Abstract: This study presents an investigation of
electrochemical variables and an application of the optimal
parameters in operating a continuous upflow electrocoagulation
reactor in removing dye. Direct red 23, which is azo-based, was used
as a representative of direct dyes. First, a batch mode was employed
to optimize the design parameters: electrode type, electrode distance,
current density and electrocoagulation time. The optimal parameters
were found to be iron anode, distance between electrodes of 8 mm
and current density of 30 A·m-2 with contact time of 5 min. The
performance of the continuous upflow reactor with these parameters
was satisfactory, with >95% color removal and energy consumption
in the order of 0.6-0.7 kWh·m-3.
Abstract: The electrochemical coagulation of a kaolin
suspension was investigated at the currents of 0.06, 0.12, 0.22, 0.44,
0.85 A (corresponding to 0.68, 1.36, 2.50, 5.00, 9.66 mA·cm-2,
respectively) for the contact time of 5, 10, 20, 30, and 50 min. The
TSS removal efficiency at currents of 0.06 A, 0.12 A and 0.22 A
increased with the amount of iron generated by the sacrificial anode,
while the removal efficiencies did not increase proportionally with
the amount of iron generated at the currents of 0.44 and 0.85 A,
where electroflotation was clearly observed. Zeta potential
measurement illustrated the presence of the highly positive charged
particles created by sorption of highly charged polymeric metal
hydroxyl species onto the negative surface charged kaolin particles at
both low and high applied currents. The disappearance of the
individual peaks after certain contact times indicated the attraction
between these positive and negative charged particles causing
agglomeration. It was concluded that charge neutralization of the
individual species was not the only mechanism operating in the
electrocoagulation process at any current level, but electrostatic
attraction was likely to co-operate or mainly operate.