Abstract: Calcium oxide (CaO) as carbon dioxide (CO2)
adsorbent at the elevated temperature has been very well-received
thus far. The CaO can be synthesized from natural calcium carbonate
(CaCO3) sources through the reversible calcination-carbonation
process. In the study, cockle shell has been selected as CaO
precursors. The objectives of the study are to investigate the
performance of calcination and carbonation with respect to different
temperature, heating rate, particle size and the duration time. Overall,
better performance is shown at the calcination temperature of 850oC
for 40 minutes, heating rate of 20oC/min, particle size of < 0.125mm
and the carbonation temperature is at 650oC. The synthesized
materials have been characterized by nitrogen physisorption and
surface morphology analysis. The effectiveness of the synthesized
cockle shell in capturing CO2 (0.72 kg CO2/kg adsorbent) which is
comparable to the commercialized adsorbent (0.60 kg CO2/kg
adsorbent) makes them as the most promising materials for CO2
capture.
Abstract: As the fossil fuels kept on depleting, intense research in developing hydrogen (H2) as the alternative fuel has been done to cater our tremendous demand for fuel. The potential of H2 as the ultimate clean fuel differs with the fossil fuel that releases significant amounts of carbon dioxide (CO2) into the surrounding and leads to the global warming. The experimental work was carried out to study the production of H2 from palm kernel shell steam gasification at different variables such as heating rate, steam to biomass ratio and adsorbent to biomass ratio. Maximum H2 composition which is 61% (volume basis) was obtained at heating rate of 100oCmin-1, steam/biomass of 2:1 ratio, and adsorbent/biomass of 1:1 ratio. The commercial adsorbent had been modified by utilizing the alcoholwater mixture. Characteristics of both adsorbents were investigated and it is concluded that flowability and floodability of modified CaO is significantly improved.