Abstract: In this study, we report the synthesis and
characterization of nanohydroxyapatite (nHAp) in gelatin-starch
matrix via biomimetic method. Characterization of the samples was
performed using X-ray diffraction (XRD) and Fourier Transform
infrared spectroscopy (FT-IR). The Size and morphology of the
nHAp samples were determined using scanning and transmission
electron microscopy (SEM and TEM). The results reveal that the
shape and morphology of nHAp is influenced by presence of
biopolymers as template. Carbonyl and amino groups from gelatin
and hydroxyl from starch play crucial roles in HAp formation on the
surface of gelatin-starch.
Abstract: Yam starch obtained from the water yam (munlued)
by the wet milling process was studied for some physicochemical
properties. Yam starch film was prepared by casting using glycerol as
a plasticizer. The effect of different glycerol (1.30, 1.65 and
2.00g/100g of filmogenic solution) and starch concentrations (3.30,
3.65 and 4.00g /100g of filmogenic solution) were evaluated on some
characteristics of the film. The temperature for obtaining the
gelatinized starch solution was 70-80°C and then dried at 45°C for 4
hours. The resulting starch from munlued granular morphology was
triangular and the average size of the granule was 26.68 μm. The
amylose content by colorimetric method was 26 % and the gelatinize
temperature was 70-80°C. The appearance of the film was smooth,
transparent, and glossy with average moisture content of 25.96% and
thickness of 0.01mm. Puncture deformation and flexibility increased
with glycerol content. The starch and glycerol concentration were a
significant factor of the yam starch film characteristics. Yam starch
film can be described as a biofilm providing many applications and
developments with the advantage of biodegradability.
Abstract: This study was conducted in order to determine the physical properties and stability of mayonnaise-like emulsions as affected by modified yam starches. Native yam starch was modified via pre-gelatinization and cross-linking phosphorylation procedures. The emulsions (50% oil dispersed phase) were prepared with 0.3% native potato, native yam, pre-gelatinized yam and cross-linking phosphorylation yam starches. The droplet size of surface weighted mean diameter was found to be significantly (p < 0.05) lower in the sample with cross-linking phosphorylation yam starch as compared to other samples. Moreover, the viscosity of the sample with pregelatinized yam starch was observed to be higher than that of other samples. The phase separation stability was low in the freshly prepared and stored (45 days, 5°C) emulsions containing native yam starch. This study thus generally suggested that modified yam starches were more suitable (i.e. better physical properties and stability) to be used as stabilizers in a similar system i.e. light mayonnaises, rather than a native yam starch.