Abstract: This study investigated a strategy of blending lead-laden sludge and Al-rich precursors to reduce the release of metals from the stabilized products. Using PbO as the simulated lead-laden sludge to sinter with γ-Al2O3 by Pb:Al molar ratios of 1:2 and 1:12, PbAl2O4 and PbAl12O19 were formed as final products during the sintering process, respectively. By firing the PbO + γ-Al2O3 mixtures with different Pb/Al molar ratios at 600 to 1000 °C, the lead transformation was determined through X-ray diffraction (XRD) data. In Pb/Al molar ratio of 1/2 system, the formation of PbAl2O4 is initiated at 700 °C, but an effective formation was observed above 750 °C. An intermediate phase, Pb9Al8O21, was detected in the temperature range of 800-900 °C. However, different incorporation behavior for sintering PbO with Al-rich precursors at a Pb/Al molar ratio of 1/12 was observed during the formation of PbAl12O19 in this system. In the sintering process, both temperature and time effect on the formation of PbAl2O4 and PbAl12O19 phases were estimated. Finally, a prolonged leaching test modified from the U.S. Environmental Protection Agency-s toxicity characteristic leaching procedure (TCLP) was used to evaluate the durability of PbO, Pb9Al8O21, PbAl2O4 and PbAl12O19 phases. Comparison for the leaching results of the four phases demonstrated the higher intrinsic resistance of PbAl12O19 against acid attack.
Abstract: Column leach test has been performed to examine the
behavior of leaching of sodium, calcium and potassium in landfills.
In the column leach apparatus, two different layers of contaminated
and uncontaminated soils of different height ratios (ratio of depth of
contaminated soil to the depth of uncontaminated soil) are taken.
Water is poured from an overhead tank at a particular flowrate to the
inlet of the soil column for a certain ponding depth over the
contaminated soil. Subsequent infiltration causes leaching and the
leachates are collected from the bottom of the column. The
concentrations of Na, Ca and K in the leachate are measured using
flame photometry. The experiments are further extended by changing
the rates of flow from the overhead tank to the inlet of the column in
achieving the same ponding depth. The experiments are performed
for different scenarios in which the height ratios are altered and the
variations of concentrations of Na, Ca, and K are observed. The study
brings an estimation of leaching in landfill sites for different heights
and precipitation intensity where a ponding depth is maintained over
the landfill. It has been observed that the leaching behavior of Na,
Ca, and K are not similar. Calcium exhibits highest amount of
leaching compared to Sodium and Potassium under similar
experimental conditions.
Abstract: The leaching behavior and structure of Li2O-CeO2- Fe2O3-P2O5 glasses incorporated with simulated high level nuclear wastes (HLW) were studied. The leach rates of gross and each constituent element were determined from the total weight loss of the specimen and the leachate analyses by inductively coupled argon plasma spectroscopy (ICP). The gross leach rate of the 4.5Li2O- 9.7CeO2-34.7Fe2O3-51.5P2O5 glass waste form containing 45 mass% simulated HLW is of the order of 10