Abstract: Laser beam welding of dissimilar sheet metal
combinations such as Ti/Al, SS/Al and Cu/Al are increasingly
demanded due to high energy densities with less fusion and heat
affected zones. A good weld joint strength involves combinations of
dissimilar metals and the formation of solid solution in the weld pool.
Many metal pairs suffer from significant intermetallic phase
formation during welding which greatly reduces their strength. The
three different sheet metal mentioned above is critically reviewed and
phase diagram for the combinations are given. The aim of this study
is to develop an efficient metal combinations and the influence on
their interfacial characteristics. For that the following parameters
such as weld geometry, residual distortion, micro hardness,
microstructure and mechanical properties are analyzed
systematically.
Abstract: Al/Cu clad sheet has been fabricated by using differential speed rolling (DSR) process, which caused severe shear deformation between Al and Cu plate to easily bond to each other. Rolling was carried out at 100 and 150oC with speed ratios from 1.4 to 2.2, in which the total thickness reduction was in the range between 14 and 46%. Interfacial microstructure and mechanical properties of Al/Cu clad were investigated by scanning electron microscope equipped with energy dispersive X-ray detector, and tension tests. The DSR process was very effective to provide a good interface for atoms diffusion during subsequent annealing. The strength of bonding was higher with the increasing speed ratio. Post heat treatment enhanced the mechanical properties of clad sheet by forming intermetallic compounds in the interface area.
Abstract: Aluminum/Copper clad sheet has been fabricated using
asymmetric extrusion method, which caused severe shear deformation
between Al and Cu plate to easily bond to each other. Interfacial
microstructure and mechanical properties of Al/Cu clad were studied
by scanning electron microscope equipped with energy dispersive
X-ray detector, micro-hardness, and tension tests. The asymmetric
extrusion bonding was very effective to provide a good interface for
atoms diffusion during subsequent annealing. The strength of bonding
was higher with the increasing extrusion ratio.