Abstract: An efficient method is developed for the response of a group of vertical, cylindrical fixed-head, finite length piles embedded in a homogeneous elastic stratum, subjected to harmonic force atop the pile group cap. Pile to pile interaction is represented through simplified beam-on-dynamic-Winkler-foundation (BDWF) with realistic frequency-dependent springs and dashpots. Pile group effect is considered through interaction factors. New closed-form expressions for interaction factors and curvature ratios atop the pile are extended by considering different boundary conditions at the tip of the piles (fixed, hinged). In order to investigate the fundamental characteristics of inertial bending strains in pile groups, inertial bending strains at the head of each pile are expressed in terms of slenderness ratio. The results of parametric study give valuable insight in understanding the behavior of fixed head pile groups in fundamental natural frequency of soil stratum.
Abstract: This paper presents effects of distilled water, seawater
and sustained bending strains of 30% and 50% ultimate strain at
room temperature, on the durability of unidirectional pultruded
carbon fiber reinforced polymer (CFRP) plates. In this study,
dynamic mechanical analyzer (DMA) was used to investigate the
synergic effects of the immersions and bending strains on the viscoelastic
properties of (CFRP) such as storage modulus, tan delta and
glass transition temperature. The study reveals that the storage
modulus and glass transition temperature increase while tan delta
peak decreases in the initial stage of both immersions due to the
progression of curing. The storage modulus and Tg subsequently
decrease and tan delta increases due to the matrix plasticization. The
blister induced damages in the unstrained seawater samples enhance
water uptake and cause more serious degradation of Tg and storage
modulus than in water immersion. Increasing sustained bending
decreases Tg and storage modulus in a long run for both immersions
due to resin matrix cracking and debonding. The combined effects of
immersions and strains are not clearly reflected due to the statistical
effects of DMA sample sizes and competing processes of molecular
reorientation and postcuring.