Abstract: TiO2/MgO composite films were prepared by coating
the magnesium acetate solution in the pores of mesoporous TiO2
films using a dip coating method. Concentrations of magnesium
acetate solution were varied in a range of 1x10-4 – 1x10-1 M. The
TiO2/MgO composite films were characterized by scanning electron
microscopy (SEM), transmission electron microscropy (TEM),
electrochemical impedance spectroscopy(EIS) , transient voltage
decay and I-V test. The TiO2 films and TiO2/MgO composite films
were immersed in a 0.3 mM N719 dye solution. The Dye-sensitized
solar cells with the TiO2/MgO/N719 structure showed an optimal
concentration of magnesium acetate solution of 1x10-3 M resulting in
the MgO film estimated thickness of 0.0963 nm and giving the
maximum efficiency of 4.85%. The improved efficiency of dyesensitized
solar cell was due to the magnesium oxide film as the wide
band gap coating decays the electron back transfer to the triiodide
electrolyte and reduce charge recombination.
Abstract: ZnS nanoparticles of different size have been
synthesized using a colloidal particles method. Zns nanoparticles
prepared with capping agent (mercaptoethanol) then were
characterized using X-ray diffraction (XRD) and UV-Vis
spectroscopy. The particle size of the nanoparticles calculated from
the XRD patterns has been found in the range 1.85-2.44nm.
Absorption spectra have been obtained using UV-Vis
spectrophotometer to find the optical band gap and the obtained
values have been founded to being range 3.83-4.59eV. It was also
found that energy band gap increase with the increase in molar
capping agent solution.
Abstract: In this investigation, anatase TiO2 thin films were
grown by radio frequency magnetron sputtering on glass substrates at
a high sputtering pressure and room temperature. The anatase films
were then annealed at 300-600 °C in air for a period of 1 hour. To
examine the structure and morphology of the films, X-ray diffraction
(XRD) and atomic force microscopy (AFM) methods were used
respectively. From X-ray diffraction patterns of the TiO2 films, it was
found that the as-deposited film showed some differences compared
with the annealed films and the intensities of the peaks of the
crystalline phase increased with the increase of annealing
temperature. From AFM images, the distinct variations in the
morphology of the thin films were also observed. The optical
constants were characterized using the transmission spectra of the
films obtained by UV-VIS-IR spectrophotometer. Besides, optical
thickness of the film deposited at room temperature was calculated
and cross-checked by taking a cross-sectional image through SEM.
The optical band gaps were evaluated through Tauc model. It was
observed that TiO2 films produced at room temperatures exhibited
high visible transmittance and transmittance decreased slightly with
the increase of annealing temperatures. The films were found to be
crystalline having anatase phase. The refractive index of the films
was found from 2.31-2.35 in the visible range. The extinction
coefficient was nearly zero in the visible range and was found to
increase with annealing temperature. The allowed indirect optical
band gap of the films was estimated to be in the range from 3.39 to
3.42 eV which showed a small variation. The allowed direct band
gap was found to increase from 3.67 to 3.72 eV. The porosity was
also found to decrease at a higher annealing temperature making the
film compact and dense.