Abstract: An important problem for the CaSO4/CaSO4・1/2H2O
Chemical heat pump (CHP) is that the material is deactivated through
repetitive reaction between hydration and dehydration in which the
crystal phase of the material is transformed from III-CaSO4 to
II-CaSO4. We investigated suppression on the phase change by adding
a sulfated compound. The most effective material was MgSO4. MgSO4
doping increased the durability of CaSO4 in the actual CHP repetitive
cycle of hydration/dehydration to 3.6 times that of undoped CaSO4.
The MgSO4-doped CaSO4 showed a higher phase transition
temperature and activation energy for crystal transformation from
III-CaSO4 to II-CaSO4. MgSO4 doping decreased the crystal lattice
size of CaSO4・1/2H2O and II-CaSO4 to smaller than that of undoped
CaSO4. Modification of the crystal structure is considered to be related
to the durability change in CaSO4 resulting from MgSO4 doping.
Abstract: Gypsum (CaSO4.2H2O) is a mineral that is found in
large quantities in the Turkey and in the World. In this study, the
dissolution of this mineral in the diammonium hydrogen phosphate
solutions has been studied. The dissolution and dissolution kinetics of
gypsum in diammonium hydrogen phosphate solutions will be useful
for evaluating of solid wastes containing gypsum. Parameters such as
diammonium hydrogen phosphate concentration, temperature and
stirring speed affecting on the dissolution rate of the gypsum in
diammonium hydrogen phosphate solutions were investigated. In
experimental studies have researched effectiveness of the selected
parameters. The dissolution of gypsum were examined in two parts at
low and high temperatures. The experimental results were
successfully correlated by linear regression using Statistica program.
Dissolution curves were evaluated shrinking core models for solidfluid
systems. The activation energy was found to be 34.58 kJ/mol
and 44.45 kJ/mol for the low and the high temperatures. The
dissolution of gypsum was controlled by chemical reaction both low
temperatures and high temperatures.
Abstract: This paper involved the performance of a hightemperature
X-Ray powder diffraction analysis (XRD) of a sample of
chemical gypsum generated in the production of titanium white; this
gypsum originates by neutralizing highly acidic water with limestone
suspension. Specifically, it was gypsum formed in the first stage of
neutralization when the resulting material contains, apart from
gypsum, a number of waste products resulting from the
decomposition of ilmenite by sulphuric acid. So it can be described as
red titanogypsum. By conducting the experiment using XRD
apparatus Bruker D8 Advance with a Cu anode (λkα=1.54184 Å)
equipped with high-temperature chamber Anton Paar HTK 16, it was
possible to identify clearly in the sample each phase transition in the
system of CaSO4·xH2O.
Abstract: The reduction of greenhouse gases emissions is highly
discussed ecological theme at present. In addition to power industry
also main production sectors of binders, i.e. cement, air and hydraulic
lime are very sensitive to these questions. One of the possibilities
how CO2 emissions can be reduced directly at clinker burnout is
represented by partial substitution of lime with a material containing
limy ions at absence of carbonate group. Fluidised fly ash is one of
such potential raw materials where CaO can be found free and also
bound in anhydrite, CaSO4. At application of FBC (fluidized bed
combustion) fly ash with approximate 20% CaO content and its
dosing ratio to high percent lime 1:2, corresponding stechiometrically
to the preparation of raw material powder, approximately 0,37 t CO2
per 1 ton of one-component cement would be released at clinker
burnout compared to 0,46 t CO2 when orthodox raw materials are
used. The reduction of CO2 emissions thus could reach even 20%.
Abstract: A phase diagram of the Ag2SO4 - CaSO4 (Silver sulphate – Calcium Sulphate) binaries system using conductivity, XRD (X-Ray Diffraction Technique) and DTA (Differential Thermal Analysis) data is constructed. The eutectic reaction (liquid -» a-Ag2SO4 + CaSO4) is observed at 10 mole% CaSO4 and 645°C. Room temperature solid solubility limit up to 5.27 mole % of Ca 2+ in Ag2SO4 is set using X-ray powder diffraction and scanning electron microscopy results. All compositions beyond this limit are two-phase mixtures below and above the transition temperature (≈ 416°C). The bulk conductivity, obtained following complex impedance spectroscopy, is found decreasing with increase in CaSO4 content. Amongst other binary compositions, the 80AgSO4-20CaSO4 gave improved sinterability/packing density.
Abstract: In order to study of hydropriming and halopriming on
germination and early growth stage of wheat (Triticum aestivum) an
experiment was carried out in laboratory of the Department of
Agronomy and Plant breeding, Shahrood University of Technology.
Seed treatments consisted of T1: control (untreated seeds), T2:
soaking in distilled water for 18 h (hydropriming). T3: soaking in -
1.2 MPa solution of CaSO4 for 36 h (halopriming). Germination and
early seedling growth were studied using distilled water (control) and
under osmotic potentials of -0.4, -0.8 and -1.2 MPa for NaCl and
polyethylene glycol (PEG 6000), respectively. Results showed that
Hydroprimed seeds achieved maximum germination seedling dry
weight, especially during the higher osmotic potentials. Minimum
germination was recorded at untreated seeds (control) followed by
osmopriming. Under high osmotic potentials, hydroprimed seeds had
higher GI (germination index) as compared to haloprimed or
untreated seeds. Interaction effect of seed treatment and osmotic
potential significantly affected the seedling vigour index (SVI).