace extraction with hexane. Firstly, a water washing was carried out to eliminate the water soluble compounds. Then, an experimental design was developed for the autohydrolysis experiments carried out in the hydrothermal pressure reactor. The studied variables were temperature (30, 60 and 90 ºC) and time (30, 60, 90 min). On the other hand, aliquots of liquid obtained fractions were analysed by HPLC to determine the fructose and sucrose contents present in the liquid fraction. Finally, the obtained results of sugars contents and the yields of the different experiments were fitted to a neuro-fuzzy and to a polynomial model.
Abstract: Currently, the polyurethanes industry is dependent on fossil resources to obtain their basic raw materials (polyols and isocyanate), as these are obtained from petroleum products. The aim of this work was to use biopolyols from liquefied Pseudotsuga (Pseudotsuga menziesii) and Turkey oak (Quercus cerris) barks for the production of polyurethane foams and optimize the process. Liquefaction was done with glycerol catalyzed by KOH. Foams were produced following different formulations and using biopolyols from both barks. Subsequently, the foams were characterized according to their mechanical properties and the reaction of the foam formation was monitored by FTIR-ATR. The results show that it is possible to produce polyurethane foams using bio-based polyols and the liquefaction conditions are very important because they influence the characteristics of biopolyols and, consequently the characteristics of the foams. However, the process has to be further optimized so that it can obtain better quality foams.
Abstract: Polyurethane foams (PUF) has been prepared from
vegetable; soybean based polyols. They were characterized into
flexible and semi rigid polyurethane foam. This work is directed to
production of flexible polyurethane foams by a process involving the
reaction of mixture of 2,4- and 2,6-Toluene di Isocyanate isomers,
with portion of to blends of soy polyols with petroleum polyol in the
presence of other ingredients such as blowing agents, silicone
surfactants and accelerating agents. Additon of chain extender
improves the property then further decreases the properties on further
addition of the same. The objective of this work was to study the
effect of chain extender and role of phosphoric acid catalyst to the
final properties and correlate the morphology image with mechanical
properties of these foams.
Abstract: Polyurethane foam (PUF) were prepared by
reacting polyols synthesized from soy-oil into mixture of 2,4-
Toluene diisocyanate (TDI) with 4,4--Methylene Diamine
Isocyanate (MDI) with ratio of 70:30. The polyols obtained
via esterification reaction were categorize into different
temperature of reaction and by used of varied concentration
of phosphoric acid catalyst. The purpose of catalysts is to
shifting selectivity to a desired and value added of product.
The effect of stoichiometric balance (molar ratio of
epoxide/ethylene glycol) to the concentration of the catalyst
on the final properties was evaluated.