Abstract: Pressure vessels are usually operating at temperatures
where the conditions of linear elastic fracture mechanics are no
longer met because massive plasticity precedes crack propagation. In
this work the development of a surface crack in a pressure vessel
subject to bending and tension under elastic-plastic fracture
mechanics conditions was investigated. Finite element analysis was
used to evaluate the hydrostatic stress, the J-integral and crack
growth for semi-elliptical surface-breaking cracks. The results
showed non-uniform stress triaxiality and crack driving force around
the crack front at large deformation levels. Different ductile crack
extensions were observed which emphasis the dependent of ductile
tearing on crack geometry and type of loading. In bending the crack
grew only beneath the surface, and growth was suppressed at the
deepest segment. This contrasts to tension where the crack breaks
through the thickness with uniform growth along the entire crack
front except at the free surface. Current investigations showed that
the crack growth developed under linear elastic fracture mechanics
conditions will no longer be applicable under ductile tearing
scenarios.