Abstract: The goal of this work is to develop sustainable and durable ceramic cellular structures using widely available natural resources- clay and milled waste glass. Present paper describes method of obtaining clay ceramic foam (CCF) with addition of milled waste glass in 5, 7 and 10 wt% by direct foaming with high speed mixer-disperser (HSMD). For more efficient clay and waste glass milling and mixing, the high velocity disintegrator was used. The CCF with 5, 7, and 10 wt% were obtained at 900, 950, 1000 and 1050 °C firing temperature and they have demonstrated mechanical compressive strength for all 12 samples ranging from 3.8 to 14.3 MPa and porosity 76-65%. Obtained CCF has compressive strength 14.3 MPa and porosity 65.3%.
Abstract: Present paper describes method of obtaining clay
ceramic foam (CCF) and foam concrete (FC), by direct foaming with
high speed mixer-disperser (HSMD). Three foaming agents (FA) are
compared for the FC and CCF production: SCHÄUMUNGSMITTEL
W 53 FLÜSSIG (Zschimmer & Schwarz Gmbh, Germany), SCF-
1245 (Sika, test sample, Latvia) and FAB-12 (Elade, Latvija). CCF
were obtained at 950, 1000°C, 1150°C and 1150°C firing temperature
and have mechanical compressive strength 1.2, 2.55 and 4.3 MPa and
porosity 79.4, 75.1, 71.6%, respectively. Obtained FC has 6-14 MPa
compressive strength and porosity 44-55%. The goal of this work
was development of a sustainable and durable ceramic cellular
structures using HSMD.