Abstract: Fibre reinforced concrete (FRC) has been widely used in industrial pavements and non-structural elements such as pipes, culverts, tunnels, and precast elements. The strengthening effect of fibres in the concrete matrix is achieved primarily due to the bridging effect of fibres at the crack interfaces. The workability of the concrete was reduced on addition of high percentages of steel fibres. The optimum percentage of addition of steel fibres varies with its aspect ratio. For this study, 1% addition of steel has resulted to be the optimum percentage for both Hooked and Crimped Steel Fibres and was added to the beam specimens. The fibres restrain efficiently the cracks and take up residual stresses beyond the cracking. In this sense, diagonal cracks are effectively stitched up by fibres crossing it. The failure of beams within the shear failure range changed from shear to flexure in the presence of sufficient steel fibre quantity. The shear strength is increased with the addition of steel fibres and had exceeded the enhancement obtained with the transverse reinforcement. However, such increase is not directly in proportion with the quantity of fibres used. Considering all the clarification made in the present experimental investigation, it is concluded that 1% of crimped steel fibres with an aspect ratio of 50 is the best type of steel fibres for replacement of transverse stirrups in high strength concrete beams when compared to the steel fibres with hooked ends.
Abstract: This paper investigates and evaluates experimentally the structural behavior of high strength concrete (HSC) beams under fire and compares it with that of Normal strength concrete (NSC) beams. The main investigated parameters are: concrete compressive strength (300 or 600 kg/cm2); the concrete cover thickness (3 or 5 cm); the degree of temperature (room temperature or 600 oC); the type of cooling (air or water); and the fire exposure time (3 or 5 hours). Test results showed that the concrete compressive strength decreases significantly as the exposure time to fire increases.
Abstract: When high strength reinforced concrete is exposed to
high temperature due to a fire, deteriorations occur such as loss in
strength and elastic modulus, cracking and spalling of the concrete.
Therefore, it is important to understand risk of structural safety in
building structures by studying structural behaviors and rehabilitation
of fire damaged high strength concrete structures. This paper aims at
investigating rehabilitation effect on fire damaged high strength
concrete beams using experimental and analytical methods. In the
experiments, flexural specimens with high strength concrete are
exposed to high temperatures according to ISO 834 standard time
temperature curve. From four-point loading test, results show that
maximum loads of the rehabilitated beams are similar to or higher than
those of the non-fire damaged RC beam. In addition, structural
analyses are performed using ABAQUS 6.10-3 with same conditions
as experiments to provide accurate predictions on structural and
mechanical behaviors of rehabilitated RC beams. The parameters are
the fire cover thickness and strengths of repairing mortar. Analytical
results show good rehabilitation effects, when the results predicted
from the rehabilitated models are compared to structural behaviors of
the non-damaged RC beams. In this study, fire damaged high strength concrete beams are
rehabilitated using polymeric cement mortar. The predictions from the
finite element (FE) models show good agreements with the
experimental results and the modeling approaches can be used to
investigate applicability of various rehabilitation methods for further
study.
Abstract: The results of an experimental program conducted on seventeen simply supported concrete beams to study the effect of transverse reinforcement on the behavior of lap splice of steel reinforcement in tension zones in high strength concrete beams, are presented. The parameters included in the experimental program were the concrete compressive strength, the lap splice length, the amount of transverse reinforcement provided within the splice region, and the shape of transverse reinforcement around spliced bars. The experimental results showed that the displacement ductility increased and the mode of failure changed from splitting bond failure to flexural failure when the amount of transverse reinforcement in splice region increased, and the compressive strength increased up to 100 MPa. The presence of transverse reinforcement around spliced bars had pronounced effect on increasing the ultimate load, the ultimate deflection, and the displacement ductility. The prediction of maximum steel stresses for spliced bars using ACI 318-05 building code was compared with the experimental results. The comparison showed that the effect of transverse reinforcement around spliced bars has to be considered into the design equations for lap splice length in high strength concrete beams.
Abstract: This article presents the analysis of experimental values regarding cracking pattern, specific strains and deformability for reinforced high strength concrete beams. The beams have the concrete class C80/95 and a longitudinal reinforcement ratio of 2.01%, respectively 3.39%. The elements were subjected to flexure under static short-term and long-term loading. The experimental values are compared with calculation values using the design relationships according to Eurocode 2.