Abstract: Interest in using bacteria in cement materials due to its positive influences has been increased. Cement materials such as mortar and concrete basically suffer from higher porosity and water absorption compared to other building materials such as steel materials. Because of the negative side-effects of certain chemical techniques, biological methods have been proposed as a desired and environmentally friendly strategy for reducing concrete porosity and diminishing water absorption. This paper presents the results of an experimental investigation carried out to evaluate the influence of Sporosarcina pasteurii bacteria on the behaviour of two types of concretes (light weight aggregate concrete and normal weight concrete). The resistance of specimens to water penetration by testing water absorption and evaluating the electrical resistance of those concretes was examined and compared. As a conclusion, 20% increase in electrical resistance and 10% reduction in water absorption of lightweight aggregate concrete (LWAC) and for normal concrete the results show 7% decrease in water absorption and almost 10% increase in electrical resistance.
Abstract: In this investigation an elastic stress analysis is carried out a woven steel fiber reinforced thermoplastic cantilever beam loaded uniformly at the upper surface. The composite beam material consists of low density polyethylene as a thermoplastic (LDFE, f.2.12) and woven steel fibers. Granules of the polyethylene are put into the moulds and they are heated up to 160°C by using electrical resistance. Subsequently, the material is held for 5min under 2.5 MPa at this temperature. The temperature is decreased to 30°C under 15 MPa pressure in 3min. Closed form solution is found satisfying both the governing differential equation and boundary conditions. We investigated orientation angle effect on stress distribution of composite cantilever beams. The results show that orientation angle play an important role in determining the responses of a woven steel fiber reinforced thermoplastic cantilever beams and an optimal design of these structures.
Abstract: Steel corrosion in concrete is considered as a main
engineering problems for many countries and lots of expenses has been paid for their repair and maintenance annually. This problem
may occur in all engineering structures whether in coastal and offshore or other areas. Hence, concrete structures should be able to
withstand corrosion factors existing in water or soil. Reinforcing
steel corrosion enhancement can be measured by use of concrete
electrical resistance; and maintaining high electric resistivity in concrete is necessary for steel corrosion prevention. Lots of studies
devoted to different aspects of the subjects worldwide. In this paper, an evaluation of the effects of W/C ratio, cementitious materials, and
percent increase in silica fume were investigated on electric resistivity of high strength concrete. To do that, sixteen mix design
with one aggregate grading was planned. Five of them had varying amount of W/C ratio and other eleven mixes was prepared with
constant W/C ratio but different amount of cementitious materials.
Silica fume and super plasticizer were used with different proportions
in all specimens. Specimens were tested after moist curing for 28 days. A total of 80 cube specimens (50 mm) were tested for concrete
electrical resistance. Results show that concrete electric resistivity can be increased with increasing amount of cementitious materials
and silica fume.