Abstract: A composite made of plasma functionalized multiwall
carbon nanotubes (MWNTs) coated with SnO2 was synthesized by
sonochemical precipitation method. Thick layer of this
nanocomposite material was used as ethanol sensor at low
temperatures. The composite sensitivity for ethanol has increased by
a factor of 2 at room temperature and by a factor of 13 at 250°C in
comparison to that of pure SnO2. SEM image of nanocomposite
material showed MWNTs were embedded in SnO2 matrix and also a
higher surface area was observed in the presence of functionalized
MWNTs. Greatly improved sensitivity of the composite material to
ethanol can be attributed to new gas accessing passes through
MWNTs and higher specific surface area.
Abstract: The paper reports the preparation and photocatalytic
activity of ZnO/SnO2 and SnO2 nanoparticles. These nanoparticles
were synthesized by hydrothermal method. The products were
characterized by X-ray diffraction (XRD) and scanning electron
microscopy (SEM). Their grain sizes are about 50-100 nm. The
photocatalytic activities of these materials were investigated for
congo red removal from aqueous solution under UV light irradiation.
It was shown that the use of ZnO/SnO2 as photocatalyst have better
photocatalytic activity for degradation of congo red than SnO2 or
TiO2 (anatase, particle size: 30nm) alone.
Abstract: In this study, a low temperature sensor highly selective to CO in presence of methane is fabricated by using 4 nm SnO2 quantum dots (QDs) prepared by sonication assisted precipitation. SnCl4 aqueous solution was precipitated by ammonia under sonication, which continued for 2 h. A part of the sample was then dried and calcined at 400°C for 1.5 h and characterized by XRD and BET. The average particle size and the specific surface area of the SnO2 QDs as well as their sensing properties were compared with the SnO2 nano-particles which were prepared by conventional sol-gel method. The BET surface area of sonochemically as-prepared product and the one calcined at 400°C after 1.5 hr are 257 m2/gr and 212 m2/gr respectively while the specific surface area for SnO2 nanoparticles prepared by conventional sol-gel method is about 80m2/gr. XRD spectra revealed pure crystalline phase of SnO2 is formed for both as-prepared and calcined samples of SnO2 QDs. However, for the sample prepared by sol-gel method and calcined at 400°C SnO crystals are detected along with those of SnO2. Quantum dots of SnO2 show exceedingly high sensitivity to CO with different concentrations of 100, 300 and 1000 ppm in whole range of temperature (25- 350°C). At 50°C a sensitivity of 27 was obtained for 1000 ppm CO, which increases to a maximum of 147 when the temperature rises to 225°C and then drops off while the maximum sensitivity for the SnO2 sample prepared by the sol-gel method was obtained at 300°C with the amount of 47.2. At the same time no sensitivity to methane is observed in whole range of temperatures for SnO2 QDs. The response and recovery times of the sensor sharply decreases with temperature, while the high selectivity to CO does not deteriorate.
Abstract: The selection of parents and breeding strategies for
the successful maize hybrid production will be facilitated by
heterotic groupings of parental lines and determination of combining
abilities of them. Fourteen maize inbred lines, used in maize breeding
programs in Iran, were crossed in a diallel mating design. The 91 F1
hybrids and the 14 parental lines were studied during two years at
four locations of Iran for investigation of combining ability of
gentypes for grain yield and to determine heterotic patterns among
germplasm sources, using both, the Griffing-s method and the biplot
approach for diallel analysis. The graphical representation offered by
biplot analysis allowed a rapid and effective overview of general
combining ability (GCA) and specific combining ability (SCA)
effects of the inbred lines, their performance in crosses, as well as
grouping patterns of similar genotypes. GCA and SCA effects were
significant for grain yield (GY). Based on significant positive GCA
effects, the lines derived from LSC could be used as parent in crosses
to increase GY. The maximum best- parent heterosis values and
highest SCA effects resulted from crosses B73 × MO17 and A679 ×
MO17 for GY. The best heterotic patterns were LSC × RYD, which
would be potentially useful in maize breeding programs to obtain
high-yielding hybrids in the same climate of Iran.