Abstract: Polymer composite nano-fibers including (1, 3 wt %)
silver nano-particles have been produced by electrospinning method.
Polyacrylonitrile/N,N-dimethylformamide (PAN/DMF) solution have
been prepared and the amount of silver nitrate have been adjusted to
PAN weight. Silver nano-particles were obtained from reduction of
silver ions into silver nano-particles by chemical reduction by
hydrazine hydroxide (N2H5OH). The different amount of silver salt
was loaded into polymer matrix to obtain polyacrylonitrile composite
nano-fiber containing silver nano-particles. The effect of the amount
of silver nano-particles on the properties of composite nano-fiber web
was investigated. Electrical conductivity, mechanical properties,
thermal properties were examined by Microtest LCR Meter 6370
(0.01 mΩ-100 MΩ), Tensile tester, Differential scanning calorimeter
DSC (Q10) and SEM respectively. Also antimicrobial efficiency test
(ASTM E2149-10) was done against to Staphylococcus aureus
bacteria. It has been seen that breaking strength, conductivity,
antimicrobial effect, enthalpy during cyclization increase by use of
silver nano-particles while the diameter of nano-fiber decreases.
Abstract: Preparation of size controlled nano-particles of silver catalyst on carbon substrate from e-waste has been investigated. Chemical route was developed by extraction of the metals available in nitric acid followed by treatment with hydrofluoric acid. Silver metal particles deposited with an average size 4-10 nm. A stabilizer concentration of 10- 40 g/l was used. The average size of the prepared silver decreased with increase of the anode current density. Size uniformity of the silver nano-particles was improved distinctly at higher current density no more than 20mA... Grain size increased with EK time whereby aggregation of particles was observed after 6 h of reaction.. The chemical method involves adsorption of silver nitrate on the carbon substrate. Adsorbed silver ions were directly reduced to metal particles using hydrazine hydrate. Another alternative method is by treatment with ammonia followed by heating the carbon loaded-silver hydroxide at 980°C. The product was characterized with the help of XRD, XRF, ICP, SEM and TEM techniques.
Abstract: Silver nano-particles have been used for antibacterial
purpose and it is also believed to have removal of odorous compounds,
oxidation capacity as a metal catalyst. In this study, silver
nano-particles in nano sizes (5-30 nm) were prepared on the surface of
NaHCO3, the supporting material, using a sputtering method that
provided high silver content and minimized conglomerating problems
observed in the common AgNO3 photo-deposition method. The silver
nano-particles were dispersed by dissolving Ag-NaHCO3 into water,
and the dispersed silver nano-particles in the aqueous phase were
applied to remove inorganic odor compounds, H2S, in a scrubbing
reactor. Hydrogen sulfide in the gas phase was rapidly removed by the
silver nano-particles, and the concentration of sulfate (SO4
2-) ion
increased with time due to the oxidation reaction by silver as a
catalyst. Consequently, the experimental results demonstrated that the
silver nano-particles in the aqueous solution can be successfully
applied to remove odorous compounds without adding additional
energy sources and producing any harmful byproducts