Abstract: This work describes an investigation on the effect of filler metals diameter to weld joint, and low alloy carbon steel A516 Grade 70 is the base metal. Commercially SA516 Grade70 is frequently used for the manufacturing of pressure vessels, boilers and storage tank, etc. In fabrication industry, the hardness of the weld joint is between the important parameters to check, after heat treatment of the weld. Submerged arc welding (SAW) is used with two filler metal diameters, and this solid wire electrode is used for SAW non-alloy and for fine grain steels (SFA 5.17). The different diameters were selected (Ø = 2.4 mm and Ø = 4 mm) to weld two specimens. Both specimens were subjected to the same preparation conditions, heat treatment, macrograph, metallurgy micrograph, and micro-hardness test. Samples show almost similar structure with highest hardness. It is important to indicate that the thickness used in the base metal is 22 mm, and all specifications, preparation and controls were according to the ASME section IX. It was observed that two different filler metal diameters performed on two similar specimens demonstrated that the mechanical property (hardness) increases with decreasing diameter. It means that even the heat treatment has the same effect with the same conditions, the filler metal diameter insures a depth weld penetration and better homogenization. Hence, the SAW welding technique mentioned in the present study is favorable to implicate for the industry using the small filler metal diameter.
Abstract: In recent years, the failure accidents in petrochemical industry have been frequent, and have posed great security problems in personnel and property. The improvement of petrochemical safety is highly requested in order to prevent re-occurrence of severe accident. This study focuses on surveying the failure cases occurred in petrochemical field, which were extracted from journals of engineering failure, including engineering failure analysis and case studies in engineering failure analysis. The relation of failure mode, failure mechanism, type of components, and type of materials was analyzed in this study. And the analytical results showed that failures occurred more frequently in vessels and piping among the petrochemical equipment. Moreover, equipment made of carbon steel and stainless steel accounts for the majority of failures compared to other materials. This may be related to the application of the equipment and the performance of the material. In addition, corrosion failures were the largest in number of occurrence in the failure of petrochemical equipment, in which stress corrosion cracking accounts for a large proportion. This may have a lot to do with the service environment of the petrochemical equipment. Therefore, it can be concluded that the corrosion prevention of petrochemical equipment is particularly important.
Abstract: Dual-phase high carbon steels (DHCS) are commonly known for their improved strength, hardness, and abrasive resistance properties due to co-presence of retained austenite and martensite at the same time. Retained austenite is a meta-stable phase at room temperature, and stability of this phase governs the response of DHCS at different conditions. This research paper studies the effect of RA stability on corrosion behaviour of high carbon steels after they have been immersed into 1.0 M NaCl solution for various times. For this purpose, two different steels with different RA stabilities have been investigated. The surface morphology of the samples before and after corrosion attack was observed by secondary electron microscopy (SEM) and atomic force microscopy (AFM), along with the weight loss and Vickers hardness analysis. Microstructural investigations proved the preferential attack to retained austenite phase during corrosion. Hence, increase in the stability of retained austenite in dual-phase steels led to decreasing the weight loss rate.
Abstract: Thermo-mechanical processing with various processing parameters was applied to 0.2%C-0.6%Mn-2S%i-0.8%Cr low alloyed high strength steel. The aim of the processing was to achieve the microstructures typical for transformation induced plasticity (TRIP) steels. Thermo-mechanical processing used in this work incorporated two or three deformation steps. The deformations were in all the cases carried out during the cooling from soaking temperatures to various bainite hold temperatures. In this way, 4-10% of retained austenite were retained in the final microstructures, consisting further of ferrite, bainite, martensite and pearlite. The complex character of TRIP steel microstructure is responsible for its good strength and ductility. The strengths achieved in this work were in the range of 740 MPa – 836 MPa with ductility A5mm of 31-41%.
Abstract: The main object of this paper is to present the research results of the development of a hybrid stainless steel girder system for bridge construction undertaken at University of Ryukyu. In order to prevent the corrosion damage and reduce the fabrication costs, a hybrid stainless steel girder in bridge construction is developed, the stainless steel girder of which is stiffened and braced by structural carbon steel materials. It is verified analytically and experimentally that the ultimate strength of the hybrid stainless steel girder is equal to or greater than that of conventional carbon steel girder. The benefit of the life-cycle cost of the hybrid stainless steel girder is also shown.
Abstract: The iron content of the ore used is crucial for the productivity and coke consumption rate in blast furnace pig iron production. Therefore, most iron ore deposits are processed in beneficiation plants to increase the iron content and remove impurities. In several comminution stages, the particle size of the ore is reduced to ensure that the iron oxides are physically liberated from the gangue. Subsequently, physical separation processes are applied to concentrate the iron ore. The fine-grained ore concentrates produced need to be transported, stored, and processed. For smooth operation of these processes, the flow properties of the material are crucial. The flowability of powders depends on several properties of the material: grain size, grain size distribution, grain shape, and moisture content of the material. The flowability of powders can be measured using ring shear testers. In this study, the influence of the moisture content on the flowability for the Krivoy Rog magnetite iron ore concentrate was investigated. Dry iron ore concentrate was mixed with varying amounts of water to produce samples with a moisture content in the range of 0.2 to 12.2%. The flowability of the samples was investigated using a Schulze ring shear tester. At all measured values of the normal stress (1.0 kPa – 20 kPa), the flowability decreased significantly from dry ore to a moisture content of approximately 3-5%. At higher moisture contents, the flowability was nearly constant, while at the maximum moisture content the flowability improved for high values of the normal stress only. The results also showed an improving flowability with increasing consolidation stress for all moisture content levels investigated. The wall friction angle of the dust with carbon steel (S235JR), and an ultra-high molecule low-pressure polyethylene (Robalon) was also investigated. The wall friction angle increased significantly from dry ore to a moisture content of approximately 3%. For higher moisture content levels, the wall friction angles were nearly constant. Generally, the wall friction angle was approximately 4° lower at the higher wall normal stress.
Abstract: Corrosion problem which exists in every stage of oil and gas production has been a great challenge to the operators in the industry. The conventional carbon steel with all its inherent advantages has been adjudged susceptible to the aggressive corrosion environment of oilfield. This has aroused increased interest in the use of micro alloyed steels for oil and gas production and transportation. The corrosion behavior of three commercially supplied micro alloyed steels designated as A, B, and C have been investigated with API 5L X65 as reference samples. Electrochemical corrosion tests were conducted in an unbuffered 3.5 wt% NaCl solution saturated with CO2 at 30 0C for 24 hours. Pre-corrosion analyses revealed that samples A, B and X65 consist of ferrite-pearlite microstructures but with different grain sizes, shapes and distribution whereas sample C has bainitic microstructure with dispersed acicular ferrites. The results of the electrochemical corrosion tests showed that within the experimental conditions, the corrosion rate of the samples can be ranked as CR(A)< CR(X65)< CR(B)< CR(C). These results are attributed to difference in microstructures of the samples as depicted by ASTM grain size number in accordance with ASTM E112-12 Standard and ferrite-pearlite volume fractions determined by ImageJ Fiji grain size analysis software.
Abstract: In this work, effects of the friction and truncation on the dynamics of a double-cone gravitational motor, self-propelled on a straight V-shaped horizontal rail, are evaluated. Such mechanism has a variable radius of contact, and, on one hand, it is similar to a pulley mechanism that changes the potential energy into the kinetic energy of rotation, but on the other hand, it is similar to a pendulum mechanism that converts the potential energy of the suspended body into the kinetic energy of translation along a circular path. Movies of the self- propelled double-cones, made of S45C carbon steel and wood, along rails made of aluminum alloy, were shot for various opening angles of the rails. Kinematical features of the double-cones were estimated through the slow-motion processing of the recorded movies. Then, a kinematical model is derived under assumption that the distance traveled by the contact points on the rectilinear rails is identical with the distance traveled by the contact points on the truncated conical surface. Additionally, a dynamic model, for this particular contact problem, was proposed and validated against the experimental results. Based on such model, the traction force and the traction torque acting on the double-cone are identified. One proved that the rolling traction force is always smaller than the sliding friction force; i.e., the double-cone is rolling without slipping. Results obtained in this work can be used to achieve the proper design of such gravitational motor.
Abstract: The numerical simulation based on the Finite Element Method (FEM) is widely used in academic institutes and in the industry. It is a useful tool to predict many phenomena present in the classical manufacturing forming processes such as fracture. But, the results of such numerical model depend strongly on the parameters of the constitutive behavior model. The influences of thermal and mechanical loads cause damage. The temperature and strain rate dependent materials’ properties and their modelling are discussed. A Johnson-Cook Model of damage has been selected for the numerical simulations. Virtual software called the ABAQUS 6.11 is used for finite element analysis. This model was introduced in order to give information concerning crack initiation during thermal and mechanical loads.
Abstract: Optimisation of the physical and mechanical properties of cold rolled thin strips is achieved by controlling the rolling parameters. In this paper, the factors affecting the asymmetrical cold rolling of thin low carbon steel strip have been studied at a speed ratio of 1.1 without lubricant applied. The effect of rolling parameters on the resulting microstructure was also investigated. It was found that under dry condition, work roll shifting and work roll cross angle can improve the strip profile, and the result is more significant with an increase of work roll cross angle rather than that of work roll shifting. However, there was no obvious change in microstructure. In addition, effects of rolling parameters on strip profile and microstructure have also been discussed.
Abstract: A model to predict the plastic zone size for material
under plane stress condition has been developed and verified
experimentally. The developed model is a function of crack size,
crack angle and material property (dislocation density). Simulation
and validation results show that the model developed show good
agreement with experimental results. Samples of low carbon steel
(0.035%C) with included surface crack angles of 45o, 50o, 60o, 70o
and 90o and crack depths of 2mm and 4mm were subjected to low
strain rate between 0.48 x 10-3 s-1 – 2.38 x 10-3 s-1. The mechanical
properties studied were ductility, tensile strength, modulus of
elasticity, yield strength, yield strain, stress at fracture and fracture
toughness. The experimental study shows that strain rate has no
appreciable effect on the size of plastic zone while crack depth and
crack angle plays an imperative role in determining the size of the
plastic zone of mild steel materials.
Abstract: This research paper portrays a comparative analysis of
thermomechanical behaviour of Shielded Metal Arc Welding
(SMAW) and Gas Tungsten Arc Welding (GTAW) of low carbon
steel of AISI 1020 grade butt joints. The thermal history has been
obtained by experimental work. We have focused on temperature
dependent cooling rate as depicted by Adam’s two-dimensional
model. The effect of moving point heat source of SMAW and GTAW
on mechanical properties has been judged by optical and scanning
electron micrographs of different regions in weld joints. The
microhardness study has been carried to visualize the joint strength
due to formation of different phases.
Abstract: The present work is aimed at examining carbon steel
oil pipelines corrosion using three natural extracts (Eruca Sativa,
Rosell and Mango peels) that are used as inhibitors of different
concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds
are used as corrosion mediums. Weight loss method was used for
measuring the corrosion rate of the carbon steel specimens immersed
in technical white oil at 100ºC at various time intervals in absence
and presence of the two sulphur compounds. The corroded specimens
are examined using the chemical wear test, scratch test and hardness
test. The scratch test is carried out using scratch loads from 0.5 Kg to
2.0 Kg. The scratch width is obtained at various scratch load and test
conditions. The Brinell hardness test is carried out and investigated
for both corroded and inhibited specimens. The results showed that
three natural extracts can be used as environmentally friendly
corrosion inhibitors.
Abstract: In the present study, the properties of Al-Al2O3
nanocomposite hollow sphere structures were investigated. For this
reason, the Al-based nanocomposite hollow spheres with different
amounts of nano-alumina reinforcement (0-10wt %) and different
ratio of thickness to diameter (t/D: 0.06-0.3) were prepared via a
powder metallurgy method. Then, the effect of mentioned parameters
was studied on physical and quasi static mechanical properties of
their related prepared structures (open/closed cell) such as density,
hardness, strength, and energy absorption. It was found that, as the
t/D ratio increases the relative density, compressive strength and
energy absorption increase. The highest values of strength and energy
absorption were obtained from the specimen with 5 wt. % of
nanoparticle reinforcement, t/D of 0.3 (t=1 mm, D=400μm) as 22.88
MPa and 13.24 MJ/m3, respectively. The moderate specific strength
of prepared composites in the present study showed the good
consistency with the properties of others low carbon steel composite
with similar structure.
Abstract: Micro-alloyed steel components are used in
automotive industry for the necessity to make the manufacturing
process cycles shorter when compared to conventional steel by
eliminating heat treatment cycles, so an important saving of costs and
energy can be reached by reducing the number of operations. Microalloying
elements like vanadium, niobium or titanium have been
added to medium carbon steels to achieve grain refinement with or
without precipitation strengthening along with uniform
microstructure throughout the matrix. Present study reports the
applicability of medium carbon vanadium micro-alloyed steel in hot
forging. Forgeability has been determined with respect to different
cooling rates, after forging in a hydraulic press at 50% diameter
reduction in temperature range of 900-11000C. Final microstructures,
hardness, tensile strength, and impact strength have been evaluated.
The friction coefficients of different lubricating conditions, viz.,
graphite in hydraulic oil, graphite in furnace oil, DF 150 (Graphite,
Water-Based) die lubricant and dry or without any lubrication were
obtained from the ring compression test for the above micro-alloyed
steel. Results of ring compression tests indicate that graphite in
hydraulic oil lubricant is preferred for free forging and dry lubricant
is preferred for die forging operation. Exceptionally good forgeability
and high resistance to fracture, especially for faster cooling rate has
been observed for fine equiaxed ferrite-pearlite grains, some amount
of bainite and fine precipitates of vanadium carbides and
carbonitrides. The results indicated that the cooling rate has a
remarkable effect on the microstructure and mechanical properties at
room temperature.
Abstract: In sheet metal forming process, raw material
mechanical properties are important parameters. This paper is to
compare the wall’s incline angle or formability of SS 400 steel and
SUS 304 stainless steel in single point incremental forming. The two
materials are ferrous base alloyed, which have the different unit cell,
mechanical property and chemical composition. They were forming
into cone shape specimens having 100 mm diameter with different
wall’s incline angle: 90o, 75o and 60o. The investigation was
continued until the specimens formed surface facture. The
experimental result showed that the smaller the wall incline angle
higher the formability with the both materials. The formability limit
of the ferrous base alloy was approx. 60o wall’s incline angle. By
nature, SS 400 has higher formability than SUS 304. This result can
be used as the initial data in designing the single point incremental
forming parts.
Abstract: In this research article a comprehensive investigation
has been carried out to determine the effect of thermal cycle on
temperature dependent process parameters developed during gas
tungsten arc (GTA) welding of high carbon (AISI 1090) steel butt
joints. An experiment based thermal analysis has been performed to
obtain the thermal history. We have focused on different
thermophysical properties such as thermal conductivity, heat transfer
coefficient and cooling rate. Angular torch model has been utilized to
find out the surface heat flux and its variation along the fusion zone as
well as along the longitudinal direction from fusion boundary. After
welding and formation of weld pool, heat transfer coefficient varies
rapidly in the vicinity of molten weld bead and heat affected zone. To
evaluate the heat transfer coefficient near the fusion line and near the
rear end of the plate (low temperature region), established correlation
has been implemented and has been compared with empirical
correlation which is noted as coupled convective and radiation heat
transfer coefficient. Change in thermal conductivity has been
visualized by analytical model of moving point heat source. Rate of
cooling has been estimated by using 2-dimensional mathematical
expression of cooling rate and it has shown good agreement with
experimental temperature cycle. Thermophysical properties have been
varied randomly within 0 -10s time span.
Abstract: In this study, Electrical Discharge Machining (EDM) is used to modify the surface of high carbon steel En31 with the help of tool electrode (Copper-Chromium-Nickel) manufactured by powder metallurgy (PM) process. The effect of EDM on surface roughness during surface alloying is studied. Taguchi’s Design of experiment (DOE) and L18 orthogonal array is used to find the best level of input parameters in order to achieve high surface finish. Six input parameters are considered and their percentage contribution towards surface roughness is investigated by analysis of variances (ANOVA). Experimental results show that an hard alloyed surface (1.21% carbon, 2.14% chromium and 1.38% nickel) with surface roughness of 3.19µm can be generated using EDM with PM tool. Additionally, techniques like Scanning Electron Microscope (SEM) and Energy Dispersive Spectroscopy (EDS) are used to analyze the machined surface and EDMed layer composition, respectively. The increase in machined surface micro-hardness (101%) may be related to the formation of carbides containing chromium.
Abstract: In this paper, the behavior of different types of DST columns has been studied under bending load. Briefly, composite columns consist of an internal carbon steel tube and an external stainless steel wall that the between the walls are filled with concrete. Composite columns are expected to combine the advantages of all three materials and have the advantage of high flexural stiffness of CFDST columns. In this research, ABAQUS software is used for finite element analysis then the results of ultimate strength of the composite sections are illustrated.
Abstract: Spheroidization heat treatment was conducted on the SK85 high carbon steel sheets with various initial microstructures obtained after cold rolling by various reduction ratios at a couple of annealing temperatures. On the high carbon steel sheet with fine pearlite microstructure, obtained by soaking at 800oC for 2hr in a box furnace and then annealing at 570oC for 5min in a salt bath furnace followed by water quenching, cold rolling was conducted by reduction ratios of 20, 30, and 40%. Heat treatment for spheroidization was carried out at 600 and 720oC for the various time intervals from 0.1 to 32 hrs. Area fraction of spheroidized cementite was measured with an image analyzer as a function of cold reduction ratios and duration times. Tensile tests were carried out at room temperature on the spheoidized high carbon steel.