Abstract: The exemplary mechanical performance and durability of ultra-high performance concrete (UHPC) has led to its rapid emergence as an advanced cementitious material. The uncharacteristically high mechanical strength and ductility of UHPC makes it a promising potential material for defense structures which may be subject to highly dynamic loads like impact or blast. However, the mechanical response of UHPC under dynamic loading has not been fully characterized. In particular, there is a need to characterize the energy absorption of UHPC under high-frequency shear loading. This paper presents preliminary results from a parametric study of the dynamic shear energy absorption of UHPC using the Charpy impact test. UHPC mixtures with compressive strengths in the range of 100-150 MPa exhibited dynamic shear energy absorption in the range of 0.9-1.5 kJ/m. Energy absorption is shown to be sensitive to the water/cement ratio, silica fume content, and aggregate gradation. Energy absorption was weakly correlated to compressive strength. Results are highly sensitive to specimen preparation methods, and there is a demonstrated need for a standardized test method for high frequency shear in cementitious composites.
Abstract: In this study, first thermoplastic composite materials
/plates that have high ballistic impact resistance were produced. For
this purpose, the thermoplastic prepreg and the vacuum bagging
technique were used to produce a composite material. Thermoplastic
prepregs (resin-impregnated fiber) that are supplied ready to be used,
namely high-density polyethylene (HDPE) was chosen as matrix and
unidirectional glass fiber was used as reinforcement. In order to
compare the fiber configuration effect on mechanical properties,
unidirectional and biaxial prepregs were used. Then the
microstructural properties of the composites were investigated with
scanning electron microscopy (SEM) analysis. Impact properties of
the composites were examined by Charpy impact test and tensile
mechanical tests and then the effects of ultraviolet irradiation were
investigated on mechanical performance.
Abstract: Three dimensional non-Interlaced carbon fibre
reinforced silicon carbide (3-D-Cf/SiC) composites with pyrocarbon
interphase were fabricated using isothermal chemical vapor
infiltration (ICVI) combined with polymer impregnation pyrolysis
(PIP) process. Polysilazane (PSZ) is used as a preceramic polymer to
obtain silicon carbide matrix. Thermo gravimetric analysis (TGA),
Infrared spectroscopic analysis (IR) and X-ray diffraction (XRD)
analysis were carried out on PSZ pyrolysed at different temperatures
to understand the pyrolysis and obtaining the optimum pyrolysing
condition to yield β-SiC phase. The density of the composites was
1.94 g cm-3 after the 3-D carbon preform was SiC infiltrated for 280 h
with one intermediate polysilazane pre-ceramic PIP process.
Mechanical properties of the composite materials were investigated
under tensile, flexural, shear and impact loading. The values of
tensile strength were 200 MPa at room temperature (RT) and 195
MPa at 500°C in air. The average RT flexural strength was 243 MPa.
The lower flexural strength of these composites is because of the
porosity. The fracture toughness obtained from single edge notched
beam (SENB) technique was 39 MPa.m1/2. The work of fracture
obtained from the load-displacement curve of SENB test was 22.8
kJ.m-2. The composites exhibited excellent impact resistance and the
dynamic fracture toughness of 44.8 kJ.m-2 is achieved as determined
from instrumented Charpy impact test. The shear strength of the
composite was 93 MPa, which is significantly higher compared 2-D
Cf/SiC composites. Microstructure evaluation of fracture surfaces
revealed the signatures of fracture processes and showed good
support for the higher toughness obtained.