Abstract: Resistance spot welding (RSW) has been used widely to join sheet metals. It has been a challenge to get required weld quality in spot welding of dissimilar thickness materials. Weld parameters are not generally available in standards for thickness beyond 4mm. This paper presents the welding process design and parameter optimization of RSW used in joining of low carbon steel sheet of thickness 0.8 mm and metal strips of cross section 10 x 5mm for electrical motor applications. Taguchi quality design was adopted for weld current and time optimization using L9 orthogonal array. Optimum process parameters (current- 3.5kA and time- 10 cycles) were obtained from the Taguchi analysis and shear test results. Confirmation experiment result revealed that the weld quality was within acceptable interval. Further, numerical simulation of RSW process was carried out with selected weld parameters to quantify the temperature at faying surface and check for formation of appropriate nugget. The nugget geometry measured after peel test and predicted from numerical validation method were similar and in accordance with the standards.
Abstract: The objective of this project is to study the corrosion
behaviour and hardness based on the presence of martensite in dual
phase steel. This study was conducted on six samples of dual phase
steel which have different percentage of martensite. A total of 9
specimens were prepared by intercritical annealing process to study
the effect of temperature to the formation of martensite. The low
carbon steels specimens were heated for 25 minutes in a specified
temperature ranging from 7250C to 8250C followed by rapid cooling
in water. The measurement of corrosion rate was done by using
extrapolation tafel method, while potentiostat was used to control and
measured the current produced. This measurement is performed
through a system named CMS105. The result shows that a specimen
with higher percentage of martensite is likely to corrode faster.
Hardness test for each specimen was conducted to compare its
hardness with low carbon steel. The results obtained indicate that the
specimen hardness is proportional to the amount of martensite in dual
phase steel.
Abstract: Constant amplitude fatigue crack growth (FCG) tests
were performed on dissimilar metal welded plates of Type 316L
Stainless Steel (SS) and IS 2062 Grade A Carbon steel (CS). The
plates were welded by TIG welding using SS E309 as electrode. FCG
tests were carried on the Side Edge Notch Tension (SENT)
specimens of 5 mm thickness, with crack initiator (notch) at base
metal region (BM), weld metal region (WM) and heat affected zones
(HAZ). The tests were performed at a test frequency of 10 Hz and at
load ratios (R) of 0.1 & 0.6. FCG rate was found to increase with
stress ratio for weld metals and base metals, where as in case of
HAZ, FCG rates were almost equal at high ΔK. FCG rate of HAZ of
stainless steel was found to be lowest at low and high ΔK. At
intermediate ΔK, WM showed the lowest FCG rate. CS showed
higher crack growth rate at all ΔK. However, the scatter band of data
was found to be narrow. Fracture toughness (Kc) was found to vary
in different locations of weldments. Kc was found lowest for the
weldment and highest for HAZ of stainless steel. A novel method of
characterizing the FCG behavior using an Infrared thermography
(IRT) camera was attempted. By monitoring the temperature rise at
the fast moving crack tip region, the amount of plastic deformation
was estimated.
Abstract: Carbon steel is used in boilers, pressure vessels, heat
exchangers, piping, structural elements and other moderatetemperature
service systems in which good strength and ductility are
desired. ASME Boiler and Pressure Vessel Code, Section II Part A
(2004) provides specifications of ferrous materials for construction of
pressure equipment, covering wide range of mechanical properties
including high strength materials for power plants application.
However, increased level of springback is one of the major problems
in fabricating components of high strength steel using bending.
Presented work discuss the springback simulations for five different
steels (i.e. SA-36, SA-299, SA-515 grade 70, SA-612 and SA-724
grade B) using finite element analysis of air V-bending. Analytical
springback simulations of hypothetical layered materials are
presented. Result shows that; (i) combination of the material property
parameters controls the springback, (ii) layer of the high ductility
steel on the high strength steel greatly suppresses the springback.
Abstract: This paper presents an experimental investigation on
the machinability of laser-sintered material using small ball end mill focusing on wear mechanisms. Laser-sintered material was produced
by irradiating a laser beam on a layer of loose fine SCM-Ni-Cu powder. Bulk carbon steel JIS S55C was selected as a reference steel.
The effects of powder consolidation mechanisms and unsintered
powder on the tool life and wear mechanisms were carried out. Results indicated that tool life in cutting laser-sintered material is
lower than that in cutting JIS S55C. Adhesion of the work material and chipping were the main wear mechanisms of the ball end mill in
cutting laser-sintered material. Cutting with the unsintered powder
surrounding the tool and laser-sintered material had caused major fracture on the cutting edge.
Abstract: A study of the H-beam's nanosize structure phase
states after thermomechanical strengthening was carried out by TEM.
The following processes were analyzed. 1. The dispersing of the
cementite plates by cutting them by moving dislocations. 2. The
dissolution of cementite plates and repeated precipitation of the
cementite particles on the dislocations, the boundaries, subgrains and
grains. 3. The decay of solid solution of carbon in the α-iron after
"self-tempering" of martensite. 4. The final transformation of the
retained austenite in beinite with α-iron particles and cementite
formation. 5. The implementation of the diffusion mechanism of γ ⇒
α transformation.
Abstract: The aim of this paper is to compare the effectiveness and electrochemical behavior of typical oilfield corrosion inhibitors with previous oilfield corrosion inhibitors under the same electrochemical techniques to control preferential weld corrosion of X65 pipeline steel in artificial seawater saturated with carbon dioxide at a pressure of one bar. A secondary aim is to investigate the conditions under which current reversal takes place. A flow channel apparatus was used in the laboratory to simulate the actual condition that occurs in marine pipelines. Different samples from the parent metal, the weld metal and the heat affected zone in the pipeline steel were galvanically coupled. The galvanic currents flowing between the weld regions were recorded using zero-resistance ammeters and tested under static and flowing conditions in both inhibited and uninhibited media. The results show that a current reversal took place when 30ppm of both green oilfield inhibitors were present, resulting in accelerated weld corrosion.
Abstract: In this study acoustic emission (AE) signals obtained during deformation and fracture of two types of ferrite-martensite dual phase steels (DPS) specimens have been analyzed in frequency domain. For this reason two low carbon steels with various amounts of carbon were chosen, and intercritically heat treated. In the introduced method, identifying the mechanisms of failure in the various phases of DPS is done. For this aim, AE monitoring has been used during tensile test of several DPS with various volume fraction of the martensite (VM) and attempted to relate the AE signals and failure mechanisms in these steels. Different signals, which referred to 2-3 micro-mechanisms of failure due to amount of carbon and also VM have been seen. By Fast Fourier Transformation (FFT) of signals in distinct locations, an excellent relationship between peak frequencies in these areas and micro-mechanisms of failure were seen. The results were verified by microscopic observations (SEM).
Abstract: The paper presents the results of microhardness and
microstructure of low carbon steel surface melted using carbon
dioxide laser with a wavelength of 10.6μm and a maximum output
power of 2000W. The processing parameters such as the laser power,
and the scanning rate were investigated in this study. After surface
melting two distinct regions formed corresponding to the melted zone
MZ, and the heat affected zone HAZ. The laser melted region
displayed a cellular fine structures while the HAZ displayed
martensite or bainite structure. At different processing parameters,
the original microstructure of this steel (Ferrite+Pearlite) has been
transformed to new phases of martensitic and bainitic structures. The
fine structure and the high microhardness are evidence of the high
cooling rates which follow the laser melting. The melting pool and
the transformed microstructure in the laser surface melted region of
carbon steel showed clear dependence on laser power and scanning
rate.
Abstract: Most buildings have been using anchor bolts
commonly for installing outdoor advertising structures. Anchor bolts
of common carbon steel are widely used and often installed
indiscriminately by inadequate installation standards. In the area
where strong winds frequently blow, falling accidents of outdoor
advertising structures can occur and cause a serious disaster, which is
very dangerous and to be prevented. In this regard, the development of
high-performance anchor bolts is urgently required. In the present
study, 25Cr-8Ni-1.5Si-1Mn-0.4C alloy was produced by traditional
vacuum induction melting (VIM) for the application of anchor bolt.
The alloy composition is revealed as a duplex microstructure from
thermodynamic phase analysis by FactSage® and confirmed by
metallographic experiment. Addition of Nitrogen to the alloy was
found to reduce the ferritic phase domain and significantly increase the
hardness and the tensile strength. Microstructure observation revealed
mixed structure of austenite and ferrite with fine carbide distributed
along the grain and phase boundaries.
Abstract: Dual phase steels (DPS)s have a microstructure
consisting of a hard second phase called Martensite in the soft Ferrite
matrix. In recent years, there has been interest in dual-phase steels,
because the application of these materials has made significant usage;
particularly in the automotive sector Composite microstructure of
(DPS)s exhibit interesting characteristic mechanical properties such
as continuous yielding, low yield stress to tensile strength
ratios(YS/UTS), and relatively high formability; which offer
advantages compared with conventional high strength low alloy
steels(HSLAS). The research dealt with the characterization of
damage in (DPS)s. In this study by review the mechanisms of failure
due to volume fraction of martensite second phase; a new method is
introduced to identifying the mechanisms of failure in the various
phases of these types of steels. In this method the acoustic emission
(AE) technique was used to detect damage progression. These failure
mechanisms consist of Ferrite-Martensite interface decohesion and/or
martensite phase fracture. For this aim, dual phase steels with
different volume fraction of martensite second phase has provided by
various heat treatment methods on a low carbon steel (0.1% C), and
then AE monitoring is used during tensile test of these DPSs. From
AE measurements and an energy ratio curve elaborated from the
value of AE energy (it was obtained as the ratio between the strain
energy to the acoustic energy), that allows detecting important
events, corresponding to the sudden drops. These AE signals events
associated with various failure mechanisms are classified for ferrite
and (DPS)s with various amount of Vm and different martensite
morphology. It is found that AE energy increase with increasing Vm.
This increasing of AE energy is because of more contribution of
martensite fracture in the failure of samples with higher Vm. Final
results show a good relationship between the AE signals and the
mechanisms of failure.
Abstract: A way of achieving nanodimentional structural elements in high carbon steel by special kind of heat treatment and cold plastic deformation is being explored. This leads to increasing interlamellar spacing of ferrite-carbide mixture. Decreasing the interlamellar spacing with cooling temperature increasing is determined. Experiments confirm such interlamellar spacing with which high carbon steel demonstrates the highest treatment and hardening capability. Total deformation degree effect on interlamellar spacing value in a ferrite-carbide mixture is obtained. Mechanical experiments results show that high carbon steel after heat treatment and repetitive cold plastic deformation possesses high tensile strength and yield strength keeping good percentage elongation.
Abstract: In this work, bending fatigue life of notched
specimens with various notch geometries and dimensions is
investigated by experiment and Manson-Caffin theoretical method. In
this theoretical method, fatigue life of notched specimens is
calculated using the fatigue life obtained from the experiments for
plain specimens (without notch). Three notch geometries including
∪-shape, ∨-shape and C -shape notches are considered in this
investigation. The experiments are conducted on a rotary bending
Moore machine. The specimens are made of a low carbon steel alloy,
which has wide application in industry. The stress- life curves are
captured for all notched specimen by experiment. The results indicate
that Manson-Caffin analytical method cannot adequately predict
the fatigue life of notched specimen. However, it seems that the
difference between the experiments and Manson-Caffin predictions
can be compensated by a proportional factor.
Abstract: This paper reports the evolving properties of a 3 mm low carbon steel plate after Laser Beam Forming achieve this objective, the chemical analyse material and the formed components were carried thereafter both were characterized through microhardness profiling microstructural evaluation and tensile testing. showed an increase in the elemental concentration of the component when compared to the as received attributed to the enhancement property of the LBF process Ultimate Tensile Strength (UTS) and the Vickers the formed component shows an increase when compared to the as received material, this was attributed to strain hardening and grain refinement brought about by the LBF process. The microstructure of the as received steel consists of equiaxed ferrit that of the formed component exhibits elongated orming process (LBF). To es of the as received out and compared; profiling, The chemical analyses formed material; this can be process. The microhardness of ferrite and pearlite while grains.
Abstract: The aim of this research is to evaluate surface
roughness and develop a multiple regression model for surface roughness as a function of cutting parameters during the turning of
flame hardened medium carbon steel with TiN-Al2O3-TiCN coated inserts. An experimental plan of work and signal-to-noise ratio (S/N)
were used to relate the influence of turning parameters to the
workpiece surface finish utilizing Taguchi methodology. The effects
of turning parameters were studied by using the analysis of variance (ANOVA) method. Evaluated parameters were feed, cutting speed,
and depth of cut. It was found that the most significant interaction among the considered turning parameters was between depth of cut and feed. The average surface roughness (Ra) resulted by TiN-Al2O3-
TiCN coated inserts was about 2.44 μm and minimum value was 0.74 μm. In addition, the regression model was able to predict values for surface roughness in comparison with experimental values within
reasonable limit.
Abstract: The objective of present work is to stimulate the
machining of material by electrical discharge machining (EDM) to
give effect of input parameters like discharge current (Ip), pulse on
time (Ton), pulse off time (Toff) which can bring about changes in the
output parameter, i.e. material removal rate. Experimental data was
gathered from die sinking EDM process using copper electrode and
Medium Carbon Steel (AISI 1040) as work-piece. The rules of
membership function (MF) and the degree of closeness to the
optimum value of the MMR are within the upper and lower range of
the process parameters. It was found that proposed fuzzy model is in
close agreement with the experimental results. By Intelligent, model
based design and control of EDM process parameters in this study
will help to enable dramatically decreased product and process
development cycle times.
Abstract: Solidification cracking and hydrogen cracking are some defects generated in the fusion welding of ultrahigh carbon steels. However, friction stir welding (FSW) of such steels, being a solid-state technique, has been demonstrated to alleviate such problems encountered in traditional welding. FSW include different process parameters that must be carefully defined prior processing. These parameters included but not restricted to: tool feed, tool RPM, tool geometry, tool tilt angle. These parameters form a key factor behind avoiding warm holes and voids behind the tool and in achieving a defect-free weld. More importantly, these parameters directly affect the microstructure of the weld and hence the final mechanical properties of weld. For that, 3D finite element (FE) thermo-mechanical model was developed using DEFORM 3D to simulate FSW of carbon steel. At points of interest in the joint, tracking is done for history of critical state variables such as temperature, stresses, and strain rates. Typical results found include the ability to simulate different weld zones. Simulations predictions were successfully compared to experimental FSW tests. It is believed that such a numerical model can be used to optimize FSW processing parameters to favor desirable defect free weld with better mechanical properties.
Abstract: This article presents the simulation, parameterization and optimization of an electromagnet with the C–shaped configuration, intended for the study of magnetic properties of materials. The electromagnet studied consists of a C-shaped yoke, which provides self–shielding for minimizing losses of magnetic flux density, two poles of high magnetic permeability and power coils wound on the poles. The main physical variable studied was the static magnetic flux density in a column within the gap between the poles, with 4cm2 of square cross section and a length of 5cm, seeking a suitable set of parameters that allow us to achieve a uniform magnetic flux density of 1x104 Gaussor values above this in the column, when the system operates at room temperature and with a current consumption not exceeding 5A. By means of a magnetostatic analysis by the finite element method, the magnetic flux density and the distribution of the magnetic field lines were visualized and quantified. From the results obtained by simulating an initial configuration of electromagnet, a structural optimization of the geometry of the adjustable caps for the ends of the poles was performed. The magnetic permeability effect of the soft magnetic materials used in the poles system, such as low– carbon steel (0.08% C), Permalloy (45% Ni, 54.7% Fe) and Mumetal (21.2% Fe, 78.5% Ni), was also evaluated. The intensity and uniformity of the magnetic field in the gap showed a high dependence with the factors described above. The magnetic field achieved in the column was uniform and its magnitude ranged between 1.5x104 Gauss and 1.9x104 Gauss according to the material of the pole used, with the possibility of increasing the magnetic field by choosing a suitable geometry of the cap, introducing a cooling system for the coils and adjusting the spacing between the poles. This makes the device a versatile and scalable tool to generate the magnetic field necessary to perform magnetic characterization of materials by techniques such as vibrating sample magnetometry (VSM), Hall-effect, Kerr-effect magnetometry, among others. Additionally, a CAD design of the modules of the electromagnet is presented in order to facilitate the construction and scaling of the physical device.