Abstract: Many of thermosetting resins have application only in filled state, reinforced with different mineral fillers. The co-filling of polymers with mineral filler and gases creates a possibility for production of polymer composites materials with low density. This processing leads to forming of new materials – gas-filled plastics (polymer foams). The properties of these materials are determined mainly by the shape and size of internal structural elements (pores). The interactions on the phase boundaries have influence on the materials properties too. In the present work, the gas-filled urea-formaldehyde resins were reinforced by waste phosphogypsum. The waste phosphogypsum (CaSO4.2H2O) is a solid by-product in wet phosphoric acid production processes. The values of the interactions polymer-filler were increased by using two modifying agents: polyvinyl acetate for polymer matrix and sodium metasilicate for filler. Technological methods for gas-filling and recipes of urea-formaldehyde based materials with apparent density 20-120 kg/m3 were developed. The heat conductivity of the samples is between 0.024 and 0.029 W/moK. Tensile analyses were carried out at 10 and 50% deformation and show values 0.01-0.14 MPa and 0.01-0.09 MPa, respectively. The apparent density of obtained materials is between 20 and 92 kg/m3. The changes in the tensile properties and density of these materials according to sodium metasilicate content were studied too. The mechanism of phosphogypsum adsorption modification was studied using methods of FT-IR spectroscopy. The structure of the gas-filled urea-formaldehyde resins was described by results of electron scanning microscopy at three different magnification ratios – x50, x150 and x 500. The aim of present work is to study the possibility of the usage of phosphogypsum as mineral filler for urea-formaldehyde resins and development of a technology for the production of gas-filled reinforced polymer composite materials. The structure and the properties of obtained composite materials are suitable for thermal and sound insulation applications.
Abstract: Flue gas desulfurization gypsum (FGD) is a waste
material arouse from coal power plants. Hydroxyapatite (HAP) is a
biomaterial with porous structure. In this study, FGD gypsum which
retrieved from coal power plant in Turkey was characterized and
HAP particles which can be used as an adsorbent in wastewater
treatment application were synthesized from the FGD gypsum. The
raw materials are characterized by using X Ray Diffraction (XRD)
and Fourier transform infrared spectroscopy (FT-IR) techniques and
produced HAP are characterized by using XRD. As a result, HAP
particles were synthesized at the molar ratio of 5:10, 5:15, 5:20, 5:24,
at room temperature, in alkaline medium (pH=11) and in 1 hour-reaction
time. Among these conditions, 5:20 had the best result.
Abstract: In this study, the feasibility of incorporating ceramic
waste from bricks (perforated brick and double hollow brick) and
extruded polystyrene (XPS) waste, is analysed.
Results show that it is possible to incorporate up to 25% of
ceramic waste and 4% of XPS waste over the weight of gypsum in a
gypsum matrix. Furthermore, with the addition of ceramic waste an
8% of surface hardness increase and a 25% of capillary water
absorption reduction can be obtained. On the other hand, with the
addition of XPS, a 26% reduction of density and a 37% improvement
of thermal conductivity can be obtained.
The obtained results are favorable to use these materials in order to
produce prefabricated gypsum and also as material for interior
cladding walls.
Abstract: Gypsum (CaSO4.2H2O) is a mineral that is found in
large quantities in the Turkey and in the World. In this study, the
dissolution of this mineral in the diammonium hydrogen phosphate
solutions has been studied. The dissolution and dissolution kinetics of
gypsum in diammonium hydrogen phosphate solutions will be useful
for evaluating of solid wastes containing gypsum. Parameters such as
diammonium hydrogen phosphate concentration, temperature and
stirring speed affecting on the dissolution rate of the gypsum in
diammonium hydrogen phosphate solutions were investigated. In
experimental studies have researched effectiveness of the selected
parameters. The dissolution of gypsum were examined in two parts at
low and high temperatures. The experimental results were
successfully correlated by linear regression using Statistica program.
Dissolution curves were evaluated shrinking core models for solidfluid
systems. The activation energy was found to be 34.58 kJ/mol
and 44.45 kJ/mol for the low and the high temperatures. The
dissolution of gypsum was controlled by chemical reaction both low
temperatures and high temperatures.
Abstract: This paper involved the performance of a hightemperature
X-Ray powder diffraction analysis (XRD) of a sample of
chemical gypsum generated in the production of titanium white; this
gypsum originates by neutralizing highly acidic water with limestone
suspension. Specifically, it was gypsum formed in the first stage of
neutralization when the resulting material contains, apart from
gypsum, a number of waste products resulting from the
decomposition of ilmenite by sulphuric acid. So it can be described as
red titanogypsum. By conducting the experiment using XRD
apparatus Bruker D8 Advance with a Cu anode (λkα=1.54184 Å)
equipped with high-temperature chamber Anton Paar HTK 16, it was
possible to identify clearly in the sample each phase transition in the
system of CaSO4·xH2O.
Abstract: Removal of Methylene Blue (MB) from aqueous
solution by adsorbing it on Gypsum was investigated by batch
method. The studies were conducted at 25°C and included the effects
of pH and initial concentration of Methylene Blue. The adsorption
data was analyzed by using the Langmuir, Freundlich and Tempkin
isotherm models. The maximum monolayer adsorption capacity was
found to be 36 mg of the dye per gram of gypsum. The data were
also analyzed in terms of their kinetic behavior and was found to
obey the pseudo second order equation.