Abstract: The influence of cultivation factors such as content of ammonium sulfate, glucose and water in the culture medium and particle size of dry orange waste, on their bioconversion for pectinase production was studied using complete factorial design. A polygalacturonase (PG) was isolated using ion exchange chromatography under gradient elution 0-0,5 m/l NaCl (column equilibrate with acetate buffer pH 4,5), subsequently by sephadex G75 column chromatography was applied and the molecular weight was obtained about 51,28 KDa. Purified PG enzyme exhibits a pH and temperature optima of activity at 5 and 35°C respectively. Treatment of apple juice by purified enzyme extract yielded a clear juice, which was competitive with juice yielded by pure Sigma Aldrich Aspergillus niger enzyme.
Abstract: Ceramic Waste Aggregates (CWAs) were made from
electric porcelain insulator wastes supplied from an electric power
company, which were crushed and ground to fine aggregate sizes. In
this study, to develop the CWA mortar as an eco–efficient, ground
granulated blast–furnace slag (GGBS) as a Supplementary
Cementitious Material (SCM) was incorporated. The water–to–binder
ratio (W/B) of the CWA mortars was varied at 0.4, 0.5, and 0.6. The
cement of the CWA mortar was replaced by GGBS at 20 and 40% by
volume (at about 18 and 37% by weight). Mechanical properties of
compressive and splitting tensile strengths, and elastic modulus were
evaluated at the age of 7, 28, and 91 days. Moreover, the chloride
ingress test was carried out on the CWA mortars in a 5.0% NaCl
solution for 48 weeks. The chloride diffusion was assessed by using an
electron probe microanalysis (EPMA). To consider the relation of the
apparent chloride diffusion coefficient and the pore size, the pore size
distribution test was also performed using a mercury intrusion
porosimetry at the same time with the EPMA. The compressive
strength of the CWA mortars with the GGBS was higher than that
without the GGBS at the age of 28 and 91 days. The resistance to the
chloride ingress of the CWA mortar was effective in proportion to the
GGBS replacement level.
Abstract: We investigated the structure and electronic properties
of the compound Mg1-xBixO with varying concentrations of 0, ¼, ½,
and ¾ x bismuth in the the cesium chloride (CsCl), zinc-blende
(ZnS), nickel arsenide (NiAs) NaCl (rock-salt) and WZ (wurtzite)
phases. We calculated. The calculations were performed using the
first-principles pseudo-potential method within the framework of spin
density functional theory (DFT).
Abstract: Waxapple (Syzygium samarngense Merr.et Perry) is an
important tropical fruit in Taiwan. The famous producing area is
located on the coast in Pingtung County. Land subsidence and climate
change will tend to soil alkalization more seriously. This study was to
evaluate the effects of NaCl in waxapple seedlings. NaCl salinity
reduced waxapple shoot growth; it may due to reducing relative water
content in leaf and new shoot. Leaf Cl and Na concentration were
increased but K, Ca, and Mg content had no significant difference after
irrigated with NaCl for six weeks. In roots, Na and Cl content increase
significantly with 90 mM NaCl treatment, but K, Ca, and Mg content
was reduced. 30-90mM Nacl treatment do not effect K/Na, Ca/Na and
Mg/Na ratio, but decrease significantly in 90mM treatment in roots.
The leaf and root electrolyte leakage were significantly affected by 90
mM NaCl treatment. Suggesting 90mM was optimum concentration
for sieve out other tolerance waxapples verities.
Abstract: Due to water shortage, application of saline water for
irrigation is an urgent in agriculture. In this study the effect of
calcium and potassium application as additive in saline root media for
reduce salinity adverse effects was investigated on tomato growth in
a hydroponic system with unequal distribution of salts in the root
media, which was divided in to two equal parts containing full
Johnson nutrient solution and 40 mMNaCl solution, alone or in
combination with KCl (6 mM), CaCl2 (4 mM), K+Ca (3+2 mM) or
half-strength Johnson nutrient solution. The root splits were
exchanged every 7 days. Results showed that addition of calcium,
calcium-potassium and nutrition elements equivalent to half the
concentration of Johnson formula to the saline-half of culture media
minimized the reduction in plant growth caused by NaCl, although
addition of potassium to culture media wasn’t effective. The greatest
concentration of sodium was observed at the shoot of treatments
which had smallest growth. According to the results of this study, in
case of dynamic and non-uniform distribution of salts in the root
media, by addition of additive to the saline solution, it would be
possible to use of saline water with no significant growth reduction.
Abstract: The hydrogenated amorphous carbon films (α-C:H)
were deposited on p-type Si (100) substrates at different thicknesses by
radio frequency plasma enhanced chemical vapor deposition
technique (rf-PECVD). Raman spectra display asymmetric
diamond-like carbon (DLC) peaks, representative of the α-C:H films.
The decrease of intensity ID/IG ratios revealed the sp3 content arise at
different thicknesses of the α-C:H films. In terms of mechanical
properties, the high hardness and elastic modulus values showed the
elastic and plastic deformation behaviors related to sp3 content in
amorphous carbon films. Electrochemical properties showed that the
α-C:H films exhibited excellent corrosion resistance in air-saturated
3.5 wt.% NaCl solution for pH 2 at room temperature. Thickness
increasing affected the small sp2 clusters in matrix, restricting the
velocity transfer and exchange of electrons. The deposited α-C:H films
exhibited excellent mechanical properties and corrosion resistance.
Abstract: Since the marine environmental conditions are
extremely different from the other ones, marine actinomycetes might
produce novel bioactive compounds. Therefore, actinomycete strains
were screened from marine water and sediment samples collected
from the coastal areas of Northern Vietnam. Ninety-nine
actinomycete strains were obtained on starch-casein agar media by
dilution technique, only seven strains, named HP112, HP12, HP411,
HPN11, HP 11, HPT13 and HPX12, showed significant antibacterial
activity against both gram-positive and gram-negative bacteria
(Bacillus subtilis ATCC 6633, Staphylococcus epidemidis ATCC
12228, Escherichia coli ATCC 11105). Further studies were carried
out with the most active HP411 strain against Candida albicans
ATCC 10231. This strain could grow rapidly on starch casein agar
and other media with high salt containing 7-10% NaCl at 28-30oC.
Spore-chain of HP411 showed an elongated and circular shape with
10 to 30 spores/chain. Identification of the strain was carried out by
employing the taxonomical studies including the 16S rRNA
sequence. Based on phylogenetic and phenotypic evidence it is
proposed that HP411 to be belongs to species Streptomyces
variabilis. The potent of the crude extract of fermentation broth of
HP411 that are effective against wide range of pathogens: both grampositive,
gram-negative and fungi. Further studies revealed that the
crude extract HP411 could obtain the anticancer activity for cancer
cell lines: Hep-G2 (liver cancer cell line); RD (cardiac and skeletal
muscle letters cell line); FL (membrane of the uterus cancer cell line).
However, the actinomycetes from marine ecosystem will be useful
for the discovery of new drugs in the future.
Abstract: Al-Si-Mg-Ni(-Cu) alloys are widely used in the automotive industry. They have the advantage of low weight associated with low coefficient of thermal expansion and excellent mechanical properties – mainly at high temperatures. The corrosion resistance of these alloys in coastal area, particularly sea water, however is not yet known. In this investigation, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization have been used to evaluate the corrosion resistance of Al-6Si-0.5Mg-2Ni (-2Cu) alloys in simulated sea water environments. The potentiodynamic polarization curves reveal that 2 wt% Cu content alloy (Alloy-2) is more prone to corrosion than the Cu free alloy (Alloy-1). But the EIS test results showed that corrosion resistance or charge transfer resistance (Rct) increases with the addition of Cu. Due to addition of Cu and thermal treatment, the magnitude of open circuit potential (OCP), corrosion potential (Ecorr) and pitting corrosion potential (Epit) of Al-6Si-0.5Mg-2Ni alloy in NaCl solution were shifted to the more noble direction.
Abstract: This research studies the electroplating of zinc coating
in the zinc chloride bath mixed with supercritical CO2. The sodium
fluoride (NaF) was used as the bath additive to change the structure
and property of the coating, and therefore the roughness and corrosion
resistance of the zinc coating was investigated. The surface
characterization was performed using optical microscope (OM), X-ray
diffractometer (XRD), and α-step profilometer. Moreover, the
potentiodynamic polarization measurement in 3% NaCl solution was
employed in the corrosion resistance evaluation. Because of the
emulsification of the electrolyte mixed in Sc-CO2, the electroplated
zinc produced the coating with smoother surface, smaller grain, better
throwing power and higher corrosion resistance. The main role played
by the NaF was to reduce the coating’s roughness and grain size. In
other words, the CO2 mixed with the electrolyte under the supercritical
condition performed the similar function as brighter and leveler in zinc
electroplating to enhance the throwing power and corrosion resistance
of the coating.
Abstract: The effect of exogenous application; seed priming or foliar spraying of salicylic acid (SA) on Yecora Rojo and Paragon wheat cv. under NaCl-salinity. Gas exchange parameters, growth parameters, yield and yield components were reduced in both cultivars under salinity stress with foliar spray and soaking seeds. Exogenous application of SA through foliar spraying or seed soaking showed a slight increases or decreases with the application method or between cultivars. SA foliar spraying exhibited a slight improvement over SA seed soaking in most parameters, particularly in Paragon. Although, seed soaking was less effective than foliar spraying, it was a slightly better with Yecora Rojo in some parameters. However, the low SA concentration; 0.5mM tended to improve most parameters in both cultivars. From data of the experiment, it has been concluded that the effect of SA depends on cultivar genotype and SA concentration.
Abstract: Germination and seedling responses of seven safflower seed genotypes (Dinçer, Remzibey, Black Sun2 cultivars and A19, F4, I1, J19 lines) to different salinity concentrations (0, 5, 10 and 20g l-1) and temperatures (10 and 20oC) evaluated in Completely Randomized Factorial Designs in Department of Field Crops of Selcuk University, Konya, Turkey. Seeds in the control (distilled water) had at 10 and 20oC the highest germination percentage (93.88 and 94.32%), shoot length (4.60 and 8.72cm) and root length (4.27 and 6.54cm) shoot dry weight (22.37mg and 25.99mg) and root dry weight (2.22 and 2.47mg). As the salt concentration increased, values of all characters were decreased. In this experiment, in 20g l-1 salt concentration found germination percentage (21.28 and 26.66%), shoot (1.32 and 1.35cm) and root length (1.04 and 1.10cm) shoot (8.05mg and 7.49mg) and root dry weight (0.83 and 0.98mg) at 10 and 20oC.
Abstract: This paper describes the research carried out to develop a process to increase the NaCl percentage of crude salt which is obtained from the conventional solar evaporation process. In this study refined salt was produced from crude solar salt by a chemico-physical method which consists of coagulation, precipitation and filtration. Initially crude salt crystals were crushed and dissolved in water. Optimum amounts of calcium hydroxide, sodium carbonate and Polyaluminiumchloride (PAC) were added to the solution respectively.
Refined NaCl solution was separated out by a filtration process. The solution was tested for Total Suspended Solids, SO42-, Mg2+, Ca2+. With optimum dosage of reagents, the results showed that a level of 99.60% NaCl could be achieved. Further this paper discusses the economic viability of the proposed process. A 83% profit margin can be achieved by this process and it is an increase of 112.3% compared to the traditional process.
Abstract: Metal working fluids were used in the preparation of oil in water emulsions. The size of oil droplets were evaluated by using the analysis of video images taken from the zeta potential measurements. The evaluated size distributions for emulsions were also tested by microscopic analysis. In addition, emulsion stabilities were discussed depending on electrolyte concentration and pH. The results showed that the stability of oil emulsions was strongly related to pH and the concentration of CaCl2. However, the same dependency was not observed for NaCl.
Abstract: The persistent nature of perfluorochemicals (PFCs) has attracted global concern in recent years. Perfluorooctanesulfonate (PFOS) and perfluorooctanoate (PFOA) are the most commonly found PFC compounds, and thus their fate and transport play key roles in PFC distribution in the natural environment. The kinetic behavior of PFOS or PFOA on boehmite consists of a fast adsorption process followed by a slow adsorption process which may be attributed to the slow transport of PFOS or PFOA into the boehmite pore surface. The adsorption isotherms estimated the maximum adsorption capacities of PFOS and PFOA on boehmite as 0.877 μg/m2 and 0.633 μg/m2, with the difference primarily due to their different functional groups. The increase of solution pH led to a moderate decrease of PFOS and PFOA adsorption, owing to the increase of ligand exchange reactions and the decrease of electrostatic interactions. The presence of NaCl in solution demonstrated negative effects for PFOS and PFOA adsorption on boehmite surfaces, with potential mechanisms being electrical double layer compression, competitive adsorption of chloride.
Abstract: The effect of cross linking of the protein isolates of
three legumes with the microbial enzyme transglutaminase (EC
2.3.2.13) on the functional properties at different NaCl concentration
was studied. The reduction in the total free amino groups (OD340) of
the polymerized protein showed that TGase treatment cross-linking
the protein subunit of each legume. The solubility of the protein
polymer of each legume was greatly improved at high concentration
of NaCl. At 1.2 M NaCl the solubility of the native legumes protein
was significantly decreased but after polymerization slightly
improved. Cross linked proteins were less turbid on heating to higher
temperature as compared to native proteins and the temperature at
which the protein turns turbid also increased in the polymerized
proteins. The emulsifying and foaming properties of the protein
polymer were greatly improved at all concentrations of NaCl for all
legumes.
Abstract: Polymer-like organic thin films were deposited on both
aluminum alloy type 6061 and glass substrates at room temperature by
Plasma Enhanced Chemical Vapor Deposition (PECVD) methodusing
benzene and hexamethyldisiloxane (HMDSO) as precursor materials.
The surface and physical properties of plasma-polymerized organic
thin films were investigated at different r.f. powers. The effects of
benzene/argon ratio on the properties of plasma polymerized benzene
films were also investigated. It is found that using benzene alone
results in a non-coherent and non-adherent powdery deposited
material. The chemical structure and surface properties of the asgrown
plasma polymerized thin films were analyzed on glass
substrates with FTIR and contact angle measurements. FTIR spectra
of benzene deposited film indicated that the benzene rings are
preserved when increasing benzene ratio and/or decreasing r.f.
powers. FTIR spectra of HMDSO deposited films indicated an
increase of the hydrogen concentration and a decrease of the oxygen
concentration with the increase of r.f. power. The contact angle (θ) of
the films prepared from benzene was found to increase by about 43%
as benzene ratio increases from 10% to 20%. θ was then found to
decrease to the original value (51°) when the benzene ratio increases
to 100%. The contact angle, θ, for both benzene and HMDSO
deposited films were found to increase with r.f. power. This signifies
that the plasma polymerized organic films have substantially low
surface energy as the r.f power increases. The corrosion resistance of
aluminum alloy substrate both bare and covered with plasma
polymerized thin films was carried out by potentiodynamic
polarization measurements in standard 3.5 wt. % NaCl solution at
room temperature. The results indicate that the benzene and HMDSO
deposited films are suitable for protection of the aluminum substrate
against corrosion. The changes in the processing parameters seem to
have a strong influence on the film protective ability. Surface
roughness of films deposited on aluminum alloy substrate was
investigated using scanning electron microscopy (SEM). The SEM
images indicate that the surface roughness of benzene deposited films
increase with decreasing the benzene ratio. SEM images of benzene
and HMDSO deposited films indicate that the surface roughness
decreases with increasing r.f. power. Studying the above parameters
indicate that the films produced are suitable for specific practical
applications.
Abstract: Evaluation of crop plants resistance to environmental
stresses specially in germination stage is a critical factor in their
selection in different conditions of cultivation. Therefore use of a
procedure in controllable situation can help to evaluate plants
reaction to stress quickly and precisely. In order to study germination
characteristics of flax in water and salinity stress conditions were
conducted two laboratories experimental. The two experimental were
conducted in 4-replicant completing random design for salinity and
water stress. The treatment, for salinity and water stress was three
potential (zero, 40, 80 mM) of NaCl and three potential (zero, -2, -4
bar) of PEG respectively. Germination percentage and rate, in
addition to Radical and plumule length and dry-weight and
plumule/Radical ration were measured. All of characteristics reduce
under water stress conditions. salinity stress significant reduce
germination rate and Radical and plumule length of flax seeds.
Hydropriming and osmopriming significant increased germination
rate, plumule length and plumule/Radical ration ration of flax seeds.
But germination percentage and Radical and plumule dry weight
significant increased only in hydropriming treat. Hydropriming and
osmopriming could not be used to improved germination under saline
and drought stress. But has more tolerance in salinity and drought
stress in flax by less reduce in Radical and plumule length under
saline and drought stress.
Abstract: Dehydration process was carried out for tomato slices of var. Avinash after giving different pre-treatments such as calcium chloride (CaCl2), potassium metabisulphite (KMS), calcium chloride and potassium metabisulphite (CaCl2 +KMS), and sodium chloride (NaCl). Untreated samples served as control. Solar drier and continuous conveyor (tunnel) drier were used for dehydration. Quality characteristics of tomato slices viz. moisture content, sugar, titratable acidity, lycopene content, dehydration ratio, rehydration ratio and non-enzymatic browning as affected by dehydration process were studied. Storage study was also carried out for a period of six months for tomato powder packed into different types of packaging materials viz. metalized polyester (MP) film and low density poly ethylene (LDPE). Changes in lycopene content and non-enzymatic browning (NEB) were estimated during storage at room temperature. Pretreatment of 5 mm thickness of tomato slices with calcium chloride in combination with potassium metabisulphite and drying using a tunnel drier with subsequent storage of product in metalized polyester bags was selected as the best process.
Abstract: Liquid-liquid extraction is a process using two immiscible
liquids to extract compounds from one phase without high
temperature requirement. Mostly, the technical implementation of
this process is carried out in mixer-settlers or extraction columns. In
real chemical processes, chemicals may have high viscosity and
contain impurities. These impurities may change the settling behavior
of the process without measurably changing the physical properties
of the phases. In the current study, the settling behavior and the affected
parameters in a high-viscosity system were observed. Batchsettling
experiments were performed to experimentally quantify the
settling behavior and the mixer-settler model of Henschke [1] was
used to evaluate the behavior of the toluene + water system. The
viscosity of the system was increased by adding polyethylene glycol
4000 to the aqueous phase. NaCl and Na2SO4 were used to study the
influence of electrolytes. The results from this study show that increasing
the viscosity of water has a higher influence on the settling
behavior in comparison to the effects of the electrolytes. It can be
seen from the experiments that at high salt concentrations, there was
no effect on the settling behavior.
Abstract: Plant growth is affected by the osmotic stress as well as toxicity of salt in leaves. In order to study of salt stress effects on stomatal conductance and growth rate and relationship between them as wells osmotic and Na+-specific effects on these traits, four bread wheat genotypes differing in salt tolerance were selected. Salinity was applied when the leaf 4 was fully expanded. Sodium (Na+) concentrations in flag leaf blade at 3 salinity levels (0, 100 and 200 mM NaCl) were measured. Salt-tolerant genotypes showed higher stomatal conductance and growth rate compared to salt-sensitive ones. After 10 and 20 days exposure to salt, stomatal conductance and relative growth rate were reduced, but the reduction was greater in sensitive genotypes. Growth rate was reduced severely in the first period (1-10 days) of salt commencements and it was due to osmotic effect of salt not Na+ toxicity. In the second period (11-20 days) after salt treatment growth reduced only when salt accumulated to toxic concentrations in the leaves. A positive relationship between stomatal conductance and relative growth rate showed that stomatal conductance can be a reliable indicator of growth rate, and finally can be considered as a sensitive indicator of the osmotic stress. It seems 20 days after salinity, the major effect of salt, especially at low to moderate salinity levels on growth properties was due to the osmotic effect of salt, not to Na+-specific effects within the plant.