Abstract: Fibre reinforced concrete (FRC) has been widely used in industrial pavements and non-structural elements such as pipes, culverts, tunnels, and precast elements. The strengthening effect of fibres in the concrete matrix is achieved primarily due to the bridging effect of fibres at the crack interfaces. The workability of the concrete was reduced on addition of high percentages of steel fibres. The optimum percentage of addition of steel fibres varies with its aspect ratio. For this study, 1% addition of steel has resulted to be the optimum percentage for both Hooked and Crimped Steel Fibres and was added to the beam specimens. The fibres restrain efficiently the cracks and take up residual stresses beyond the cracking. In this sense, diagonal cracks are effectively stitched up by fibres crossing it. The failure of beams within the shear failure range changed from shear to flexure in the presence of sufficient steel fibre quantity. The shear strength is increased with the addition of steel fibres and had exceeded the enhancement obtained with the transverse reinforcement. However, such increase is not directly in proportion with the quantity of fibres used. Considering all the clarification made in the present experimental investigation, it is concluded that 1% of crimped steel fibres with an aspect ratio of 50 is the best type of steel fibres for replacement of transverse stirrups in high strength concrete beams when compared to the steel fibres with hooked ends.
Abstract: This work reports about an approach for an automatic adaptation of concrete formulations based on genetic algorithms (GA) to optimize a wide range of different fit-functions. In order to achieve the goal, a method was developed which provides a numerical description of a fibre reinforced concrete (FRC) mixture regarding the production technology and the property spectrum of the concrete. In a first step, the FRC mixture with seven fixed components was characterized by varying amounts of the components. For that purpose, ten concrete mixtures were prepared and tested. The testing procedure comprised flow spread, compressive and bending tensile strength. The analysis and approximation of the determined data was carried out by GAs. The aim was to obtain a closed mathematical expression which best describes the given seven-point cloud of FRC by applying a Gene Expression Programming with Free Coefficients (GEP-FC) strategy. The seven-parametric FRC-mixtures model which is generated according to this method correlated well with the measured data. The developed procedure can be used for concrete mixtures finding closed mathematical expressions, which are based on the measured data.
Abstract: Unreinforced concrete is a comparatively brittle substance when exposed to tensile stresses, the required tensile strength is provided by the introduction of steel which is used as reinforcement. The strength of concrete may be improved tremendously by the addition of fibre. This study focused on investigating the compressive strength of mass concrete mixed with different percentage of plastic fibre. Twelve samples of concrete cubes with varied percentage of plastic fibre at 7, 14 and 28 days of water submerged curing were tested under compression loading. The result shows that the compressive strength of plastic fibre reinforced concrete increased with rise in curing age. The strength increases for all percentage dosage of fibre used for the concrete. The density of the Plastic Fibre Reinforced Concrete (PFRC) also increases with curing age, which implies that during curing, concrete absorbs water which aids its hydration. The least compressive strength obtained with the introduction of plastic fibre is more than the targeted 20 N/mm2 recommended for construction work showing that PFRC can be used where significant loading is expected.
Abstract: The purpose of this research was to investigate the
creep behaviour of the heterogeneous Timber-UHPFRC beams. New
developments have been done to further improve the structural
performance, such as strengthening of the timber (glulam) beam by
bonding composite material combine with an ultra-high performance
fibre reinforced concrete (UHPFRC) internally reinforced with or
without carbon fibre reinforced polymer (CFRP) bars. However, in
the design of wooden structures, in addition to the criteria of
strengthening and stiffness, deformability due to the creep of wood,
especially in horizontal elements, is also a design criterion. Glulam,
UHPFRC and CFRP may be an interesting composite mix to respond
to the issue of creep behaviour of composite structures made of
different materials with different rheological properties. In this paper,
we describe an experimental and analytical investigation of the creep
performance of the glulam-UHPFRC-CFRP beams assembled by
bonding. The experimental investigations creep behaviour was
conducted for different environments: in- and outside under constant
loading for approximately a year. The measured results are compared
with numerical ones obtained by an analytical model. This model was
developed to predict the creep response of the glulam-UHPFRCCFRP
beams based on the creep characteristics of the individual
components. The results show that heterogeneous glulam-UHPFRC
beams provide an improvement in both the strengthening and
stiffness, and can also effectively reduce the creep deflection of
wooden beams.
Abstract: Thin-walled elements with a matrix set on a base of
high-valuable Portland cement with dispersed reinforcement from
alkali-resistant glass fibres are used in a range of applications as
claddings of buildings and infrastructure constructions as well as
various architectural elements of residential buildings.
Even though their elementary thickness and therefore total weight
is quite low, architects and building companies demand on even
further decreasing of the bulk density of these fibre-cement elements
for the reason of loading elimination of connected superstructures
and easier assembling in demand conditions.
By the means of various kinds of light-weight aggregates it is
possible to achieve light-weighing of these composite elements.
From the range of possible fillers with different material properties
granulated expanded glass worked the best.
By the means of laboratory testing an effect of two fillers based on
expanded glass on the fibre reinforced cement composite was
verified.
Practical applicability was tested in the production of commonly
manufactured glass fibre reinforced concrete elements, such as
channels for electrical cable deposition, products for urban equipment
and especially various cladding elements.
Even though these are not structural elements, it is necessary to
evaluate also strength characteristics and resistance to environment
for their durability in certain applications.
Abstract: The results reported in this paper are the part of an extensive laboratory investigation undertaken to study the effects of fibre parameters on the permeability and strength characteristics of steel fibre reinforced concrete (SFRC). The effect of varying fibre content and curing age on the water permeability, compressive and split tensile strengths of SFRC was investigated using straight steel fibres having an aspect ratio of 65. Samples containing three different weight fractions of 1.0%, 2.0% and 4.0% were cast and tested for permeability and strength after 7, 14, 28 and 60 days of curing. Plain concrete samples were also cast and tested for reference purposes.
Permeability was observed to decrease significantly with the addition of steel fibres and continued to decrease with increasing fibre content and increasing curing age. An exponential relationship was observed between permeability and compressive and split tensile strengths for SFRC as well as PCC. To evaluate the effect of fibre content on the permeability and strength characteristics, the Analysis of Variance (ANOVA) statistical method was used. An a level (probability of error) of 0.05 was used for ANOVA test. Regression analysis was carried out to develop relationship between permeability, compressive strength and curing age.
Abstract: Ten simply supported grossly underreinforced
tapered concrete beams of full size were tested upto complete
collapse under flexural effect .Out of 10 beams, 5 beams were
nonfibrous and the remaining beams contained fibres. The beams
had a variation in the tapered angle as 2°, 4°, 6°, 8° and 10°. The
concrete mix, conventional steel and the type of fibre used were
held constant. Flat corrugated steel fibres were utilized as
secondary reinforcement. The strength and stability parameters
were measured. It is established that the fibrous tapered beams can
be used economically in earthquake prone areas.
Abstract: Concrete pavement has superior durability and longer
structural life than asphalt pavement. Concrete pavement requires
less maintenance compared to asphalt pavement which requires maintenance and major rehabilitation. Use of the concrete pavement
has been grown over the past decade in developing countries. Fibre reinforced concrete (FRC) has been successfully used in design of concrete pavement in past decade. In this research, the effect of fibre
volume fraction in modulus of rupture, load-deflection, equivalent flexural strength (fe,3) and the equivalent flexural strength ratio (Re,3)
has been used in different fibre volume fraction. Crimped-type flat
steel fibre of size 50 x 2.0 x 0.6 mm was used with 1.0%, 1.5% and 2.0% volume fraction. Beam specimens of size 500 x 100 x 100 mm were used for flexural as well as with JCI method for analysis flexural toughness, equivalent flexural strength. It was obtained as the 2% fibre volume fractions; reduce 45% of the concrete pavement
thickness.
Abstract: The article presents findings from the study and
analysis of the results of an experimental programme focused on the
production of concrete and fibre reinforced concrete in which natural
aggregate has been substituted with brick or concrete recyclate. The
research results are analyzed to monitor the effect of mechanicalphysical
characteristics on the durability properties of tested
cementitious composites. The key parts of the fibre reinforced
concrete mix are the basic components: aggregates – recyclate,
cement, fly ash, water and fibres. Their specific ratios and the
properties of individual components principally affect the resulting
behaviour of fresh fibre reinforced concrete and the characteristics of
the final product. The article builds on the sources dealing with the
use of recycled aggregates from construction and demolition waste in
the production of fibre reinforced concrete. The implemented
procedure of testing the composite contributes to the building
sustainability in environmental engineering.
Abstract: In this study, the thermal and mechanical properties of
basalt fibre reinforced concrete were investigated. The volume
fractions of basalt fibre of (0.1, 0.2, 0.3, and 0.5% by total mix
volume) were used. Properties such as heat transfer, compressive and
splitting tensile strengths were examined. Results indicated that the
strength increases with increase the fibre content till 0.3% then there
is a slight reduction when 0.5% fibre used. Lower amount of heat
conducted through the thickness of concrete specimens than the
conventional concrete was also recorded.
Abstract: This paper in essence presents comparative
experimental data on the mechanical performance of steel and
synthetic fibre-reinforced concrete under compression, tensile split
and flexure. URW1050 steel fibre and HPP45 synthetic fibre, both
with the same concrete design mix, have been used to make cube
specimens for a compression test, cylinders for a tensile split test and
beam specimens for a flexural test. The experimental data
demonstrated steel fibre reinforced concrete to be stronger in flexure
at early stages, whilst both fibre reinforced concrete types displayed
comparatively the same performance in compression, tensile splitting
and 28-day flexural strength. In terms of post-crack controlHPP45
was preferable.