Abstract: Slurry infiltrated fiber concrete (SIFCON) is considered as a special type of high strength high-performance fiber reinforced concrete, extremely strong, and ductile. The objective of this study is to investigate the durability of SIFCON to corrosion in chloride environments. Six different SIFCON mixes were made in addition to two refinance mixes with 0% and 1.5% steel fiber content. All mixes were exposed to 10% chloride solution for 180 days. Half of the specimens were partially immersed in chloride solution, and the others were exposed to weekly cycles of wetting and drying in 10% chloride solution. The effectiveness of using corrosion inhibitors, mineral admixture, and epoxy protective coating were also evaluated as protective measures to reduce the effect of chloride attack and to improve the corrosion resistance of SIFCON mixes. Corrosion rates, half-cell potential, electrical resistivity, total permeability tests had been monitored monthly. The results indicated a significant improvement in performance for SIFCON mixes exposed to chloride environment, when using corrosion inhibitor or epoxy protective coating, whereas SIFCON mix contained mineral admixture (metakaolin) did not improve the corrosion resistance at the same level. The cyclic wetting and drying exposure were more aggressive to the specimens than the partial immersion in chloride solution although the observed surface corrosion for the later was clearer.
Abstract: Acidification is a technique used in oil reservoirs
to improve annual production, reduce the skin and increase the
pressure of an oil well while eliminating the formation damage that
occurs during the drilling process, completion and, amongst others,
to create new channels allowing the easy circulation of oil around
a producing well. This is achieved by injecting an acidizing fluid
at a relatively low pressure to prevent fracturing formation. The
treatment fluid used depends on the type and nature of the reservoir
rock traversed as well as its petrophysical properties. In order to
understand the interaction mechanisms between the treatment fluids
used for the reservoir rock acidizing, several candidate wells for
stimulation were selected in the large Hassi Messaoud deposit in
southern Algeria. The stimulation of these wells is completed using
different fluids composed mainly of HCl acid with other additives
such as corrosion inhibitors, clay stabilizers and iron controllers.
These treatment fluids are injected over two phases, namely with
clean tube (7.5% HCl) and matrix aidizing with HCl (15%). The
stimulation results obtained are variable according to the type of
rock traversed and its mineralogical composition. These results show
that there has been an increase in production flow and head pressure
respectively from 1.99 m3 / h to 3.56 m3 / h and from 13 Kgf / cm2
to 20 kgf / cm2 in the sands formation having good petrophysical
properties of (porosity = 16%) and low amount of clay (Vsh = 6%).
Abstract: The present work is aimed at examining carbon steel
oil pipelines corrosion using three natural extracts (Eruca Sativa,
Rosell and Mango peels) that are used as inhibitors of different
concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds
are used as corrosion mediums. Weight loss method was used for
measuring the corrosion rate of the carbon steel specimens immersed
in technical white oil at 100ºC at various time intervals in absence
and presence of the two sulphur compounds. The corroded specimens
are examined using the chemical wear test, scratch test and hardness
test. The scratch test is carried out using scratch loads from 0.5 Kg to
2.0 Kg. The scratch width is obtained at various scratch load and test
conditions. The Brinell hardness test is carried out and investigated
for both corroded and inhibited specimens. The results showed that
three natural extracts can be used as environmentally friendly
corrosion inhibitors.
Abstract: Corrosion inhibitors are widely used in concrete
industry to reduce the corrosion rate of steel rebar which is present in
contact with aggressive environments. The present work aims to
using Zamzam water from well located within the Masjid al-Haram
in Mecca, Saudi Arabia 20 m (66 ft) east of the Kaaba, the holiest
place in Islam as corrosion inhibitor for steel in rain water and
simulated acid rain. The effect of Zamzam water was investigated by
electrochemical impedance spectroscopy (EIS) and Potentiodynamic
polarization techniques in Department of Civil Engineering - IUT
Saint-Nazaire, Nantes University, France. Zamzam water is
considered to be one of the most important steel corrosion inhibitor
which is frequently used in different industrial applications. Results
showed that zamzam water gave a very good inhibition for steel
corrosion in rain water and simulated acid rain.
Abstract: The aim of this paper is to compare the effectiveness and electrochemical behavior of typical oilfield corrosion inhibitors with previous oilfield corrosion inhibitors under the same electrochemical techniques to control preferential weld corrosion of X65 pipeline steel in artificial seawater saturated with carbon dioxide at a pressure of one bar. A secondary aim is to investigate the conditions under which current reversal takes place. A flow channel apparatus was used in the laboratory to simulate the actual condition that occurs in marine pipelines. Different samples from the parent metal, the weld metal and the heat affected zone in the pipeline steel were galvanically coupled. The galvanic currents flowing between the weld regions were recorded using zero-resistance ammeters and tested under static and flowing conditions in both inhibited and uninhibited media. The results show that a current reversal took place when 30ppm of both green oilfield inhibitors were present, resulting in accelerated weld corrosion.
Abstract: There was a high rate of corrosion in Pyrolysis
Gasoline Hydrogenation (PGH) unit of Arak Petrochemical Company
(ARPC), and it caused some operational problem in this plant. A
commercial chemical had been used as anti-corrosion in the
depentanizer column overhead in order to control the corrosion rate.
Injection of commercial corrosion inhibitor caused some
operational problems such as fouling in some heat exchangers. It was
proposed to replace this commercial material with another more
effective trouble free, and well-known additive by R&D and
operation specialists.
At first, the system was simulated by commercial simulation
software in electrolytic system to specify low pH points inside the
plant. After a very comprehensive study of the situation and technical
investigations ,ammonia / monoethanol amine solution was proposed
as neutralizer or corrosion inhibitor to be injected in a suitable point
of the plant. For this purpose, the depentanizer column and its
accessories system was simulated again in case of this solution
injection.
According to the simulation results, injection of new anticorrosion
substance has no any side effect on C5 cut product and
operating conditions of the column. The corrosion rate will be
cotrolled, if the pH remains at the range of 6.5 to 8 . Aactual plant
test run was also carried out by injection of ammonia / monoethanol
amine solution at the rate of 0.6 Kg/hr and the results of iron content
of water samples and corrosion test coupons confirmed the
simulation results.
Now, ammonia / monoethanol amine solution is injected to a
suitable pint inside the plant and corrosion rate has decreased
significantly.