Abstract: spherical porous carbon particles with
controllable porosity with a mean size of 2.5m have been
prepared using a spray drying method with organic particle
colloidal template. As a precursor, a mixing solution of carbon
nanopowder and polystyrene (PS) particles as a template was
used. The result showed that the particles with a good porous
structure could be obtained. The pore size and shape (spherical)
were identical to the initial template, giving a potential way for
further developments. The control of particle porosity was also
possible and reported in this paper, in which this control could
be achieved by means of PS concentration.
Abstract: Combined experimental and computational analysis of
hygrothermal performance of an interior thermal insulation system
applied on a brick wall is presented in the paper. In the experimental
part, the functionality of the insulation system is tested at simulated
difference climate conditions using a semi-scale device. The
measured temperature and relative humidity profiles are used for the
calibration of computer code HEMOT that is finally applied for a
long-term hygrothermal analysis of the investigated structure.
Abstract: This paper presents the modeling results of an
innovative system for the temperature control in the interior
compartment of a stationary automobile facing the solar energy from
the sun. A very thin layer of PCM inside a pouch placed in the
ceiling of the car in which the heating energy is absorbed and release
with melting and solidification of phase change materials. As a result
the temperature of the car interior is maintained in the comfort
condition. The amount of required PCM has been calculated to be
about 755 g. The PCM-temperature controlling system is simple and
has a potential to be implemented as a practical solution to prevent
undesirable heating of the automobile-s cabin.
Abstract: Herein, the organic semiconductor methyl orange
(MO), is investigated for the first time for its electronic applications.
For this purpose, Al/MO/n-Si heterojunction is fabricated through
economical cheap and simple “drop casting” technique. The currentvoltage
(I-V) measurements of the device are made at room
temperature under dark conditions. The I-V characteristics of
Al/MO/n-Si junction exhibits asymmetrical and rectifying behavior
that confirms the formation of diode. The diode parameters such as
rectification ratio (RR), turn on voltage (Vturn on), reverse saturation
current (I0), ideality factor (n), barrier height ( b
f ), series resistance
(Rs) and shunt resistance (Rsh) are determined from I-V curves using
Schottky equations. These values of these parameters are also
extracted and verified by applying Cheung’s functions. The
conduction mechanisms are explained from the forward bias I-V
characteristics using the power law.
Abstract: Experimental investigation of the effect of
hydrophobic injection on siloxane basis on the properties of oldfashioned
type of ceramic brick is presented in the paper. At the
experimental testing, the matrix density, total open porosity, pore size
distribution, sorptivity, water absorption coefficient, sorption and
desorption isotherms are measured for the original, as well as the
hydrophobic-injection treated brick. On the basis of measured data,
the functionality of the hydrophobic injection for the moisture ingress
prevention into the studied ceramic brick is assessed.
Abstract: The current practice of determination of moisture diffusivity of building materials under laboratory conditions is predominantly aimed at the absorption phase. The main reason is the simplicity of the inverse analysis of measured moisture profiles. However, the liquid moisture transport may exhibit significant hysteresis. Thus, the moisture diffusivity should be different in the absorption (wetting) and desorption (drying) phase. In order to bring computer simulations of hygrothermal performance of building materials closer to the reality, it is then necessary to find new methods for inverse analysis which could be used in the desorption phase as well. In this paper we present genetic algorithm as a possible method of solution of the inverse problem of moisture transport in desorption phase. Its application is demonstrated for AAC as a typical building material.
Abstract: Thermal water hammer is a special type of water
hammer which rarely occurs in heat exchangers. In biphasic fluids, if
steam bubbles are surrounded by condensate, regarding lower
condensate temperature than steam, they will suddenly collapse. As a
result, the vacuum caused by an extreme change in volume lead to
movement of the condensates in all directions and their collision the
force produced by this collision leads to a severe stress in the pipe
wall. This phenomenon is a special type of water hammer. According
to fluid mechanics, this phenomenon is a particular type of transient
flows during which abrupt change of fluid leads to sudden pressure
change inside the tube. In this paper, the mechanism of abrupt failure
of 80 tubes of 481 tubes of a methanol heat exchanger is discussed.
Initially, due to excessive temperature differences between heat
transfer fluids and simultaneous failure of 80 tubes, thermal shock
was presupposed as the reason of failure. Deeper investigation on
cross-section of failed tubes showed that failure was, ductile type of
failure, so the first hypothesis was rejected. Further analysis and more
accurate experiments revealed that failure of tubes caused by thermal
water hammer. Finally, the causes of thermal water hammer and
various solutions to avoid such mechanism are discussed.
Abstract: In this study, mechanically alloyed Al 2024 powder is
densified by conventional sintering and by equal channel angular
pressing (ECAP) with and without back pressure. The powder was
encapsulated in an aluminium can for consolidation through ECAP.
The properties obtained in the compacts by conventional sintering
route and by ECAP are compared. The effect of conventional
sintering and ECAP on consolidation behaviour of powder,
microstructure, density and hardness is discussed. Room temperature
back pressure aided ECAP results in nearly full denser (97% of its
theoretical density) compact at room temperature. NanoIndentation
technique was used to determine the modulus of the consolidated
compacts.
Abstract: In this study, single nozzle method used for
electrospinning technique which composite polymer solution with
cellulose nanowiskers (CNW) was treated by ultrasonic sonificator
have been compared with coaxial (double) nozzle method, in terms of
mechanical, thermal and morphological properties of composite
nanofiber. The effect of water content in composite polymer solution
on properties of nanofiber has also been examined. It has been seen
that single nozzle method which polymer solution does not contain
water has better results than that of coaxial method, in terms of
mechanical, thermal and morphological properties of nanofiber.
However, it is necessary to make an optimization study on setting
condition of ultrasonic treatment to get better dispersion of CNW in
composite nanofiber and to get better mechanical and thermal
properties
Abstract: The aim of our work is to study phase composition,
particle size and magnetic response of Fe2O3/TiO2 nanocomposites
with respect to the final annealing temperature. Those nanomaterials
are considered as smart catalysts, separable from a liquid/gaseous
phase by applied magnetic field. The starting product was obtained
by an ecologically acceptable route, based on heterogeneous
precipitation of the TiO2 on modified g-Fe2O3 nanocrystals dispersed
in water. The precursor was subsequently annealed on air at
temperatures ranging from 200 oC to 900 oC. The samples were
investigated by synchrotron X-ray powder diffraction (S-PXRD),
magnetic measurements and Mössbauer spectroscopy. As evidenced
by S-PXRD and Mössbauer spectroscopy, increasing the annealing
temperature causes evolution of the phase composition from
anatase/maghemite to rutile/hematite, finally above 700 oC the
pseudobrookite (Fe2TiO5) also forms. The apparent particle size of
the various Fe2O3/TiO2 phases has been determined from the highquality
S-PXRD data by using two different approaches: the Rietveld
refinement and the Debye method. Magnetic response of the samples
is discussed in considering the phase composition and the particle
size.