Abstract: Chemical detection is still a continuous challenge when
it comes to designing single-walled carbon nanotube (SWCNT)
sensors with high selectivity, especially in complex chemical
environments. A perfect example of such an environment would be in
thermally oxidized soybean oil. At elevated temperatures, oil oxidizes
through a series of chemical reactions which results in the formation of
monoacylglycerols, diacylglycerols, oxidized triacylglycerols, dimers,
trimers, polymers, free fatty acids, ketones, aldehydes, alcohols,
esters, and other minor products. In order to detect the rancidity of
oxidized soybean oil, carbon nanotube chemiresistor sensors have
been coated with polyethylenimine (PEI) to enhance the sensitivity
and selectivity. PEI functionalized SWCNTs are known to have a high
selectivity towards strong electron withdrawing molecules. The
sensors were very responsive to different oil oxidation levels and
furthermore, displayed a rapid recovery in ambient air without the
need of heating or UV exposure.
Abstract: To reduce the carbon dioxide emission into the
atmosphere, adsorption is believed to be one of the most attractive
methods for post-combustion treatment of flue gas. In this work,
activated carbon (AC) was modified by polyethylenimine (PEI) via
impregnation in order to enhance CO2 adsorption capacity. The
adsorbents were produced at 0.04, 0.16, 0.22, 0.25, and 0.28 wt%
PEI/AC. The adsorption was carried out at a temperature range from
30 °C to 75 °C and five different gas pressures up to 1 atm. TG-DTA,
FT-IR, UV-visible spectrometer, and BET were used to characterize
the adsorbents. Effects of PEI loading on the AC for the CO2
adsorption were investigated. Effectiveness of the adsorbents on the
CO2 adsorption including CO2 adsorption capacity and adsorption
temperature was also investigated. Adsorption capacities of CO2 were
enhanced with the increase in the amount of PEI from 0.04 to 0.22
wt% PEI before the capacities decreased onwards from0.25 wt% PEI
at 30 °C. The 0.22 wt% PEI/AC showed higher adsorption capacity
than the AC for adsorption at 50 °C to 75 °C.