Abstract: In this study, the reduction of Cr(VI) by use of scrap
iron, a cheap and locally available industrial waste, was investigated
in continuous system. The greater scrap iron efficiency observed for
the first two sections of the column filling indicate that most of the
reduction process was carried out in the bottom half of the column
filling. This was ascribed to a constant decrease of Cr(VI)
concentration inside the filling, as the water front passes from the
bottom to the top end of the column. While the bottom section of the
column filling was heavily passivated with secondary mineral phases,
the top section was less affected by the passivation process; therefore
the column filling would likely ensure the reduction of Cr(VI) for
time periods longer than 216 hours. The experimental results indicate
that fixed beds columns packed with scrap iron could be successfully
used for the first step of Cr(VI) polluted wastewater treatment.
However, the mass of scrap iron filling should be carefully estimated
since it significantly affects the Cr(VI) reduction efficiency.
Abstract: The reduction of hexavalent chromium by scrap iron
was investigated in continuous system, using long-term column
experiments, for aqueous Cr(VI) solutions having low buffering
capacities, over the Cr(VI) concentration range of 5 – 40 mg/L. The
results showed that the initial Cr(VI) concentration significantly
affects the reduction capacity of scrap iron. Maximum reduction
capacity of scrap iron was observed at the beginning of the column
experiments; the lower the Cr(VI) concentration, the greater the
experiment duration with maximum scrap iron reduction capacity.
However, due to passivation of active surface, scrap iron reduction
capacity continuously decreased in time, especially after Cr(VI)
breakthrough. The experimental results showed that highest
reduction capacity recorded until Cr(VI) breakthrough was 22.8 mg
Cr(VI)/g scrap iron, at CI = 5 mg/L, and decreased with increasing
Cr(VI) concentration. In order to assure total reduction of greater
Cr(VI) concentrations for a longer period of time, either the mass of
scrap iron filling, or the hydraulic retention time should be increased.
Abstract: Hexavalent chromium is highly toxic to most living organisms and a known human carcinogen by the inhalation route of exposure. Therefore, treatment of Cr(VI) contaminated wastewater is essential before their discharge to the natural water bodies. Cr(VI) reduction to Cr(III) can be beneficial because a more mobile and more toxic chromium species is converted to a less mobile and less toxic form. Zero-valence-state metals, such as scrap iron, can serve as electron donors for reducing Cr(VI) to Cr(III). The influence of pH on scrap iron capacity to reduce Cr(VI) was investigated in this study. Maximum reduction capacity of scrap iron was observed at the beginning of the column experiments; the lower the pH, the greater the experiment duration with maximum scrap iron reduction capacity. The experimental results showed that highest maximum reduction capacity of scrap iron was 12.5 mg Cr(VI)/g scrap iron, at pH 2.0, and decreased with increasing pH up to 1.9 mg Cr(VI)/g scrap iron at pH = 7.3.