Abstract: Thermo-mechanical processing with various processing parameters was applied to 0.2%C-0.6%Mn-2S%i-0.8%Cr low alloyed high strength steel. The aim of the processing was to achieve the microstructures typical for transformation induced plasticity (TRIP) steels. Thermo-mechanical processing used in this work incorporated two or three deformation steps. The deformations were in all the cases carried out during the cooling from soaking temperatures to various bainite hold temperatures. In this way, 4-10% of retained austenite were retained in the final microstructures, consisting further of ferrite, bainite, martensite and pearlite. The complex character of TRIP steel microstructure is responsible for its good strength and ductility. The strengths achieved in this work were in the range of 740 MPa – 836 MPa with ductility A5mm of 31-41%.
Abstract: An important goal of parboiling is a decrease of rice broken percentage and at the beginning Selected paddy of variety of rice Tarom and soaked at three different temperatures 45 Cº, 65 Cº and 80 Cº orderly for 5 hours, 4 hours and 1.5 hours to moisture of 40 % and then in steaming stage to operate these action two steaming methods are selected steaming under pressure condition and steaming in atmosphere pressure and In the first method after exerting air, the steam pressure is increase to 1 Kg/Cm2 which is done in two different duration times of 2.5 and 5 minutes and in second method used of three times of 5,10 and 15 minutes and dry to 8% moisture and decreases of rice broken percentage at best condition in variety of Tarom of 37.2 % to 7.3 % and increases yield percentage at best condition in variety of Tarom of 69.4 % to 75.93 % and bran percentage decreased in variety of Tarom of 9.53 % to 2.2-3.2 % and this issue cause increases yield percentage in rice and use of This method is very significant for our country because broken percentage of rice in our country is 23-33 %.