Abstract: Indoor air environment is a big concern in the last few decades in the developing countries, with increased focus on monitoring the air quality. In this work, an experimental study has been conducted to establish the existence of carbon nanoparticles below the size range of 10 nm in the non-sooting zone of a LPG/air partially premixed flame. Mainly, four optical techniques, UV absorption spectroscopy, fluorescence spectroscopy, dynamic light scattering and TEM have been used to characterize and measure the size of carbon nanoparticles in the sampled materials collected from the inner surface of the flame front. The existence of the carbon nanoparticles in the sampled material has been confirmed with the typical nature of the absorption and fluorescence spectra already reported in the literature. The band gap energy shows that the particles are made up of three to six aromatic rings. The size measurement by DLS technique also shows that the particles below the size range of 10 nm. The results of DLS are also corroborated by the TEM image of the same material.
Abstract: Oxygen Reduction Reaction (ORR) performance of
iron and nitrogen co-doped porous carbon nanoparticles (Fe-NPC)
with various physical and (electro) chemical properties have been
investigated. Fe-NPC nanoparticles are synthesized via a facile
soft-templating procedure by using Iron (III) chloride hexa-hydrate as
iron precursor and aminophenol-formaldehyde resin as both carbon
and nitrogen precursor. Fe-NPC nanoparticles shows high surface area
(443.83 m2g-1), high pore volume (0.52 m3g-1), narrow mesopore size
distribution (ca. 3.8 nm), high conductivity (IG/ID=1.04), high kinetic
limiting current (11.71 mAcm-2) and more positive onset potential
(-0.106 V) compared to metal-free NPC nanoparticles (-0.295V)
which make it high efficient ORR metal-free catalysts in alkaline
solution. This study may pave the way of feasibly designing iron and
nitrogen containing carbon materials (Fe-N-C) for highly efficient
oxygen reduction electro-catalysis.
Abstract: Carbon nanotubes (CNTs) possess unique structural,
mechanical, thermal and electronic properties, and have been
proposed to be used for applications in many fields. However, to
reach the full potential of the CNTs, many problems still need to be
solved, including the development of an easy and effective
purification procedure, since synthesized CNTs contain impurities,
such as amorphous carbon, carbon nanoparticles and metal particles.
Different purification methods yield different CNT characteristics
and may be suitable for the production of different types of CNTs. In
this study, the effect of different purification chemicals on carbon
nanotube quality was investigated. CNTs were firstly synthesized by
chemical vapor deposition (CVD) of acetylene (C2H2) on a
magnesium oxide (MgO) powder impregnated with an iron nitrate
(Fe(NO3)3·9H2O) solution. The synthesis parameters were selected
as: the synthesis temperature of 800°C, the iron content in the
precursor of 5% and the synthesis time of 30 min. The liquid phase
oxidation method was applied for the purification of the synthesized
CNT materials. Three different acid chemicals (HNO3, H2SO4, and
HCl) were used in the removal of the metal catalysts from the
synthesized CNT material to investigate the possible effects of each
acid solution to the purification step. Purification experiments were
carried out at two different temperatures (75 and 120 °C), two
different acid concentrations (3 and 6 M) and for three different time
intervals (6, 8 and 15 h). A 30% H2O2 : 3M HCl (1:1 v%) solution
was also used in the purification step to remove both the metal
catalysts and the amorphous carbon. The purifications using this
solution were performed at the temperature of 75°C for 8 hours.
Purification efficiencies at different conditions were evaluated by
thermogravimetric analysis. Thermal and electrical properties of
CNTs were also determined. It was found that the obtained electrical
conductivity values for the carbon nanotubes were typical for organic
semiconductor materials and thermal stabilities were changed
depending on the purification chemicals.
Abstract: spherical porous carbon particles with
controllable porosity with a mean size of 2.5m have been
prepared using a spray drying method with organic particle
colloidal template. As a precursor, a mixing solution of carbon
nanopowder and polystyrene (PS) particles as a template was
used. The result showed that the particles with a good porous
structure could be obtained. The pore size and shape (spherical)
were identical to the initial template, giving a potential way for
further developments. The control of particle porosity was also
possible and reported in this paper, in which this control could
be achieved by means of PS concentration.