Abstract: The relationship between biodegradation and mechanical behavior is fundamental for studies of the application of cellulose acetate films as a possible material for biodegradable packaging. In this work, the biodegradation of cellulose acetate (CA) with DS 2.5 was analyzed in simulated soil. CA films were prepared by casting and buried in the simulated soil. Samples were taken monthly and analyzed, the total time of biodegradation was 6 months. To characterize the biodegradable CA, the DMA technique was employed. The main result showed that the time of exposure to the simulated soil affects the mechanical properties of the films and the values of crystallinity. By DMA analysis, it was possible to conclude that as the CA is biodegraded, its mechanical properties were altered, for example, storage modulus has increased with biodegradation and the modulus of loss has decreased. Analyzes of DSC, XRD, and FTIR were also carried out to characterize the biodegradation of CA, which corroborated with the results of DMA. The observation of the carbonyl band by FTIR and crystalline indices obtained by XRD were important to evaluate the degradation of CA during the exposure time.
Abstract: In this work, the composites were prepared with poly(lactic acid) (PLA) and olive husk flour (OHF) with different percentages (10, 20 and 30%) using extrusion method followed by injection molding. The morphological, mechanical properties and thermal behavior of composites were investigated. Tensile strength and elongation at break of composites showed a decreasing trend with increasing fiber content. On the other hand, Young modulus and storage modulus were increased. The addition of OHF resulted in a decrease in thermal stability of composites. The presence of OHF led to an increase in percentage of crystallinity (Xc) of PLA matrix.
Abstract: An ion implantation technique was used for designing the surface area of a titanium alloy and for irradiation-enhanced hardening of the surface. The Ti6Al4V alloy was treated by nitrogen ion implantation at fluences of 2·1017 and 4·1017 cm-2 and at ion energy 90 keV. The depth distribution of the nitrogen was investigated by Rutherford Backscattering Spectroscopy. The gradient of mechanical properties was investigated by nanoindentation. The continuous measurement mode was used to obtain depth profiles of the indentation hardness and the reduced storage modulus of the modified surface area. The reduced storage modulus and the hardness increase with increasing fluence. Increased fluence shifts the peak of the mechanical properties as well as the peak of nitrogen concentration towards to the surface. This effect suggests a direct relationship between mechanical properties and nitrogen distribution.
Abstract: This work aims to investigate the structure–property
relationship in ternary nanocomposites consisting of polypropylene
as the matrix, polyamide 66 as the minor phase and treated nanoclay
DELLITE 67G as the reinforcement. All PP/PA66/Nanoclay systems
with polypropylene grafted maleic anhydride PP-g-MAH as a
compatibilizer were prepared via melt compounding and
characterized in terms of nanoclay content. Morphological structure
was investigated by scanning electron microscopy. The rheological
behavior of the nanocomposites was determined by various methods,
viz melt flow index (MFI) and parallel plate rheological
measurements. The PP/PP-g-MAH/PA66 nanocomposites showed a homogeneous
morphology supporting the compatibility improvement between PP,
PA66, and nanoclay. SEM results revealed the formation of
nanocomposites as the nanoclay was intercalated and exfoliated. In
the ternary nanocomposites, the rheological behavior showed that, the
complex viscosity is increased with increasing the nanoclay. The results showed that the use of nanoclay affects the variations
of storage modulus (G′), loss modulus (G″) and the melt elasticity.
Abstract: This paper presents effects of distilled water, seawater
and sustained bending strains of 30% and 50% ultimate strain at
room temperature, on the durability of unidirectional pultruded
carbon fiber reinforced polymer (CFRP) plates. In this study,
dynamic mechanical analyzer (DMA) was used to investigate the
synergic effects of the immersions and bending strains on the viscoelastic
properties of (CFRP) such as storage modulus, tan delta and
glass transition temperature. The study reveals that the storage
modulus and glass transition temperature increase while tan delta
peak decreases in the initial stage of both immersions due to the
progression of curing. The storage modulus and Tg subsequently
decrease and tan delta increases due to the matrix plasticization. The
blister induced damages in the unstrained seawater samples enhance
water uptake and cause more serious degradation of Tg and storage
modulus than in water immersion. Increasing sustained bending
decreases Tg and storage modulus in a long run for both immersions
due to resin matrix cracking and debonding. The combined effects of
immersions and strains are not clearly reflected due to the statistical
effects of DMA sample sizes and competing processes of molecular
reorientation and postcuring.
Abstract: Two types of glass fibers having different lengths
(1/16" and 1/32") were added into rigid PVC foams to enhance the
dimensional stability of extruded rigid Polyvinyl Chloride (PVC)
foam at different concentrations (0-20 phr) using a single screw
profile extruder. PVC foam-glass fiber composites (PVC-GF) were
characterized for their dimensional stability, structural, thermal, and
mechanical properties. Experimental results show that the
dimensional stability, heat resistance, and storage modulus were
enhanced without compromising the tensile and flexural strengths of
the composites. Overall, foam composites which were prepared with
longer glass fibers exhibit better mechanical and thermal properties
than those prepared with shorter glass fibers due to higher
interlocking between the fibers and the foam cells, which result in
better load distribution in the matrix.
Abstract: In this research work, poly (acrylonitrile-butadienestyrene)/
polypropylene (ABS/PP) blends were processed by melt
compounding in a twin-screw extruder. Upgrading of the thermal
characteristics of the obtained materials was attempted by the
incorporation of organically modified montmorillonite (OMMT), as
well as, by the addition of two types of compatibilizers;
polypropylene grafted with maleic anhydride (PP-g-MAH) and ABS
grafted with maleic anhydride (ABS-g-MAH). The effect of the
above treatments was investigated separately and in combination.
Increasing the PP content in ABS matrix seems to increase the
thermal stability of their blend and the glass transition temperature
(Tg) of SAN phase of ABS. From the other part, the addition of ABS
to PP promotes the formation of its β-phase, which is maximum at 30
wt% ABS concentration, and increases the crystallization temperature
(Tc) of PP. In addition, it increases the crystallization rate of PP.The
β-phase of PP in ABS/PP blends is reduced by the addition of
compatibilizers or/and organoclay reinforcement. The incorporation
of compatibilizers increases the thermal stability of PP and reduces
its melting (ΔΗm) and crystallization (ΔΗc) enthalpies. Furthermore it
decreases slightly the Tgs of PP and SAN phases of ABS/PP blends.
Regarding the storage modulus of the ABS/PP blends, it presents a
change in their behavior at about 10°C and return to their initial
behavior at ~110°C. The incorporation of OMMT to no compatibilized
and compatibilized ABS/PP blends enhances their storage modulus.
Abstract: Composites based on a biodegradable polycaprolactone (PCL) containing 0.5, 1.0 and 2.0 wt % of titanium dioxide (TiO2) micro and nanoparticles were prepared by melt mixing and the effect of filler type and contents on the thermal properties, dynamic-mechanical behaviour and morphology were investigated. Measurements of storage modulus and loss modulus by dynamic mechanical analysis (DMA) showed better results for microfilled PCL/TiO2 composites than nanofilled composites, with the same filler content. DSC analysis showed that the Tg and Tc of micro and nanocomposites were slightly lower than those of neat PCL. The crystallinity of the PCL increased with the addition of TiO2 micro and nanoparticles; however, the cc for the PCL was unchanged with micro TiO2 content. The thermal stability of PCL/TiO2 composites were characterized using thermogravimetric analysis (TGA). The initial weight loss (5 wt %) occurs at slightly higher temperature with micro and nano TiO2 addition and with increasing TiO2 content.