Abstract: This research paper reports on the feasibility and viability of eggshells ash and its effects on the water content and setting time of cement. An experiment was carried out to determine the quantity of water required in order to follow standard cement paste of normal consistency in accordance with MS EN 196-3:2007. The eggshells ash passing the 90µm sieve was used in the investigation. Eggshells ash with percentage of 0%, 0.1%, 0.5%, 1.0%, 1.5% and 2.0% were constituted to replace the cement. Chemical properties of both eggshells ash and cement are compared. From the results obtained, both eggshells ash and cement have the same chemical composition and primary composition which is the calcium compounds. Results from the setting time show that by adding the eggshells ash to the cement, the setting time of the cement decreases. In short, the higher amount of eggshells ash, the faster the rate of setting and apply to all percentage of eggshells ash that were used in this investigation. Both initial and final setting times fulfill the setting time requirements by Malaysian Standard. Hence, it is suggested that eggshells ash can be used as an admixture in concrete mix.
Abstract: The change of conditions for production companies in
high-wage countries is characterized by the globalization of
competition and the transition of a supplier´s to a buyer´s market. The
companies need to face the challenges of reacting flexibly to these
changes. Due to the significant and increasing degree of automation,
assembly has become the most expensive production process.
Regarding the reduction of production cost, assembly consequently
offers a considerable rationalizing potential. Therefore, an
aerodynamic feeding system has been developed at the Institute of
Production Systems and Logistics (IFA), Leibniz Universitaet
Hannover. This system has been enabled to adjust itself by using a
genetic algorithm. The longer this genetic algorithm is executed the
better is the feeding quality. In this paper, the relation between the
system´s setting time and the feeding quality is observed and a
function which enables the user to achieve the minimum of the total
feeding time is presented.
Abstract: Calcium phosphate cement (CPC) is one of the most
attractive bioceramics due to its moldable and shape ability to fill
complicated bony cavities or small dental defect positions. In this
study, CPC was produced by using mixture of tetracalcium phosphate
(TTCP, Ca4O(PO4)2) and dicalcium phosphate anhydrous (DCPA,
CaHPO4) in equimolar ratio (1/1) with aqueous solutions of acetic
acid (C2H4O2) and disodium hydrogen phosphate dehydrate
(Na2HPO4.2H2O) in combination with sodium alginate in order to
improve theirs moldable characteristic. The concentration of the
aqueous solutions and sodium alginate were varied to investigate the
effect of different aqueous solutions and alginate on properties of the
cements. The cement paste was prepared by mixing cement powder
(P) with aqueous solution (L) in a P/L ratio of 1.0g/0.35ml. X-ray
diffraction (XRD) was used to analyses phase formation of the
cements. Setting time and compressive strength of the set CPCs were
measured using the Gilmore apparatus and Universal testing
machine, respectively.
The results showed that CPCs could be produced by using both
basic (Na2HPO4.2H2O) and acidic (C2H4O2) solutions. XRD results
show the precipitation of hydroxyapatite in all cement samples. No
change in phase formation among cements using difference
concentrations of Na2HPO4.2H2O solutions. With increasing
concentration of acidic solutions, samples obtained less
hydroxyapatite with a high dicalcium phosphate dehydrate leaded to
a shorter setting time. Samples with sodium alginate exhibited higher
crystallization of hydroxyapatite than that of without alginate as a
result of shorten setting time in a basic solution but a longer setting
time in an acidic solution. The stronger cement was attained from
samples using the acidic solution with sodium alginate; however the
strength was lower than that of using the basic solution.