Abstract: The main objective of this experimental study is to assess the shear strength and the crack behavior of the triplets built of perforated brickwork masonry elements. In order to observe the influence of shear resistance and energy dissipating before and after retrofitting applications by using the reinforcing system, static-cyclic shear tests were employed in the structural mechanics laboratory of Sakarya University. The reinforcing system is composed of hybrid multiaxial seismic fabric consisting of alkali resistant glass and polypropylene fibers. The plaster as bonding material used in the specimen’s retrofitting consists of expanded glass granular. In order to acquire exact measuring data about the failure behavior of the two mortar joints under shear stressing, vertical load-controlled cylinder having force capacity of 50 kN and loading rate of 1.5 mm/min. with an internal inductive displacement transducers is carried out perpendicular to the triplet specimens. In this study, a total of six triplet specimens with textile reinforcement were prepared for these shear bond tests. The three of them were produced as single-sided reinforced triplets with seismic fabric, while the others were strengthened on both sides. In addition, three triplet specimens without retrofitting and plaster were also tested as reference samples. The obtained test results were given in the manner of force-displacement relationships, ductility coefficients and shear strength parameters comparatively. It is concluded that two-side seismic textile applications on masonry elements with relevant plaster have considerably increased the sheer force resistance and the ductility capacity.
Abstract: The main aim of the presented experiments is to
improve behaviour of sandwich structures under dynamic loading,
such as crash or explosion. This paper describes experimental
investigation on the response of new advanced materials to low and
high velocity load. Blast wave energy absorbers were designed using
two types of porous lightweight raw particle materials based on
expanded glass and ceramics with dimensions of 0.5-1 mm,
combined with polymeric binder. The effect of binder amount on the
static and dynamic properties of designed materials was observed.
Prism shaped specimens were prepared and loaded to obtain physicomechanical
parameters – bulk density, compressive and flexural
strength under quasistatic load, the dynamic response was determined
using Split Hopkinson Pressure bar apparatus. Numerical
investigation of the material behaviour in sandwich structure was
performed using implicit/explicit solver LS-Dyna. As the last step,
the developed material was used as the interlayer of blast resistant
litter bin, and it´s functionality was verified by real field blast tests.
Abstract: Thin-walled elements with a matrix set on a base of
high-valuable Portland cement with dispersed reinforcement from
alkali-resistant glass fibres are used in a range of applications as
claddings of buildings and infrastructure constructions as well as
various architectural elements of residential buildings.
Even though their elementary thickness and therefore total weight
is quite low, architects and building companies demand on even
further decreasing of the bulk density of these fibre-cement elements
for the reason of loading elimination of connected superstructures
and easier assembling in demand conditions.
By the means of various kinds of light-weight aggregates it is
possible to achieve light-weighing of these composite elements.
From the range of possible fillers with different material properties
granulated expanded glass worked the best.
By the means of laboratory testing an effect of two fillers based on
expanded glass on the fibre reinforced cement composite was
verified.
Practical applicability was tested in the production of commonly
manufactured glass fibre reinforced concrete elements, such as
channels for electrical cable deposition, products for urban equipment
and especially various cladding elements.
Even though these are not structural elements, it is necessary to
evaluate also strength characteristics and resistance to environment
for their durability in certain applications.
Abstract: The Bulgarian natural expanded mineral obtained from Bentonite AD perlite (A deposit of "The Broken Mountain" for perlite mining, near by the village of Vodenicharsko, in the municipality of Djebel), was loaded with silver (as ion form - Ag+ 2 and 5 wt% by the incipient wetness impregnation method), and as atomic silver - Ag0 using Tollen-s reagent (silver mirror reaction). Some physicochemical characterization of the samples are provided via: DC arc-AES, XRD, DR-IR and UV-VIS. The aim of this work was to obtain and test the silver-loaded catalyst for ozone decomposition. So the samples loaded with atomic silver show ca. 80% conversion of ozone 20 minutes after the reaction start. Then conversion decreases to ca. 20 % but stay stable during the prolongation of time.