Abstract: In this study, WC-Ni-based cemented carbides having different nickel contents were used as the substrate for cutting tool materials. Hardened steel was turned by a (Ti,W,Si)N-coated WC-Ni-based cemented carbide tool, and the tool wear was experimentally investigated. The following results were obtained: (1) In the (Ti,W,Si)N-coated WC-Ni-based cemented carbide, the hardness of the coating film was not much different from the content of the binding material, Ni, and the adhesion strength increased with a decrease in Ni content. (2) There is little difference between the wear progress of the (Ti,W,Si)N-coated WC-7%Ni-based cemented carbide tool and that of the (Ti,W,Si)N-coated WC-6%Co-based cemented carbide tool. (3) The wear progress of the (Ti,W,Si)N-coated WC-Ni-based cemented carbide became slower with a decrease in Ni content.
From the above, it is has become clear that WC-Ni-based cemented carbide can be used as a substrate for cutting tool materials.
Abstract: A judicious choice of insert material, tool geometry and
cutting conditions can make hard turning produce better surfaces than
grinding. In the present study, an attempt has been made to
investigate the effect of cutting tool materials on cutting forces (feed
force, thrust force and cutting force) in finish hard turning of AISI
D2 cold work tool steel. In conclusion of the results obtained with a
constant depth of cut and feed rate, it is important to note that cutting
force is directly affected by cutting tool material.