Abstract: Slurry infiltrated fiber concrete (SIFCON) is considered as a special type of high strength high-performance fiber reinforced concrete, extremely strong, and ductile. The objective of this study is to investigate the durability of SIFCON to corrosion in chloride environments. Six different SIFCON mixes were made in addition to two refinance mixes with 0% and 1.5% steel fiber content. All mixes were exposed to 10% chloride solution for 180 days. Half of the specimens were partially immersed in chloride solution, and the others were exposed to weekly cycles of wetting and drying in 10% chloride solution. The effectiveness of using corrosion inhibitors, mineral admixture, and epoxy protective coating were also evaluated as protective measures to reduce the effect of chloride attack and to improve the corrosion resistance of SIFCON mixes. Corrosion rates, half-cell potential, electrical resistivity, total permeability tests had been monitored monthly. The results indicated a significant improvement in performance for SIFCON mixes exposed to chloride environment, when using corrosion inhibitor or epoxy protective coating, whereas SIFCON mix contained mineral admixture (metakaolin) did not improve the corrosion resistance at the same level. The cyclic wetting and drying exposure were more aggressive to the specimens than the partial immersion in chloride solution although the observed surface corrosion for the later was clearer.
Abstract: The seriously damaged structures during earthquakes
show the need and importance of design of reinforced concrete
structures with high ductility. Reinforced concrete beam-column
joints have an important function in all structures. Under seismic
excitation, the beam column joint region is subjected to horizontal
and vertical shear forces whose magnitude is many times higher than
the adjacent beam and column. Strength and ductility of structures
depends mainly on proper detailing of the reinforcement in beamcolumn
joints and the old structures were found ductility deficient.
DSP materials are obtained by using high quantities of super
plasticizers and high volumes of micro silica. In the case of High
Performance Densified Small Particle Concrete (HPDSPC), since
concrete is dense even at the micro-structure level, tensile strain
would be much higher than that of the conventional SFRC, SIFCON
& SIMCON. This in turn will improve cracking behaviour, ductility
and energy absorption capacity of composites in addition to
durability. The fine fibers used in our mix are 0.3mm diameter and 10
mm which can be easily placed with high percentage. These fibers
easily transfer stresses and act as a composite concrete unit to take up
extremely high loads with high compressive strength. HPDSPC
placed in the beam column joints helps in safety of human life due to
prolonged failure.