Abstract: Pressure vessels are usually operating at temperatures
where the conditions of linear elastic fracture mechanics are no
longer met because massive plasticity precedes crack propagation. In
this work the development of a surface crack in a pressure vessel
subject to bending and tension under elastic-plastic fracture
mechanics conditions was investigated. Finite element analysis was
used to evaluate the hydrostatic stress, the J-integral and crack
growth for semi-elliptical surface-breaking cracks. The results
showed non-uniform stress triaxiality and crack driving force around
the crack front at large deformation levels. Different ductile crack
extensions were observed which emphasis the dependent of ductile
tearing on crack geometry and type of loading. In bending the crack
grew only beneath the surface, and growth was suppressed at the
deepest segment. This contrasts to tension where the crack breaks
through the thickness with uniform growth along the entire crack
front except at the free surface. Current investigations showed that
the crack growth developed under linear elastic fracture mechanics
conditions will no longer be applicable under ductile tearing
scenarios.
Abstract: Tensile armour wires provide a flexible pipe's
resistance to longitudinal stresses. Flexible pipe manufacturers need
to know the effect of defects such as scratches and cracks, with
dimensions less than 0.2mm which is the limit of the current nondestructive
detection technology, on the fracture stress and fracture
strain of the wire for quality assurance purposes. Recent research
involving the determination of the fracture strength of cracked wires
employed laboratory testing and classical fracture mechanics
approach using non-standardised fracture mechanics specimens
because standard test specimens could not be manufactured from the
wires owing to their sizes. In this work, the effect of miniature
cracks on the fracture properties of tensile armour wires was
investigated using laboratory and finite element tensile testing
simulations with the phenomenological shear fracture model. The
investigation revealed that the presence of cracks shallower than
0.2mm is worse on the fracture strain of the wire.
Abstract: The incidence of mechanical fracture of an
automobile piston rings prompted development of fracture analysis
method on this case. The three rings (two compression rings and one
oil ring) were smashed into several parts during the power-test (after
manufacturing the engine) causing piston and liner to be damaged.
The radial and oblique cracking happened on the failed piston rings.
The aim of the fracture mechanics simulations presented in this paper
was the calculation of particular effective fracture mechanics
parameters, such as J-integrals and stress intensity factors. Crack
propagation angles were calculated as well. Two-dimensional
fracture analysis of the first compression ring has been developed in
this paper using ABAQUS CAE6.5-1 software. Moreover, SEM
fractography was developed on fracture surfaces and is discussed in
this paper. Results of numerical calculations constitute the basis for
further research on real object.
Abstract: The damage tolerance behavior of integrally and
conventional stiffened panel is investigated based on the fracture
mechanics and finite element analysis. The load bearing capability
and crack growth characteristic of both types of the stiffened panels
having same configuration subjected to distributed tensile load is
examined in this paper. A fourteen-stringer stiffened panel is
analyzed for a central skin crack propagating towards the adjacent
stringers. Stress intensity factors and fatigue crack propagation rates
of both types of the stiffened panels are then compared. The analysis
results show that integral stiffening causes higher stress intensity
factor than conventional stiffened panel as the crack tip passes
through the stringer and the integrally stiffened panel has less load
bearing capability than the riveted stiffened panel.