Chloroform-Formic Acid Solvent Systems for Nanofibrous Polycaprolactone Webs

In this study, polycaprolactone (PCL) was dissolved in chloroform:ethanol solvent system at a concentration of 18 w/v %. 1, 2, 4, and 6 droplets of formic acid were added to the prepared 10ml PCL-chloroform:ethanol solutions separately. Fibrous webs were produced by electrospinning technique based on the horizontal working principle. Morphology of the webs was investigated by using scanning electron microscopy (SEM) whereas fiber diameters were measured by Image J Software System. The effect of formic acid addition to the mostly used chloroform solvent on fiber morphology was examined. Results indicate that there is a distinct fall in fiber diameter with the addition of formic acid drops. The average fiber diameter was measured as 2.22μm in PCL /chloroform:ethanol solution system. On the other hand, 328nm and 256 nm average fiber diameters were measured for the samples of 4 drops and 6 drops formic acid added. This study offers alternative solvent systems to produce nanoscaled, nontoxic PCL fibrous webs by electrospinning technique.

Physical and Chemical Investigation of Polycaprolactone, Nanohydroxyapatite and Poly (Vinyl Alcohol) Nanocomposite Scaffolds

Aligned and random nanofibrous scaffolds of PVA/PCL/nHA were fabricated by electrospinning method. The composite nanofibrous scaffolds were subjected to detailed analysis. Morphological investigations revealed that the prepared nanofibers have uniform morphology and the average fiber diameters of aligned and random scaffolds were 135.5 and 290 nm, respectively. The obtained scaffolds have a porous structure with porosity of 88 and 76% for random and aligned nanofibers, respectively. Furthermore, FTIR analysis demonstrated that there were strong intramolecular interactions between the molecules of PVA/PCL/nHA. On the other hand, mechanical characterizations show that aligning the nanofibers, could significantly improve the rigidity of the resultant biocomposite nanofibrous scaffolds.