Abstract: Aluminium bronze alloys are well known for their superior abrasion, tensile strength and non-magnetic properties, due to the co-presence of iron (Fe) and aluminium (Al) as alloying elements and have been commonly used in many industrial applications. However, continuous exposure to the marine environment will accelerate the risk of a tendency to Al bronze alloys parts failures. Although a higher level of corrosion resistance properties can be achieved by modifying its elemental composition, it will come at a price through the complex manufacturing process and increases the risk of reducing the ductility of Al bronze alloy. In this research, the use of ironmaking slag and waste plastic as the input source for surface modification of Al bronze alloy was implemented. Microstructural analysis conducted using polarised light microscopy and scanning electron microscopy (SEM) that is equipped with energy dispersive spectroscopy (EDS). An electrochemical corrosion test was carried out through Tafel polarisation method and calculation of protection efficiency against the base-material was determined. Results have indicated that uniform modified surface which is as the result of selective diffusion process, has enhanced corrosion resistance properties up to 12.67%. This approach has opened a new opportunity to access various industrial utilisations in commercial scale through minimising the dependency on natural resources by transforming waste sources into the protective coating in environmentally friendly and cost-effective ways.
Abstract: Corrosion problem which exists in every stage of oil and gas production has been a great challenge to the operators in the industry. The conventional carbon steel with all its inherent advantages has been adjudged susceptible to the aggressive corrosion environment of oilfield. This has aroused increased interest in the use of micro alloyed steels for oil and gas production and transportation. The corrosion behavior of three commercially supplied micro alloyed steels designated as A, B, and C have been investigated with API 5L X65 as reference samples. Electrochemical corrosion tests were conducted in an unbuffered 3.5 wt% NaCl solution saturated with CO2 at 30 0C for 24 hours. Pre-corrosion analyses revealed that samples A, B and X65 consist of ferrite-pearlite microstructures but with different grain sizes, shapes and distribution whereas sample C has bainitic microstructure with dispersed acicular ferrites. The results of the electrochemical corrosion tests showed that within the experimental conditions, the corrosion rate of the samples can be ranked as CR(A)< CR(X65)< CR(B)< CR(C). These results are attributed to difference in microstructures of the samples as depicted by ASTM grain size number in accordance with ASTM E112-12 Standard and ferrite-pearlite volume fractions determined by ImageJ Fiji grain size analysis software.
Abstract: Increase in population has increased the demand of energy to fulfill all its needs. This will result in burden on fossil fuels especially crude oil. Waste oil due to its disposal problem creates environmental degradation. In this context, this paper studies utilization of waste cooking oil and waste motor sludge for making lubricating grease. Experimental studies have been performed by variation in time and concentration of mixture of waste cooking oil and waste motor sludge. The samples were analyzed using penetration test (ASTM D-217), dropping point (ASTM D-566), work penetration (ASTM D-217) and copper strip test (ASTM D-408). Among 6 samples, sample 6 gives the best results with a good drop point and a fine penetration value. The dropping point and penetration test values were found to be 205 °C and 315, respectively. The penetration value falls under the category of NLGI (National Lubricating Grease Institute) consistency number 1.
Abstract: The corrosion behaviour of 316L stainless steel coatings obtained by cold spray method was investigated in this study. 316L powders were deposited onto Al5052 aluminum substrates. The coatings were produced using nitrogen (N2) process gas. In order to further improve the corrosion and mechanical properties of the coatings, heat treatment was applied at 250 and 750 °C. The corrosion performances of the coatings were compared using the potentiodynamic scanning (PDS) technique under in-vitro conditions (in Ringer’s solution at 37 °C). In addition, the hardness and porosity tests were carried out on the coatings. Microstructural characterization of the coatings was carried out by using scanning electron microscopy attached with energy dispersive spectrometer (SEM-EDS) and X-ray diffraction (XRD) technique. It was found that clean surfaces and a good adhesion were achieved for particle/substrate bonding. The heat treatment process provided both elimination of the anisotropy in the coating and resulting in healing-up of the incomplete interfaces between the deposited particles. It was found that the corrosion potential of the annealed coatings at 750 °C was higher than that of commercially 316 L stainless steel. Moreover, the microstructural investigations after the corrosion tests revealed that corrosion preferentially starts at inter-splat boundaries.
Abstract: The atmospheres in many cities along the coastal lines
in the world have been rapidly changed to coastal-industrial
atmosphere. Hence, it is vital to investigate the corrosion behavior of
steel exposed to this kind of environment. In this present study,
Electrochemical Impedance Spectrography (EIS) and film thickness
measurement were applied to monitor the corrosion behavior of
weathering steel covered with a thin layer of the electrolyte in a
wet-dry cyclic condition, simulating a coastal-industrial environment
at 25oC and 60% RH. The results indicate that in all cycles, the
corrosion rate increases during the drying process due to an increase in
anion concentration and an acceleration of oxygen diffusion enhanced
by the effect of the thinning out of the electrolyte. During the wet-dry
cyclic corrosion test, the long-term corrosion behavior of this steel
depends on the periods of exposure. Corrosion process is first
accelerated and then decelerated. The decelerating corrosion process is
contributed to the formation of the protective rust, favored by the
wet-dry cycle and the acid regeneration process during the rusting
process.
Abstract: Concerns on corrosion and effective coating
protection of double hull tankers and bulk carriers in service have
been raised especially in water ballast tanks (WBTs). Test
protocols/methodologies specifically that which is incorporated in the
International Maritime Organisation (IMO), Performance Standard
for Protective Coatings for Dedicated Sea Water ballast tanks (PSPC)
are being used to assess and evaluate the performance of the coatings
for type approval prior to their application in WBTs. However, some
of the type approved coatings may be applied as very thick films to
less than ideally prepared steel substrates in the WBT. As such films
experience hygrothermal cycling from operating and environmental
conditions, they become embrittled which may ultimately result in
cracking. This embrittlement of the coatings is identified as an
undesirable feature in the PSPC but is not mentioned in the test
protocols within it. There is therefore renewed industrial research
aimed at understanding this issue in order to eliminate cracking and
achieve the intended coating lifespan of 15 years in good condition.
This paper will critically review test protocols currently used for
assessing and evaluating coating performance, particularly the IMO
PSPC.
Abstract: In this study, a plasma electrolytic oxidation (PEO) process was used to form titanium-aluminum oxide coating on aluminized steel. The present work was mainly to study the effects of treatment time of PEO process on properties of the titanium coating. A potentiodynamic polarization corrosion test was employed to investigate the corrosion resistance of the coating. The friction coefficient and wear resistance of the coating were studied by using pin-on-disc test. The thermal transfer behaviors of uncoated and PEO-coated aluminized steels were also studied. It could be seen that treatment time of PEO process significantly influenced the properties of the titanium oxide coating. Samples with a longer treatment time had a better performance for corrosion and wear protection. This paper demonstrated different treatment time could alter the surface behavior of the coating material.
Abstract: Different vegetable oil based biodiesel (FAMES) were prepared by alkaline transesterification using refined oils as well as waste frying oil (WFO). Methanol and sodium hydroxide are used as catalyst under similar reaction conditions. To ensure the quality of biodiesel produced, a series of different ASTM Standard tests were carried out. In this context, various testwere done including viscosity, carbon residue, specific gravity, corrosion test, flash point, cloud point and pour point. Results revealed that characteristics of biodiesel depend on the feedstock and it is far better than petroleum diesel.
Abstract: Biodisel is a type of biofuel having similar properties of diesel fuel but lacks substances (undesirable emissions) such as sulfur, nitrogen and aromatic polycyclic. Upon filtration of waste oil, the biodiesel fuel was produced via carrying out transestrification reaction of triglycerides followed by conducting viscosity, density, flash point, cloud point, pour point and copper strip corrosion tests on the samples and comparing with EN14214 and ASTM 6751 standards and all results were found in the permitted limit. The highest yield of biodiesel production reaction was found 46.6435 g when Sodium Hydroxide catalyst in amount of 0.375g was employed, 44.2347 g when Sodium methoxide catalyst in amount of 0.5g was employed and 56.5124 g when acid sulfuric catalyst in amount of 1g was employed and 47.3290 g when two stage reaction was done.
Abstract: There was a high rate of corrosion in Pyrolysis
Gasoline Hydrogenation (PGH) unit of Arak Petrochemical Company
(ARPC), and it caused some operational problem in this plant. A
commercial chemical had been used as anti-corrosion in the
depentanizer column overhead in order to control the corrosion rate.
Injection of commercial corrosion inhibitor caused some
operational problems such as fouling in some heat exchangers. It was
proposed to replace this commercial material with another more
effective trouble free, and well-known additive by R&D and
operation specialists.
At first, the system was simulated by commercial simulation
software in electrolytic system to specify low pH points inside the
plant. After a very comprehensive study of the situation and technical
investigations ,ammonia / monoethanol amine solution was proposed
as neutralizer or corrosion inhibitor to be injected in a suitable point
of the plant. For this purpose, the depentanizer column and its
accessories system was simulated again in case of this solution
injection.
According to the simulation results, injection of new anticorrosion
substance has no any side effect on C5 cut product and
operating conditions of the column. The corrosion rate will be
cotrolled, if the pH remains at the range of 6.5 to 8 . Aactual plant
test run was also carried out by injection of ammonia / monoethanol
amine solution at the rate of 0.6 Kg/hr and the results of iron content
of water samples and corrosion test coupons confirmed the
simulation results.
Now, ammonia / monoethanol amine solution is injected to a
suitable pint inside the plant and corrosion rate has decreased
significantly.
Abstract: Magnesium alloys have gained increased attention in recent years in automotive, electronics, and medical industry. This because of magnesium alloys have better properties than aluminum alloys and steels in respects of their low density and high strength to weight ratio. However, the main problems of magnesium alloy welding are the crack formation and the appearance of porosity during the solidification. This paper proposes a unique technique to weld two thin sheets of AZ31B magnesium alloy using a paste containing Ag nanoparticles. The paste containing Ag nanoparticles of 5 nm in average diameter and an organic solvent was used to coat the surface of AZ31B thin sheet. The coated sheet was heated at 100 °C for 60 s to evaporate the solvent. The dried sheet was set as a lower AZ31B sheet on the jig, and then lap fillet welding was carried out by using a pulsed Nd:YAG laser in a closed box filled with argon gas. The characteristics of the microstructure and the corrosion behavior of the joints were analyzed by opticalmicroscopy (OM), energy dispersive spectrometry (EDS), electron probe micro-analyzer (EPMA), scanning electron microscopy (SEM), and immersion corrosion test. The experimental results show that the wrought AZ31B magnesium alloy can be joined successfully using Ag nanoparticles. Ag nanoparticles insert promote grain refinement, narrower the HAZ width and wider bond width compared to weld without and insert. Corrosion rate of welded AZ31B with Ag nanoparticles reduced up to 44 % compared to base metal. The improvement of corrosion resistance of welded AZ31B with Ag nanoparticles due to finer grains and large grain boundaries area which consist of high Al content. β-phase Mg17Al12 could serve as effective barrier and suppressed further propagation of corrosion. Furthermore, Ag distribution in fusion zone provide much more finer grains and may stabilize the magnesium solid solution making it less soluble or less anodic in aqueous