Abstract: Firstly, in order to examine the influence of the remaining amount of the rust on the coating film durability, the accelerated deterioration tests were carried out. In order to prepare test specimens, uncoated steel plates were corroded by the Salt Spray Test (SST) prior to the accelerated deterioration tests, and then the prepared test specimens were coated by epoxy resin and phthalic acid resin each of which has different gas-barrier performance. As the result, it was confirmed that the under-film corrosion occurred in the area and the adjacency to great quantities of salt exists in the rust, and did not occurred in the specimen which was applied the epoxy resin paint after the surface preparation by the power tool. Secondly, in order to clarify the influence of the corrosive factors on the coating film durability, outdoor exposure tests were conducted for one year on actual steel bridge located at a coastal area. The tests specimens consist of coated corroded plates and the uncoated steel plates, and they were installed on the different structural members of the bridge for one year. From the test results, the uncoated steel plates which were installed on the underside of the member are easily corrosive and had highly correlation with the amount of salt in the rust. On the other hand, the most corrosive under-film steel was the vertical surface of the web plate. Thus, it was confirmed that under-film corrosion rate was not match with corrosion rate of the uncoated steel. Consequently, it is estimated that the main factors of under-film corrosion are gas-barrier property of coating film and corrosive factors such as water vapor and temperature. The salt which significantly corrodes the uncoated steel plate is not directly related to the under-film corrosion.
Abstract: A composite material with carbon fiber and polymer
matrix has been used as adherent for manufacturing adhesive joints.
In order to evaluate different fiber orientations on joint performance,
the adherents with the 0°, ±15°, ±30°, ±45° fiber orientations were
used in the single lap joint configuration. The joints with an overlap
length of 25 mm were prepared according to the ASTM 1002
specifications and subjected to tensile loadings. The structural
adhesive used was a two-part epoxy to be cured at 70°C for an hour.
First, mechanical behaviors of the adherents were measured using
three point bending test. In the test, considerations were given to
stress to failure and elastic modulus. The results were compared with
theoretical ones using rule of mixture. Then, the joints were
manufactured in a specially prepared jig, after a proper surface
preparation. Experimental results showed that the fiber orientations
of the adherents affected the joint performance considerably; the
joints with ±45° adherents experienced the worst shear strength, half
of those with 0° adherents, and in general, there was a great
relationship between the fiber orientations and failure mechanisms.
Delamination problems were observed for many joints, which were
thought to be due to peel effects at the ends of the overlap. It was
proved that the surface preparation applied to the adherent surface
was adequate. For further explanation of the results, a numerical
work should be carried out using a possible non-linear analysis.
Abstract: Shrunken patterning for integrated device
manufacturing requires surface cleanliness and surface smoothness in
wet chemical processing [1]. It is necessary to control all process
parameters perfectly especially for the common cleaning technique
RCA clean (SC-1 and SC-2) [2]. In this paper the characteristic and
effect of surface preparation parameters are discussed. The properties
of RCA wet chemical processing in silicon technology is based on
processing time, temperature, concentration and megasonic power of
SC-1 and QDR. An improvement of wafer surface preparation by
the enhanced variables of the wet cleaning chemical process is
proposed.
Abstract: Adhesion strength of exterior or interior coating of
steel pipes is too important. Increasing of coating adhesion on
surfaces can increase the life time of coating, safety factor of
transmitting line pipe and decreasing the rate of corrosion and costs.
Preparation of steel pipe surfaces before doing the coating process is
done by shot and grit blasting. This is a mechanical way to do it.
Some effective parameters on that process, are particle size of
abrasives, distance to surface, rate of abrasive flow, abrasive physical
properties, shapes, selection of abrasive, kind of machine and its
power, standard of surface cleanness degree, roughness, time of
blasting and weather humidity. This search intended to find some
better conditions which improve the surface preparation, adhesion
strength and corrosion resistance of coating. So, this paper has
studied the effect of varying abrasive flow rate, changing the
abrasive particle size, time of surface blasting on steel surface
roughness and over blasting on it by using the centrifugal blasting
machine. After preparation of numbers of steel samples (according to
API 5L X52) and applying epoxy powder coating on them, to
compare strength adhesion of coating by Pull-Off test. The results
have shown that, increasing the abrasive particles size and flow rate,
can increase the steel surface roughness and coating adhesion
strength but increasing the blasting time can do surface over blasting
and increasing surface temperature and hardness too, change,
decreasing steel surface roughness and coating adhesion strength.
Abstract: One of the most common practices for strengthening
the reinforced concrete structures is the application of FRP (Fiber
Reinforce Plastic) sheets to increase the flexural and shear strengths
of the member. The elastic modulus of FRP is considerably higher
than that of concrete. This will result in debonding between the FRP
sheets and concrete surface. With conventional surface preparation of
concrete, the ultimate capacity of the FRP sheets can hardly be
achieved. New methods for preparation of the bonding surface have
shown improvements in reducing the premature debonding of FRP
sheets from concrete surface. The present experimental study focuses
on the application of grooving method to postpone debonding of the
FRP sheets attached to the side faces of concrete beams for shear
strengthening. Comparison has also been made with conventional
surface preparation method. This study clearly shows the efficiency
of grooving method compared to surface preparation method, in
preventing the debonding phenomenon and in increasing the load
carrying capacity of FRP.
Abstract: The purpose of this research is to reduce the amount of incomplete coating of stainless steel washers in the electrodeposition painting process by using an experimental design technique. The surface preparation was found to be a major cause of painted surface quality. The influence of pretreating and painting process parameters, which are cleaning time, chemical concentration and shape of hanger were studied. A 23 factorial design with two replications was performed. The analysis of variance for the designed experiment showed the great influence of cleaning time and shape of hanger. From this study, optimized cleaning time was determined and a newly designed electrical conductive hanger was proved to be superior to the original one. The experimental verification results showed that the amount of incomplete coating defects decreased from 4% to 1.02% and operation cost decreased by 10.5%.