Abstract: The purpose of this research was to investigate the
creep behaviour of the heterogeneous Timber-UHPFRC beams. New
developments have been done to further improve the structural
performance, such as strengthening of the timber (glulam) beam by
bonding composite material combine with an ultra-high performance
fibre reinforced concrete (UHPFRC) internally reinforced with or
without carbon fibre reinforced polymer (CFRP) bars. However, in
the design of wooden structures, in addition to the criteria of
strengthening and stiffness, deformability due to the creep of wood,
especially in horizontal elements, is also a design criterion. Glulam,
UHPFRC and CFRP may be an interesting composite mix to respond
to the issue of creep behaviour of composite structures made of
different materials with different rheological properties. In this paper,
we describe an experimental and analytical investigation of the creep
performance of the glulam-UHPFRC-CFRP beams assembled by
bonding. The experimental investigations creep behaviour was
conducted for different environments: in- and outside under constant
loading for approximately a year. The measured results are compared
with numerical ones obtained by an analytical model. This model was
developed to predict the creep response of the glulam-UHPFRCCFRP
beams based on the creep characteristics of the individual
components. The results show that heterogeneous glulam-UHPFRC
beams provide an improvement in both the strengthening and
stiffness, and can also effectively reduce the creep deflection of
wooden beams.
Abstract: Biopolymers have gained much attention as ecofriendly alternatives to petrochemical-based plastics because they are biodegradable and can be produced from renewable feedstocks. One class of biopolyester with many potential environmentally
friendly applications is polylactic acid (PLA) and polycaprolactone (PCL). The PLA/PCL biodegradable copolyesters were synthesized by bulk ring-opening copolymerization of successively added Llactide (LL) and ε-caprolactone (CL) in the presence of toluene, using 1-hexanol as initiator and stannous octoate (Sn(Oct)2) as catalyst. Reaction temperature, reaction time and amount of catalyst were evaluated to obtain optimum reaction conditions. The results showed that the %conversion increased with increases in reaction temperature and reaction time, but after a critical amount of catalyst was reached the %conversion decreased. The yield of PLA/PCL biopolymer achieved 98.02% at the reaction temperature 160 °C, amount of catalyst 0.3 mol% and reaction time of 48 h. In addition, the thermal properties of the product were determined by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA).